The Surface Coating of Commercial LiFePO4 by Utilizing ZIF-8 for High Electrochemical Performance Lithium Ion Battery

View ResearcherID and ORCID

XiaoLong Xu1, CongYu Qi1 (co-first author), ZhenDong Hao1, Hao Wang1,*, JinTing Jiu2, JingBing Liu1, Hui Yan1, Katsuaki Suganuma2

Abstract | Support Info
icon-htmlFull Text Html
icon-pdf-smPDF w/ Links
icon-citExport Citation
Figures
+Show more

Nano-Micro Lett. (2018) 10: 1

First Online: 26 August 2017 (Article)

DOI:10.1007/s40820-017-0154-4

*Corresponding author. E-mail: haowang@bjut.edu.cn

 

Abstract

 


Fig. 1 a Schematic illustration of the synthesis process. b TEM image, c line scanning EDS, d surface coating layer structure of LFP/CZIF-8. Regular lattice fringes of e LFP, f graphite and g Zn crystal

The requirement of energy storage equipment need to develop the lithium ion battery (LIB) with high electrochemical performance. The surface modification of commercial LiFePO4 (LFP) by utilizing zeolitic imidazolate frameworks-8 (ZIF-8) offers new possibilities for commercial LFP with high electrochemical performances. In this work, the carbonized ZIF-8 (CZIF-8) was coated on the surface of LFP particles by the in-situ growth and carbonization of ZIF-8. Transmission electron microscopy (TEM) indicates that there is an approximate 10 nm coating layer with metal zinc and graphite-like carbon on the surface of LFP/CZIF-8 sample. The N2 adsorption and desorption isotherm suggests that the coating layer has uniform and simple connecting mesopores. As cathode material, LFP/CZIF-8 cathode active material delivers a discharge specific capacity of 159.3 mAh g-1 at 0.1 C and a discharge specific energy of 141.7 mWh g-1 after 200 cycles at 5.0 C (the retention rate is approximate 99%). These results are attributed to the synergy improvement of the conductivity, the lithium ion diffusion coefficient, and the degree of freedom for volume change of LFP/CZIF-8 cathode. This work will contribute to the improvement of the cathode materials of commercial LIB.


 

Keywords

LiFePO4; Zeolitic imidazolate frameworks-8; Surface coating; Cathode; Lithium ion battery

 

Full Text Html

1 Introduction

    As the world’s population grows and the natural non-renewable resource consumes, developing the lithium ion batteries (LIBs) with high electrochemical performances become increasingly important [1-3]. Recently, LIBs with LiFePO4 (LFP) as cathodes have matured significantly and serviced the markets of modern electronics and electric vehicles [4-6]. However, the LFP with high specific energy and high cycle stability is still facing great challenge, because the electron/ion transfer and structural stability of commercial electrode materials cannot meet the harsh ultrahigh-rate working environment [7, 8]. Therefore, it is the assiduous goal to develop advanced electrode materials with high performances.

    High specific energy electrodes are highly related to voltage platforms [9, 10] and specific capacities of electrodes [11, 12]. For LFP cathode material, we have demonstrated that the increased voltage platform depends on the improvement of electrode conductivity [13]. In the past study, it was demonstrated that the carbon coating was an effective strategy to improve the conductivity of electrode material [14]. In general, the coating layer is amorphous carbon [15, 16], because the crystallization temperature of carbon is much higher than the crystal growth temperature of LFP. Meanwhile, the sp2 carbon material is conducive to the transmission of electrons [17], which may be beneficial to improve the conductive electrode material. Recently, some progress has been made in the surface coating of electrode material by using crystalline carbonaceous material at low temperature [1]. Moreover, metal elements are also used to improve the electrode conductivity due to their free electrons [18]. The improvement of the conductivity also has a significant effect on the specific capacity of the electrode material [1, 18]. These studies provide a theoretical basis for the improvement of specific energy of LFP cathode material.

    The high cycle stability mainly depends on the structural stability of the electrode material at different charge and discharge current rates [19, 20]. For LFP cathode material, both volume shrinkage (charge/lithium ion deintercalation) and expansion (discharge/lithium ion intercalation) will lead to structural damage, and thus cause capacity decline [21]. It is demonstrated that the suitable coating layer with porous structure can effectively improve the structural stability of active material by buffering volume change [22, 23]. This may be an appropriate modification method for commercial electrode materials.

    The surface coating plays an important role in the improvements of the electrochemical performances. The choice of coating materials is the key to improve the electrode performance. Zeolitic imidazolate frameworks-8 (ZIF-8) is a class of porous materials, which attracted considerable interest due to its regular polyhedral morphology and ordered pore structure [24, 25]. The pyrolysis products of ZIF-8 under anaerobic conditions are porous carbon materials with high specific surface areas and high conductivities [26, 27]. Torad [28] and Zhang [29] reported that graphite-type carbon was prepared at 800 °C by using ZIF-8 as raw materials, they also proved that crystalline carbon can be prepared at lower temperature. Moreover, the formation of metallic zinc annealed in an inert atmosphere is also conducive to the improvement of conductivity. Although ZIF-8 as coating material used to modify LIB anodes and showed excellent electrochemical performances [30, 31], ZIF-8 has not been used for surface coating of LFP cathode so far. Therefore, it is necessary to explore the effect of ZIF-8 in LFP cathode coating for improving the electrochemical performances of commercial LIB.

    In this work, we modify the commercial LFP by the growth and carbonization of ZIF-8 on the surface of LFP particles. The prepared LiFePO4/carbonized ZIF-8 (LFP/CZIF-8) was demonstrated evidentlyto improve the electrochemical performances compared with pristine commercial LFP materials.

2 Experimental

2.1 Coating Process

    The raw materials used in this experiment include methanol (99.5%, Beijing Chemical Works), zinc nitrate (99%, Tianjin Fuchen Chemical Reagent Factory), 2-methylimidazole (99%, Sinopharm Group Chemical Reagent Co., Ltd.), and commercial LiFePO4 powder (Qinghai Taifeng First Lithium Technology Co., Ltd).

