14August2018

Nano-Micro Letters

Formamidinium Lead Bromide Perovskite Microcrystals for Sensitive and Fast Photodetectors

View ResearcherID and ORCID

Fengying Zhang1, 2, Bin Yang2, Kaibo Zheng3, Songqiu Yang2, Yajuan Li2, Weiqiao Deng2, *, Rongxing He1, *

Abstract | Support Info
icon-htmlFull Text Html
icon-pdf-smPDF w/ Links
icon-citExport Citation
Figures
+Show more

Nano-Micro Lett. (2018) 10: 43

First Online: 05 March 2018 (Article)

DOI:10.1007/s40820-018-0196-2

*Corresponding author. E-mail: dengwq@dicp.ac.cn; herx@swu.edu.cn

 

Abstract

 


Toc

Because of the good thermal stability and superior carrier transport characteristics of formamidinium lead trihalide perovskite HC(NH2)2PbX3 (FAPbX3), it has been considered to be a better optoelectronic material than conventional CH3NH3PbX3 (MAPbX3). Herein, we fabricated a FAPbBr3 microcrystal-based photodetector that exhibited a good responsivity of 4000 A W−1 and external quantum efficiency up to 106% under one-photon excitation, corresponding to the detectivity greater than 1014 Jones. The responsivity is two orders of magnitude higher than that of previously reported formamidinium (FA) perovskite photodetectors. Furthermore, the FAPbBr3 photodetector’s responsivity to two-photon absorption with an 800-nm excitation source can reach 0.07 A W-1, which is four orders of magnitude higher than that of its MAPbBr3 counterparts. The response time of this photodetector is less than 1 ms. This study provides solid evidence that FAPbBr3 can be an excellent candidate for highly sensitive and fast photodetectors.


 

Keywords

Formamidinium lead trihalide (FAPbBr3); Perovskite Microcrystals; Photodetector; External quantum efficiency

 

Full Text Html

1 Introduction

    In recent years, photoelectric devices have been widely investigated [1-3], especially detectors with different morphologies and sizes, for exploring their mechanisms, simplifying their syntheses, and improving device efficiencies [4-10]. Photodetectors based on hybrid organolead trihalide perovskite CH3NH3PbX3 (MAPbX3, X = Cl, Br, I) have attracted significant attention in the optoelectronic field owing to their strong absorption coefficients (up to 105 cm−1) [11-14], carrier mobilities (2.5–1000 cm2 v−1 s−1) [15-19], long carrier lifetimes (0.08–4.5 μs) [17, 19-21], and diffusion lengths (2–175 μm) [19, 20, 22, 23]. In particular, Saidaminov et al. produced a planar-integrated photodetector using MAPbBr3 single crystals, achieving high-performance light detection in the wide wavelength range [24]. Bao et al. reported low-noise and large-linear-dynamic-range photodetectors based on MAPbBr3 and MAPbI3 [25]. Yang et al. demonstrated the great potential of metal-semiconductor-metal structures for low-cost and high-performance optoelectronic devices [26]. Moreover, Hu et al. reported high-performance and low working-voltage perovskite thin-film photodetectors [27]. Further, a UV-selective photodetector based on MAPbCl3 was also demonstrated [28, 29]. However, conventional MAPbX3 materials have poor stability [30, 31], which severely impedes device development.

     HC(NH2)2PbX3 (FAPbX3), which replaces organic methylammonium cation (MA+) with the larger formamidinium cation (FA+) [32, 33], is much more stable in air because the high Goldschmidt tolerance factor of its lattice (»1) [33-35]. Moreover, previous reports have revealed that FA-substituted compounds (e.g., FAPbX3) showed remarkably improved carrier transmission performance than MAPbX3 in both polycrystalline thin films and monocrystalline phases, including a longer carrier lifetime and lower dark carrier concentration [20, 22, 35-37]. As a result, FAPbBr3 is expected to perform better in photodetectors than MAPbBr3. However, a prototype device based on FAPbBr3 has not been reported yet, except for a two-dimensional (OA)2FAn−1PbnBr3n+1 photodetector with low responsivity [38]. Taking advantage of the high carrier mobility, stability of single crystals and the efficient charge transfer in the micron scale, we synthesized FAPbBr3 microcrystals (MCs) and deposited them as a photodetector. Detailed investigations under single- and two-photon excitation and front- and back-side excitation were performed to reveal the great potential of the fabricated photodetector as an optoelectronic device.

2 Experimental

2.1 Chemicals and Reagents

    Formamidine acetate, lead bromide (PbBr2, >98%), and hydrobromic acid (48 wt% in water) were purchased from Alfa Aesar. Gamma-butyrolactone (GBL) and N, N-dimethylformamide (DMF) were purchased from Kermel. All compounds were used without any further purification.

2.2  Synthesis of CH(NH2)2Br (FABr)

    FABr was synthesized by slowly dropping 10 mL hydrobromic acid into 50 mmol (5.205 g) formamidine acetate in a flask, accompanied by continuous stirring at 0 °C for 2 h under argon atmosphere. The product FABr was formed once the solvent was removed using a rotary evaporator at 70 °C. The crude white powder was dissolved in ethanol and subsequently reprecipitated in diethyl ether. Then, the filtered product was dried at 60 °C in a vacuum oven for 24 h for further use.

2.3 Synthesis of FAPbBr3 MCs

    FAPbBr3 MCs were grown by a modified inverse temperature crystallization method using toluene as the antisolvent. In brief, 5 mmol PbBr2 (1.835 g) and 5 mmol FABr (0.625 g) were dissolved in 10 mL mixed DMF:GBL (1:1 v/v) solvent at 25 °C, and the solution was filtered using nylon filters with a 0.22-μm pore size. Then, 1 mL precursor was diluted in 2 mL DMF and antisolvent toluene was added to obtain a saturated solution. Single-crystals of FAPbBr3 with millimeter dimensions were formed after stirring on a hot plate of 80 °C.