    The coating processes were performed as described below: LFP was dispersed into methanol to form an uniform slurry by ultrasonic. Then, zinc nitrate and 2-methylimidazole were dissolved into the above slurry by magnetic stirring for 1 h. The mixture was aged at room temperature for 24 h andthe gray powders were precipitated. The ratio of LFP dispersion : zinc nitrate : 2-methylimidazole was 100 mL : 1.029 g : 1.314 g. And the ratio of LFP : methanol was 8 g : x mL (x = 0, 188, 282, 376). The powders were washed very carefully with methanol and annealed at 500/600/700/800/900 °C with a heating rate of 5 °C min-1 under nitrogen flow to obtain the LFP/CZIF-8 samples. As the blank sample, the ZIF-8 was synthesized using the same method without LFP.

2.2 Characterization

    The phase compositions of the synthesized products were analyzed by X-ray diffraction (XRD) employing a Cu-Kα X-ray diffractometer (D8 ADVANCE Bruker AXS). The morphologies of grains were characterized by transmission electron microscopy (TEM) with an energy dispersive spectrometer (EDS), TEM images were obtained using a Philips Tecnai 20U-TWIN microscope. Surface composition of sample is investigated using X-ray photoelectron spectroscopy (XPS, ESCALAB 250 XPS using Al Kα (1486.6 eV) radiation). The N2 adsorption and desorption isotherms and Barrett-Joyner-Halenda pore-size-distribution were obtained at 77 K using an automatic surface area analyzer (Micromeritics, Gemini V2380, USA) under continuous adsorption conditions. Raman spectroscopic analysis was performed with a 532 nm FILTER In-Via Raman microscopic instrument.

2.3 Electrochemical Evaluation

    The charge and discharge performances were determined with CR 2032 coin cells. The cathode materials were prepared by mixing the LFP/CZIF-8 with acetylene black and poly-(vinylidene fluoride) in a weight ratio of 8 : 1 : 1 in N-methyl pyrrolidone to ensure homogeneity. Then the slurry was coating on an Al-foil with about 0.02 mm thickness, dried under the air atmosphere at 60 °C for 5 h and the vacuum atmosphere at 120 °C for 10 h and cut into circular strips of 15 mm in diameter. The loading densities are ∼2.3 mg cm-2. The cells were assembled in a glove box filled with high purity argon, where lithium metal was used as an anode, polypropylene film as a separator, and 1 M LiPF6 as an electrolyte consisting of ethylene carbonate/dimethyl carbonate/ethylene methyl carbonate in a volume ratio of 1 : 1 : 1 (1 M LiPF6/EC/DEC/EMC) as lithium ion electrolyte. Under each condition, five identical samples were synthesized.

    The charge and discharge performances of the LFP/CZIF-8 were tested on a channels battery analyzer (CT3008W) at different current densities between 2.5 and 4.2 V cut-off voltage using the coin-cells. The electrochemical impedance spectroscopy (EIS) measurements were performed on a PARSTAT 4000 electrochemical workstation. EIS were also recorded with frequencies ranging from 100 kHz to 10 mHz and an AC signal of 5 mV in amplitude as the perturbation. All the tests were performed at room temperature.

3 Results and Discussion

    Figure 1a shows a schematic illustration of the synthesis route for the LFP/CZIF-8. The SEM image shows the average size of LFP particles is about 4 μm in Fig. S1. In the methanol solution, the uniformly dispersed micron-scale LFP particles provide more positions for non-uniform nucleation of ZIF-8 [32]. When zinc nitrate and 2-methylimidazole are dissolved in methanol, ZIF-8 nuclei are rapidly formed on the surface of LFP particles. After aging, the ZIF-8 particles grow up and the annealing precursors (LFP/ZIF-8) formed. After high temperature annealing under nitrogen atmosphere, the organic ligands are pyrolyzed and crystallized to form graphite-like carbon. At the same time, a reducing atmosphere is formed, and the zinc ions are reduced to elemental zinc. The pore formed by the pyrolysis carbonization of the imidazole ligand is preserved due to the slow heating rate. The XRD (Fig. S2) patterns of samples shows that the peaks of all samples are indexed to the LiFePO4 phase, it indicates that the surface coating does not alter the crystal structure of LFP. Moreover, as shown in Fig. S3a, all peaks are consistent with the ZIF-8 nanocrystals, which prove that ZIF-8 can be synthesized in the methanol solution. The electrochemical performances of LFP/CZIF-8 cathode materials are evaluated and compared by charge and discharge tests using CR2032 coin cells (Fig. S4). The results illustrate that the optimal ratio of LFP/methanol is 8 g : 282 mL) and the optimal heat treatment temperature is 800 °C ).

Fig. 1 a Schematic illustration of the synthesis process. b TEM image, c line scanning EDS, d surface coating layer structure of LFP/CZIF-8. Regular lattice fringes of e LFP, f graphite and g Zn crystal

Fig. 1 a Schematic illustration of the synthesis process. b TEM image, c line scanning EDS, d surface coating layer structure of LFP/CZIF-8. Regular lattice fringes of e LFP, f graphite and g Zn crystal.

    The TEM and line scanning EDS analysis were employed to probe the composition and structure of the coating layer. The yellow line in Fig. 1b marks the line scanning EDS test range from 0 to 250 μm. The element distribution curve in Fig. 1c shows that there are C and Zn in the coating layer on the particle surface because of the existent curves of carbon and Zn in the range of 60 to 200 μm. The Zn content is less because the annealing temperature is close to its boiling point (908 °C), it causes the volatilization of metal Zn at 800 °C. A nano-scaled LFP/CZIF-8 particle with the particle size of about 300 nm is showed in Fig. 1d. There is a 10 nm coating layer on the surface of LFP/CZIF-8 particle. Figure 1e shows the clear regular lattice fringes with a d-spacing of 0.3008 nm which corresponds to the (121) plane of LFP. The regular lattice fringes with the d-spacing of 0.3348 nm corresponds to the (006) plane of graphite, and the lattice fringes of Zn were also found in the white dashed box (Fig. 1f). The enlarged image displays that the d-spacing of 0.2091 nm corresponds to the (101) plane of elemental zinc. These results demonstrate the in-situ growth of elemental zinc and graphite-like carbon on LFP surface. Moreover, the XPS results also confirm the existing of elemental zinc (Fig. S5). Two peaks at 1021.78 eV (2p3/2) and 1044.88 eV (2p1/2) and the peak splitting of 23.1 eV assure the presence of elemental zinc, which is beneficial to enhance the conductivity of LFP/CZIF-8.

Fig. 2 a An enlarged TEM image of LFP/CZIF-8. b The mechanism of conductivity improvement, FE I represents free electron in graphite, FE II is free electron in metal zinc.

Fig. 2 a An enlarged TEM image of LFP/CZIF-8. b The mechanism of conductivity improvement, FE I represents free electron in graphite, FE II is free electron in metal zinc.

    Figure 2a exhibits an enlarged TEM image of LFP/CZIF-8, showing clear lattice fringes of LFP (121), Zn (101) and graphite (006). The angle between the (121) plane of LFP and the (101) plane of Zn is 49.1o. The angle is 37.5o between the (121) plane of LFP and the (006) plane of graphite. The angle is 93.4o between (101) plane of Zn and the (006) plane of graphite. It clearly shows the heterostructure of the LFP/CZIF-8material. This indicates that the nucleation and crystal growth of ZIF-8 nanoparticles occur on the surface of LFP particle. After annealing, the graphite-like carbon and Zn are also formed. Figure 2b illustrates the conductive mechanism of the heterostructure of the LFP/CZIF-8 material. As we know, graphite has good conductivity because it is the ordered sp2 carbon and it has free electrons (yellow balls, FE I). Moreover, metal Zn contains a lot of free electrons (green balls, FE II), so it has better conductivity than graphite. As surface coating material, graphite and Zn are able to improve the conductivity of commercial LFP cathode due to their rich FEs.

Fig. 3 a The first charge and discharge curves of cathodes between 2.5 and 4.2 V at 0.1 C. b The enlarged figure remarked in a. The range of voltage is between 3.36 and 3.55 V, the range of specific capacity is between 5.0 and 55.0 mAh g-1. The distance between the voltage platforms of two discharge curves is about 54 mV.

Fig. 3 a The first charge and discharge curves of cathodes between 2.5 and 4.2 V at 0.1 C. b The enlarged figure remarked in a. The range of voltage is between 3.36 and 3.55 V, the range of specific capacity is between 5.0 and 55.0 mAh g-1. The distance between the voltage platforms of two discharge curves is about 54 mV.

    Figure 3a shows the first charge and discharge curves of LFP and LFP/CZIF-8 cathodes between 2.5 and 4.2 V at 0.1 C. The specific capacity is significantly enhanced after surface coating due to the improvement of conductivity. As shown in Fig. 3b, the range of voltage is between 3.36 and 3.55 V, the range of specific capacity is between 5.0 and 55.0 mAh g-1. The distance between the voltage platforms of two discharge curves is about 54 mV. It indicates that the conductivity enhancement leads to a dramatic increase in the discharge voltage platform, which is conducive to the improvement of specific energy.

Fig. 4 a Barrett-Joyner-Halenda pore-size-distribution and the isotherm shape of LFP and LFP/CZIF-8. b Working mechanism of the coating layer in LFP/CZIF-8

Fig. 4 a Barrett-Joyner-Halenda pore-size-distribution and the isotherm shape of LFP and LFP/CZIF-8. b Working mechanism of the coating layer in LFP/CZIF-8

    Figure 4a shows the N2 adsorption–desorption isotherms of LFP and LFP/CZIF-8. The Barrett-Joyner-Halenda pore-size-distribution line chart shows that the LFP/CZIF-8 has a hierarchical pore structure, and the pore-size distribution range centers at 1.9-244.7 nm. While, the LFP is almost nonporous. Interestingly, the mesoporous content of LFP/CZIF-8 is the highest in approximate 10 nm, which indicates that there is a large number of 10 nm mesoporous structures in the coating layer. The BET surface areas of LFP and LFP/CZIF-8 are 11.1 and 271.6 m2 g-1, respectively. The isotherm shapes of the LFP and LFP/CZIF-8 are of the type-III and type-IV patterns [33]. It indicates that LFP and LFP/CZIF-8 possess non-porous and mesoporous characteristics, respectively. Especially, the LFP/CZIF-8 shows the H1 hysteresis loop in the relative pressure (P/P0) range of 0.54 - 0.90, representing a typical mesoporous feature caused by uniform and simple connecting pores in the surface coating layer [34]. Moreover, the HRTEM image of ZIF-8 annealed at 800 °C is employed to intuitively observe the pore structure (Fig. S3b). The porous size range is similar to the result of N2 adsorption–desorption test. It implies that the coating layer of LFP/CZIF-8 possesses rich pore structure. Figure 4b illustrates the working mechanism of the coating layer of the LFP/CZIF-8 cathode materials. Such a mesoporous layer with open interconnected pore structure can significantly increase the permeability of the electrolyte and thus facilitate lithium ion diffusion, which gives a short diffusion path for mass and charge transport. This also leads to a higher degree of freedom for volume change during charge and discharge cycles, and an enhanced lithium ion intercalating behavior.

Fig. 5 a Nyquist plots of LFP and LFP/CZIF-8 cathodes in EIS curves. b The plots of impedance as a function of the inverse square root of angular frequency in the Warburg region

Fig. 5 a Nyquist plots of LFP and LFP/CZIF-8 cathodes in EIS curves. b The plots of impedance as a function of the inverse square root of angular frequency in the Warburg region.

    The EIS curves of LFP and LFP/CZIF-8 cathodes are shown in Fig. 5a, which are used to compare the ion conductivity after coating. The radius of the semicircle at high frequency region on the Z′-axis is related to the charge transfer resistance (Rct). The results show that the Rct value of LFP/CZIF-8 cathode (188.9 Ω) is obviously less than that of LFP cathode (439.3 Ω). Therefore, the conductivity is improved after coating. Figure 5b shows the slope of inclined line in low frequency representing the Warburg impedance (W) of EIS curve, which is used to study the lithium ion diffusion behavior. The slope σ can be obtained from the linear fitting of Zreal vs. ω-1/2. Using σ value, it is possible to calculate the lithium diffusion coefficient of the cathode [35]. The calculation results (Table S1) show that the lithium diffusion coefficient of LFP/CZIF-8 cathode (1.1708×10-13 cm2 s-1) is about 20 times that of LFP cathode (6.7553×10-15 cm2 s-1). It indicates that the lithium diffusion coefficient is also improved after coating.

Fig. 6 First charge-discharge curves of the LIBs with the a LFP and c LFP/CZIF-8 at different rates. Capacity retention and Coulombic efficiency of the LIBs with the b LFP and d LFP/CZIF-8 for 50 cycles at different rates. e The discharge specific energy of different cathode samples for 10 cycles at 0.1–10.0C rates, respectively, then for 100 and 200 cycles at 10.0 and 5.0C rates, respectively

Fig. 6 First charge-discharge curves of the LIBs with the a LFP and c LFP/CZIF-8 at different rates. Capacity retention and Coulombic efficiency of the LIBs with the b LFP and d LFP/CZIF-8 for 50 cycles at different rates. e The discharge specific energy of different cathode samples for 10 cycles at 0.1–10.0C rates, respectively, then for 100 and 200 cycles at 10.0 and 5.0C rates, respectively.

    Moreover, we investigate the effects of annealing temperature and the ratio of LFP/methanol on the ion conductivity by using EIS test (Fig. S6 and Table S1). We find that the increase of the coating material is beneficial to the enhancements of the ion conductivity and lithium diffusion coefficient (Fig. S6a, c). And the LFP/CZIF-8 cathode synthesized at 800 °C delivers the highest conductivity and lithium diffusion coefficient (Fig. S6b, d). The Raman spectra (Fig. S7) shows that the peak intensity ratio of the G-band and the D-band (IG/ID) is the highest when the annealing temperature is 800 °C. The results suggest that the 800 °C annealed sample has the largest degree of graphitization without damaging the coating layer. Therefore, 800 °C is the optimized annealing temperature with the highest conductivity.

    The C rate performances and cycle stability of cathode active materials are shown in Fig. 6. Compared LFP/CZIF-8 cathode (Fig. 6a) with LFP cathode (Fig. 6c), the discharge specific capacities of LFP/CZIF-8 cathode are all higher than that of LFP cathode at different C rates. The capacity of LFP/CZIF-8 cathode is 159.3 mAh g-1 at 0.1 C, while, that of LFP is 122 mAh g-1. Similarly, the capacity retention rates of LFP/CZIF-8 cathode (Fig. 6b) are also higher at all C rates compared with LFP cathode (Fig. 6d). The values of the capacity retention rates are 96.1 and 101.0% before (LFP) and after (LFP/CZIF-8) coating at 2.0 C, respectively. The electrochemical performances of LFP active material are significantly improved after coating by CZIF-8.

    The discharge specific energies of LFP and LFP/CZIF-8 cathodes’ active materials are shown in Fig. 6e. The discharge specific energies at different C rates are significantly improved, the average value of LFP/CZIF-8 cathodes’ discharge specific energy is 355.3 mWh g-1 at 1.0 C, while that of LFP is 212.7 mWh g-1. Moreover, the discharge specific energy retention rate of LFP/CZIF-8 cathode is approximate 99% after 200 cycles at 5.0 C, while LFP’s discharge specific energy retention rate is only 40%. These results are attributed to the synergy improvements of voltage platform, specific capacity, and freedom degree for volume change after surface coating.

4 Conclusions

    In summary, we studied the surface modification of commercial LiFePO4 (LFP) by utilizing ZIF-8 and synthesized the LFP/CZIF-8 cathodes by growth and carbonization of ZIF-8 on the surface of LFP. The coating layer with metal Zn and graphite-like carbon is about 10 nm. Using as the cathode material, LFP/CZIF-8 clearly improves the conductivity, the lithium ion diffusion coefficient, and the degree of freedom for volume change. Therefore, LFP/CZIF-8 delivers a discharge specific capacity of 159.3 mAh g-1 at 0.1 C and a discharge specific energy of 141.7 mWh g-1 after 200 cycles at 5.0 C (the retention rate is approximately 99%).

    Although we demonstrated that ZIF-8 was a better surface modification material for commercial LIB cathodes, several key aspects still need to be explored in the future. (1) The theoretical description and prediction of the mechanism of the enhancement of electrochemical performances should be established in future studies. (2) It is necessary to further study the controllability of the ratio of LFP, graphite and zinc. Potentially, our approach for modifying LFP cathode materials could also be applied in modifying other cathodes for commercial LIBs.

Acknowledgements

This work is supported by the Scientific and Technological Development Project of the Beijing Education Committee (No. KZ201710005009).

References

[1] X.L. Yi, W. He, X.D. Zhang, Y.Z. Yue, G.H. Yang, Z.Y. Wang, M.J. Zhou, L.Z. Wang, Graphene-like carbon sheet/Fe3O4 nanocomposites derived from soda papermaking black liquor for high performance lithium ion batteries. Electrochim. Acta 232, 550-560 (2017). doi:10.1016/j.electacta.2017.02.130
[2] K. Lu, J.T. Xu, J.T. Zhang, B. Song, H.Y. Ma, General preparation of three-dimensional porous metal oxide foams coated with nitrogen-doped carbon for enhanced lithium storage. ACS Appl. Mater. Interfaces 8(27), 17402-17408 (2016). doi:10.1021/acsami.6b04587
[3] Z.L. Zhao, F.S. Cannon, C. Nieto-Delgado, L. Pena, Lignin/collagen hybrid biomaterials as binder substitute for specialty graphites and electrodes. Carbon 108, 303-317 (2016). doi:10.1016/j.carbon.2016.07.026
[4] L. Shen, X. Zhang, E. Uchaker, C. Yuan, G. Cao, Li4Ti5O12 nanoparticles embedded in a mesoporous carbon matrix as a superior anode material for high rate lithium ion batteries. Adv. Energy Mater. 2(6), 691-698 (2012). doi:10.1002/aenm.201100720
[5] Z.J. Yao, X.H. Xia, Y. Zhong, Y.D. Wang, B.W. Zhang, D. Xie, X.L. Wang, J.P. Tu, Y.Z. Huang, Hybrid vertical graphene/lithium titanate-CNTs arrays for lithium ion storage with extraordinary performance. J. Mater. Chem. A 5(19), 8916-8921 (2017). doi:10.1039/C7TA02511D
[6] Q. Wang, S.X. Deng, H. Wang, M. Xie, J.B. Liu, H. Yan, Hydrothermal synthesis of hierarchical LiFePO4 microspheres for lithium ion battery. J. Alloy. Compd. 553, 69-74 (2013). doi:10.1016/j.jallcom.2012.11.041
[7] M. Xie, X.X. Zhang, S.X. Deng, Y.Z. Wang, H. Wang, J.B. Liu, H. Yan, J. Laaksob, E. Levanen, The effects of supercritical carbon dioxide treatment on the morphology and electrochemical performance of LiFePO4 cathode materials. RSC Adv. 3(31), 12786-12793 (2013). doi:10.1039/c3ra41133h
[8] M. Xie, X.X. Zhang, Y.Z. Wang, S.X. Deng, H. Wang, J.B. Liu, H. Yan, J. Laaksob, E. Levanen, A template-free method to prepare porous LiFePO4 via supercritical carbon dioxide. Electrochim. Acta 94, 16-20 (2013). doi:10.1016/j.electacta.2013.01.131
[9] X.L. Xu, S.X. Deng, H. Wang, J.B. Liu, H. Yan, Research progress in improving the cycling stability of high-voltage LiNi0.5Mn1.5O4 cathode in lithium-ion battery. Nano-Micro Lett. 9(2), 22 (2017). doi:10.1007/s40820-016-0123-3
[10] S.X. Deng, D.L. Mao, H. Wang, B. Wang, J.B. Liu, Y.L. Ma, H. Yan, Preparation and electrochemical properties of double-shell LiNi0.5Mn1.5O4 hollow microspheres as cathode materials for Li-ion batteries. RSC Adv. 6(51), 45369-45375 (2016). doi:10.1039/C6RA05620B
[11] X.D. Zhang, Z.Y. Bi, W. He, G. Yang, H. Liu, Y.Z. Yue, Fabricating high-energy quantum dots in ultra-thin LiFePO4 nanosheets using a multifunctional high-energy biomolecule-ATP. Energy Environ. Sci. 7(7), 2285-2294 (2014). doi:10.1039/C3EE44187C
[12] X.D. Zhang, X.L. Xu, W. He, G.H. Yang, J.X. Shen, J.H. Liu, Q.Z. Liu, LiFePO4/NaFe3V9O19/porous glass nanocomposite cathodes for Li+/Na+ mixed-ion batteries. J. Mater. Chem. A 3(44), 22247-22257 (2015). doi:10.1039/C5TA06424D
[13] X.L. Xu, Z.D. Hao, H. Wang, J.B. Liu, H. Yan, Mesoporous carbon derived from ZIF-8 for improving electrochemical performances of commercial LiFePO4. Mater. Lett. 197, 209-212 (2017). doi:10.1016/j.matlet.2017.02.093
[14] S.X. Deng, H. Wang, H. Liu, J.B. Liu, H. Yan, Research progress in improving the rate performance of LiFePO4 cathode materials. Nano-Micro Lett. 6(3), 209-226 (2014). doi:10.1007/BF03353785
[15] Y.D. Cho, G.T.K. Fey, H.M. Kao, The effect of carbon coating thickness on the capacity of LiFePO4/C composite cathodes. J. Power Sources 189(1), 256-262 (2009). doi:10.1016/j.jpowsour.2008.09.053
[16] Y.H. Nien, J.R. Carey, J.S. Chen, Physical and electrochemical properties of LiFePO4/C composite cathode prepared from various polymer-containing precursors. J. Power Sources 193(2), 822-827 (2009). doi:10.1016/j.jpowsour.2009.04.013
[17] Y.L. Xiao, J.T. Zai, B.B. Tian, X.F. Qian, Formation of NiFe2O4/expanded graphite nanocomposites with superior lithium storage properties. Nano-Micro Lett. 9, 34 (2017). doi:10.1007/s40820-017-0127-7
[18] H. Guo, X.D. Zhang, W. He, X.N. Yang, Q.Z. Liu, M. Li, J.C. Wang, Fabricating three-dimensional mesoporous carbon network-coated LiFePO4/Fe nanospheres using thermal conversion of alginate-biomass. RSC Adv. 6(21), 16933-16940 (2016). doi:10.1039/C6RA00125D
[19] L. Wu, X.H. Hu, J.F. Qian, F. Pei, F.Y. Wu, Sb-C nanofibers with long cycle life as an anode material for high-performance sodium-ion batteries. Energy Environ. Sci. 7(1), 323-328 (2014). doi:10.1039/C3EE42944J
[20] D.L. Wang, H.L. Xin, R. Hovden, H.S. Wang, Y.C. Yu, D.A. Muller, F.J. DiSalvo, H.D. Abruna, Structurally ordered intermetallic platinum-cobalt core-shell nanoparticles with enhanced activity and stability as oxygen reduction electrocatalysts. Nat. Mater. 12(1), 81-87 (2013). doi:10.1038/nmat3458
[21] Q. Zhang, S.Z. Huang, J. Jin, J. Liu, Y. Li, H.E. Wang, L.H. Chen, B.J. Wang, B.L. Su, Engineering 3D bicontinuous hierarchically macro-mesoporous LiFePO4/C nanocomposite for lithium storage with high rate capability and long cycle stability. Sci. Rep. 6, 25942 (2016). doi:10.1038/srep25942
[22] W.K. Kim, W.H. Ryu, D.W. Han, S.J. Lim, J.Y. Eom, H.S. Kwon, Fabrication of graphene embedded LiFePO4 using a catalyst assisted self assembly method as a cathode material for high power lithium-ion batteries. ACS Appl. Mater. Interfaces 6(7), 4731-4736 (2014). doi:10.1021/am405335k
[23] X.H. Tian, Y.K. Zhou, X.F. Tu, Z.T. Zhang, G.D. Du, Well-dispersed LiFePO4 nanoparticles anchored on a three-dimensional graphene aerogel as high-performance positive electrode materials for lithium-ion batteries. J. Power Sources 340, 40-50 (2017). doi:10.1016/j.jpowsour.2016.11.049
[24] P. Simon, Y. Gogotsi, B. Dunn, Where do batteries end and supercapacitors begin. Science 343(6176), 1210-1211 (2014). doi:10.1126/science.1249625
[25] D.L. Li, S.H. Wu, F.F. Wang, S.Y. Jia, Y. Liu, X. Han, L.W. Zhang, S.L. Zhang, Y.M. Wu, A facile one-pot synthesis of hemin/ZIF-8 composite as mimetic peroxidase. Mater. Lett. 178, 48-51 (2016). doi:10.1016/j.matlet.2016.04.200
[26] J. Tang, R.R. Salunkhe, J. Liu, N.L. Torad, M. Imura, S. Furukawa, Y. Yamauchi, Thermal conversion of core-shell metal-organic frameworks: a new method for selectively functionalized nanoporous hybrid carbon. J. Am. Chem. Soc. 137(4), 1572-1580 (2015). doi:10.1021/ja511539a
[27] X.D. Shi, Z.A. Zhang, Y. Fu, Y.Q. Gan, Self-template synthesis of nitrogen-doped porous carbon derived from zeolitic imidazolate framework-8 as an anode for sodium ion batteries. Mater. Lett. 161, 332-335 (2015). doi:10.1016/j.matlet.2015.08.137
[28] N.L. Torad, M. Hu, Y. Kamachi, K. Takai, M. Imura, Facile synthesis of nanoporous carbons with controlled particle sizes by direct carbonization of monodispersed ZIF-8 crystals. Chem. Commun. 49(25), 2521-2523 (2013). doi:10.1039/c3cc38955c
[29] L.J. Zhang, Z.X. Su, F.L. Jiang, L.L. Yang, J.J. Qian, Highly graphitized nitrogen-doped porous carbon nanopolyhedra derived from ZIF-8 nanocrystals as efficient electrocatalysts for oxygen reduction reactions. Nanoscale 6(12), 6590-6602 (2014). doi:10.1039/C4NR00348A
[30] X.Z. Zheng, Y.F. Li, Y.X. Xu, Z.S. Hong, M.D. Wei, Metal-organic frameworks: promising materials for enhancing electrochemical properties of nanostructured Zn2SnO4 anode in Li-ion batteries. CrystEngComm 14(6), 2112-2116 (2012). doi:10.1039/c2ce06350f
[31] G.H. Zhang, S.C. Hou, H. Zhang, W. Zeng, F.L. Yan, C.C. Li, H.G. Duan, High-performance and ultra-stable lithium-ion batteries based on MOF-derived ZnO@ ZnO quantum dots/C core-shell nanorod arrays on a carbon cloth anode. Adv. Mater. 27(14), 2400-2405 (2015). doi:10.1002/adma.201405222
[32] Q.T. Zhang, Foundation of Inorganic Materials Science. East China University of Technology Press, 2007.
[33] X.Y. Du, W. He, X.D. Zhang, J.Y. Ma, C.H. Wang, C.S. Li, Y.Z. Yue, Low temperature biosynthesis of Li2O-MgO-P2O5-TiO2 nanocrystalline glass with mesoporous structure exhibiting fast lithium ion conduction. Mater. Sci. Eng. C 33(3), 1592-1600 (2013). doi:10.1016/j.msec.2012.12.065
[34] W.H. Li, Z.Z. Yang, M.S. Li, Y. Jiang, X. Wei, X.W. Zhong, L. Gu, Y. Yu, Amorphous red phosphorus embedded in highly ordered mesoporous carbon with superior lithium and sodium storage capacity. Nano Lett. 16(3), 1546-1553 (2016). doi:10.1021/acs.nanolett.5b03903
[35] Y. Cui, X.L. Zhao, R.S. Guo, Improved electrochemical performance of La0.7Sr0.3MnO3 and carbon co-coated LiFePO4 synthesized by freeze-drying process. Electrochim. Acta 55(3), 922-926 (2010). doi:10.1016/j.electacta.2009.08.020

References

[1] X.L. Yi, W. He, X.D. Zhang, Y.Z. Yue, G.H. Yang, Z.Y. Wang, M.J. Zhou, L.Z. Wang, Graphene-like carbon sheet/Fe3O4 nanocomposites derived from soda papermaking black liquor for high performance lithium ion batteries. Electrochim. Acta 232, 550-560 (2017). doi:10.1016/j.electacta.2017.02.130
[2] K. Lu, J.T. Xu, J.T. Zhang, B. Song, H.Y. Ma, General preparation of three-dimensional porous metal oxide foams coated with nitrogen-doped carbon for enhanced lithium storage. ACS Appl. Mater. Interfaces 8(27), 17402-17408 (2016). doi:10.1021/acsami.6b04587
[3] Z.L. Zhao, F.S. Cannon, C. Nieto-Delgado, L. Pena, Lignin/collagen hybrid biomaterials as binder substitute for specialty graphites and electrodes. Carbon 108, 303-317 (2016). doi:10.1016/j.carbon.2016.07.026
[4] L. Shen, X. Zhang, E. Uchaker, C. Yuan, G. Cao, Li4Ti5O12 nanoparticles embedded in a mesoporous carbon matrix as a superior anode material for high rate lithium ion batteries. Adv. Energy Mater. 2(6), 691-698 (2012). doi:10.1002/aenm.201100720
[5] Z.J. Yao, X.H. Xia, Y. Zhong, Y.D. Wang, B.W. Zhang, D. Xie, X.L. Wang, J.P. Tu, Y.Z. Huang, Hybrid vertical graphene/lithium titanate-CNTs arrays for lithium ion storage with extraordinary performance. J. Mater. Chem. A 5(19), 8916-8921 (2017). doi:10.1039/C7TA02511D
[6] Q. Wang, S.X. Deng, H. Wang, M. Xie, J.B. Liu, H. Yan, Hydrothermal synthesis of hierarchical LiFePO4 microspheres for lithium ion battery. J. Alloy. Compd. 553, 69-74 (2013). doi:10.1016/j.jallcom.2012.11.041
[7] M. Xie, X.X. Zhang, S.X. Deng, Y.Z. Wang, H. Wang, J.B. Liu, H. Yan, J. Laaksob, E. Levanen, The effects of supercritical carbon dioxide treatment on the morphology and electrochemical performance of LiFePO4 cathode materials. RSC Adv. 3(31), 12786-12793 (2013). doi:10.1039/c3ra41133h
[8] M. Xie, X.X. Zhang, Y.Z. Wang, S.X. Deng, H. Wang, J.B. Liu, H. Yan, J. Laaksob, E. Levanen, A template-free method to prepare porous LiFePO4 via supercritical carbon dioxide. Electrochim. Acta 94, 16-20 (2013). doi:10.1016/j.electacta.2013.01.131
[9] X.L. Xu, S.X. Deng, H. Wang, J.B. Liu, H. Yan, Research progress in improving the cycling stability of high-voltage LiNi0.5Mn1.5O4 cathode in lithium-ion battery. Nano-Micro Lett. 9(2), 22 (2017). doi:10.1007/s40820-016-0123-3
[10] S.X. Deng, D.L. Mao, H. Wang, B. Wang, J.B. Liu, Y.L. Ma, H. Yan, Preparation and electrochemical properties of double-shell LiNi0.5Mn1.5O4 hollow microspheres as cathode materials for Li-ion batteries. RSC Adv. 6(51), 45369-45375 (2016). doi:10.1039/C6RA05620B
[11] X.D. Zhang, Z.Y. Bi, W. He, G. Yang, H. Liu, Y.Z. Yue, Fabricating high-energy quantum dots in ultra-thin LiFePO4 nanosheets using a multifunctional high-energy biomolecule-ATP. Energy Environ. Sci. 7(7), 2285-2294 (2014). doi:10.1039/C3EE44187C
[12] X.D. Zhang, X.L. Xu, W. He, G.H. Yang, J.X. Shen, J.H. Liu, Q.Z. Liu, LiFePO4/NaFe3V9O19/porous glass nanocomposite cathodes for Li+/Na+ mixed-ion batteries. J. Mater. Chem. A 3(44), 22247-22257 (2015). doi:10.1039/C5TA06424D
[13] X.L. Xu, Z.D. Hao, H. Wang, J.B. Liu, H. Yan, Mesoporous carbon derived from ZIF-8 for improving electrochemical performances of commercial LiFePO4. Mater. Lett. 197, 209-212 (2017). doi:10.1016/j.matlet.2017.02.093
[14] S.X. Deng, H. Wang, H. Liu, J.B. Liu, H. Yan, Research progress in improving the rate performance of LiFePO4 cathode materials. Nano-Micro Lett. 6(3), 209-226 (2014). doi:10.1007/BF03353785
[15] Y.D. Cho, G.T.K. Fey, H.M. Kao, The effect of carbon coating thickness on the capacity of LiFePO4/C composite cathodes. J. Power Sources 189(1), 256-262 (2009). doi:10.1016/j.jpowsour.2008.09.053
[16] Y.H. Nien, J.R. Carey, J.S. Chen, Physical and electrochemical properties of LiFePO4/C composite cathode prepared from various polymer-containing precursors. J. Power Sources 193(2), 822-827 (2009). doi:10.1016/j.jpowsour.2009.04.013
[17] Y.L. Xiao, J.T. Zai, B.B. Tian, X.F. Qian, Formation of NiFe2O4/expanded graphite nanocomposites with superior lithium storage properties. Nano-Micro Lett. 9, 34 (2017). doi:10.1007/s40820-017-0127-7
[18] H. Guo, X.D. Zhang, W. He, X.N. Yang, Q.Z. Liu, M. Li, J.C. Wang, Fabricating three-dimensional mesoporous carbon network-coated LiFePO4/Fe nanospheres using thermal conversion of alginate-biomass. RSC Adv. 6(21), 16933-16940 (2016). doi:10.1039/C6RA00125D
[19] L. Wu, X.H. Hu, J.F. Qian, F. Pei, F.Y. Wu, Sb-C nanofibers with long cycle life as an anode material for high-performance sodium-ion batteries. Energy Environ. Sci. 7(1), 323-328 (2014). doi:10.1039/C3EE42944J
[20] D.L. Wang, H.L. Xin, R. Hovden, H.S. Wang, Y.C. Yu, D.A. Muller, F.J. DiSalvo, H.D. Abruna, Structurally ordered intermetallic platinum-cobalt core-shell nanoparticles with enhanced activity and stability as oxygen reduction electrocatalysts. Nat. Mater. 12(1), 81-87 (2013). doi:10.1038/nmat3458
[21] Q. Zhang, S.Z. Huang, J. Jin, J. Liu, Y. Li, H.E. Wang, L.H. Chen, B.J. Wang, B.L. Su, Engineering 3D bicontinuous hierarchically macro-mesoporous LiFePO4/C nanocomposite for lithium storage with high rate capability and long cycle stability. Sci. Rep. 6, 25942 (2016). doi:10.1038/srep25942
[22] W.K. Kim, W.H. Ryu, D.W. Han, S.J. Lim, J.Y. Eom, H.S. Kwon, Fabrication of graphene embedded LiFePO4 using a catalyst assisted self assembly method as a cathode material for high power lithium-ion batteries. ACS Appl. Mater. Interfaces 6(7), 4731-4736 (2014). doi:10.1021/am405335k
[23] X.H. Tian, Y.K. Zhou, X.F. Tu, Z.T. Zhang, G.D. Du, Well-dispersed LiFePO4 nanoparticles anchored on a three-dimensional graphene aerogel as high-performance positive electrode materials for lithium-ion batteries. J. Power Sources 340, 40-50 (2017). doi:10.1016/j.jpowsour.2016.11.049
[24] P. Simon, Y. Gogotsi, B. Dunn, Where do batteries end and supercapacitors begin. Science 343(6176), 1210-1211 (2014). doi:10.1126/science.1249625
[25] D.L. Li, S.H. Wu, F.F. Wang, S.Y. Jia, Y. Liu, X. Han, L.W. Zhang, S.L. Zhang, Y.M. Wu, A facile one-pot synthesis of hemin/ZIF-8 composite as mimetic peroxidase. Mater. Lett. 178, 48-51 (2016). doi:10.1016/j.matlet.2016.04.200
[26] J. Tang, R.R. Salunkhe, J. Liu, N.L. Torad, M. Imura, S. Furukawa, Y. Yamauchi, Thermal conversion of core-shell metal-organic frameworks: a new method for selectively functionalized nanoporous hybrid carbon. J. Am. Chem. Soc. 137(4), 1572-1580 (2015). doi:10.1021/ja511539a
[27] X.D. Shi, Z.A. Zhang, Y. Fu, Y.Q. Gan, Self-template synthesis of nitrogen-doped porous carbon derived from zeolitic imidazolate framework-8 as an anode for sodium ion batteries. Mater. Lett. 161, 332-335 (2015). doi:10.1016/j.matlet.2015.08.137
[28] N.L. Torad, M. Hu, Y. Kamachi, K. Takai, M. Imura, Facile synthesis of nanoporous carbons with controlled particle sizes by direct carbonization of monodispersed ZIF-8 crystals. Chem. Commun. 49(25), 2521-2523 (2013). doi:10.1039/c3cc38955c
[29] L.J. Zhang, Z.X. Su, F.L. Jiang, L.L. Yang, J.J. Qian, Highly graphitized nitrogen-doped porous carbon nanopolyhedra derived from ZIF-8 nanocrystals as efficient electrocatalysts for oxygen reduction reactions. Nanoscale 6(12), 6590-6602 (2014). doi:10.1039/C4NR00348A
[30] X.Z. Zheng, Y.F. Li, Y.X. Xu, Z.S. Hong, M.D. Wei, Metal-organic frameworks: promising materials for enhancing electrochemical properties of nanostructured Zn2SnO4 anode in Li-ion batteries. CrystEngComm 14(6), 2112-2116 (2012). doi:10.1039/c2ce06350f
[31] G.H. Zhang, S.C. Hou, H. Zhang, W. Zeng, F.L. Yan, C.C. Li, H.G. Duan, High-performance and ultra-stable lithium-ion batteries based on MOF-derived ZnO@ ZnO quantum dots/C core-shell nanorod arrays on a carbon cloth anode. Adv. Mater. 27(14), 2400-2405 (2015). doi:10.1002/adma.201405222
[32] Q.T. Zhang, Foundation of Inorganic Materials Science. East China University of Technology Press, 2007.
[33] X.Y. Du, W. He, X.D. Zhang, J.Y. Ma, C.H. Wang, C.S. Li, Y.Z. Yue, Low temperature biosynthesis of Li2O-MgO-P2O5-TiO2 nanocrystalline glass with mesoporous structure exhibiting fast lithium ion conduction. Mater. Sci. Eng. C 33(3), 1592-1600 (2013). doi:10.1016/j.msec.2012.12.065
[34] W.H. Li, Z.Z. Yang, M.S. Li, Y. Jiang, X. Wei, X.W. Zhong, L. Gu, Y. Yu, Amorphous red phosphorus embedded in highly ordered mesoporous carbon with superior lithium and sodium storage capacity. Nano Lett. 16(3), 1546-1553 (2016). doi:10.1021/acs.nanolett.5b03903
[35] Y. Cui, X.L. Zhao, R.S. Guo, Improved electrochemical performance of La0.7Sr0.3MnO3 and carbon co-coated LiFePO4 synthesized by freeze-drying process. Electrochim. Acta 55(3), 922-926 (2010). doi:10.1016/j.electacta.2009.08.020

Citation Information

XiaoLong Xu, CongYu Qi (co-first author), ZhenDong Hao, Hao Wang, JinTing Jiu, JingBing Liu, Hui Yan, Katsuaki Suganuma, The Surface Coating of Commercial LiFePO4 by Utilizing ZIF-8 for High Electrochemical Performance Lithium Ion Battery. Nano-Micro Lett.(2018) 10: 1. http://dx.doi.org/10.1007/s40820-017-0154-4

History

Received: 28 June 2017 / Accepted: 26 August 2017


Additional Info

  • Type of Publishing: JOUR - Journal
  • Title: The Surface Coating of Commercial LiFePO4 by Utilizing ZIF-8 for High Electrochemical Performance Lithium Ion Battery
  • Author: XiaoLong Xu, CongYu Qi (co-first author), ZhenDong Hao, Hao Wang, JinTing Jiu, JingBing Liu, Hui Yan, Katsuaki Suganuma
  • Year: 2018
  • Volume: 10
  • Issue: 1
  • Journal Name: Nano-Micro Letters
  • ISSN: 2150-5551
  • URL: http://dx.doi.org/10.1007/s40820-017-0154-4
  • Abstract: The requirement of energy storage equipment need to develop the lithium ion battery (LIB) with high electrochemical performance. The surface modification of commercial LiFePO4 (LFP) by utilizing zeolitic imidazolate frameworks-8 (ZIF-8) offers new possibilities for commercial LFP with high electrochemical performances. In this work, the carbonized ZIF-8 (CZIF-8) was coated on the surface of LFP particles by the in-situ growth and carbonization of ZIF-8. Transmission electron microscopy (TEM) indicates that there is an approximate 10 nm coating layer with metal zinc and graphite-like carbon on the surface of LFP/CZIF-8 sample. The N2 adsorption and desorption isotherm suggests that the coating layer has uniform and simple connecting mesopores. As cathode material, LFP/CZIF-8 cathode active material delivers a discharge specific capacity of 159.3 mAh g-1 at 0.1 C and a discharge specific energy of 141.7 mWh g-1 after 200 cycles at 5.0 C (the retention rate is approximate 99%). These results are attributed to the synergy improvement of the conductivity, the lithium ion diffusion coefficient, and the degree of freedom for volume change of LFP/CZIF-8 cathode. This work will contribute to the improvement of the cathode materials of commercial LIB.
  • Publish Date: Saturday, 26 August 2017
  • Start Page: 1
  • DOI: 10.1007/s40820-017-0154-4