2.4  Device Preparation

    Standard photolithography and hydrochloric acid etching were used to obtain conductive glass substrates with a channel length and width of 5 µm and 1 mm, respectively. After synthesizing FAPbBr3 MCs using the above-described method, the substrates were deposited on these crystals and dried at 160 °C for 10 min.

2.5  Measurements and Characterizations

    Scanning electron microscopy (SEM) was performed using a field-emission scanning electron microscope (JEOL, JSM-7800F, 3 kV). X-ray diffraction (XRD) was performed using an X'pert PRO diffractometer equipped with Cu Kα X-ray (λ = 1.54186 Å) tubes. UV-Vis diffuse reflectance spectra were recorded at room temperature on a JASCO V-550 UV-Vis absorption spectrometer with an integrating sphere operating in 200–900 nm. Photoluminescence (PL) was recorded using a Horiba PTI QuantaMaster 400 system with an excitation of 470 nm. Time-resolved PL decay was obtained on the basis of the time-correlated single-photon counter (TCSPC) technology using a light-emitting diode (LED) to provide a 376-nm excitation beam. The decay data were analyzed using commercial software provided by Horiba. For trap-state density evaluation, one layer of conductive glass (ITO) undertaken the crystal film was used as one electrode. An 800-nm-thick gold (Au) layer deposited on top of the film by thermal evaporation was used as the other electrode. This structure had a rather simple geometry with the sample deposited on ITO and evaporated Au on opposite sides, and the structure should be kept in the dark. Current–voltage measurements were conducted using a Keithley 2400 sourcemeter. For light characterization under one-photon excitation, a monochromatic source (LED, λ = 495 nm) was used. Spectral responsivity (R) was calculated by the photocurrent (Iph) and incident power (Pinc) according to the relation R = Iph/Pinc. For two-photon irradiation, the photocurrent was generated using a femtosecond laser system (Spitfire Pro, SpectraPhysic) with an output wavelength of 800 nm and a repetition rate of 1000 Hz as the light source. 

3 Results and Discussion 

    We synthesized FAPbBr3 MCs using a modified antisolvent-assisted inverse temperature crystallization method [8, 24, 28]. To facilitate the removal of the solvent and form homogeneous crystalline films, 1 M precursor (equimolar FABr and PbBr2 dissolved in a mixed solvent as shown in experimental section) was diluted three times in DMF. The antisolvent toluene was then added to obtain a saturated solution. This saturated solution was stirred at 80 °C to accelerate the nucleation and increase the yield of the interconnected crystals. The mean size of the as-obtained FAPbBr3 MCs was ~10 ± 5 µm, as shown in the top-view SEM image (Fig. 1a). These MCs were interconnected as a continuous film with a thickness of ~150 µm, as shown in Fig. 1b. XRD results shown in Fig. 1c confirmed the cubic phase of the FAPbBr3 MCs [35, 39]. The MCs exhibited an absorption band edge at 570 nm, corresponding to a bandgap of 2.18 eV, as obtained from the Tauc plot of the absorption spectrum (Fig. 1d). The emission peak of the MCs appeared at 567 nm (insets of Fig. 1d), which was consistent with previous results [33, 37, 40]. Additionally, PL decay was measured using the TCSPC technology (Fig. 1e), and a fast component (τ1, 15 ± 1 ns) and slow decay (τ2, 282 ± 5 ns) reflected the surface and bulk carrier lifetimes of the FAPbBr3 MCs, respectively. We also conducted dark current measurements to estimate the trap-state density of the FAPbBr3 MC film, as depicted in Fig. 1f. Here, the trap-state density was calculated to be 6.98 × 1011 cm−3 according to Eq. 1:

10 3 43 gs1

where VTFL is the voltage at which trap states are fully filled by injected carriers, q and L represent the elemental charge and film thickness, respectively, ɛ0 and ɛ denote the vacuum permittivity and dielectric constant of FAPbBr3, with ɛ = 43.6 [37]. The relatively fewer defects contributed to the formation of a high-quality film, thus promoting their application in photoelectronic devices [37, 41].

Fig. 1 a Top-view and b cross-sectional SEM images. c XRD pattern d Steady-state absorption spectrum of FAPbBr3 MCs film. Left insets: the optical bandgap extracted from Tauc plot; right insets: PL spectrum. e PL decay of the sample excited at 376 nm, which could be well fitted by biexponential functions. f Current–voltage responses of FAPbBr3 MCs

Fig. 1 a Top-view and b cross-sectional SEM images. c XRD pattern d Steady-state absorption spectrum of FAPbBr3 MCs film. Left insets: the optical bandgap extracted from Tauc plot; right insets: PL spectrum. e PL decay of the sample excited at 376 nm, which could be well fitted by biexponential functions. f Current–voltage responses of FAPbBr3 MCs

    In the next step, FAPbBr3 MCs were directly deposited on interdigitated ITO substrates to form the prototype photodetector device. The length and width of the gaps between neighboring digits were 5 µm and 1 mm, respectively, as shown in Fig. S1. FAPbBr3 MCs covered the entire active area, forming Schottky barriers due to contact with the ITO electrode. Once a voltage was applied to the detector device, ion migration and carrier trapping occurred in the active layer and at the electrode/perovskite interfaces, respectively. This indicated that an Ohmic contact between the FAPbBr3 MCs and the ITO electrode was formed. The cathode collected abundant photogenerated holes, while holes from the anode were injected into the active layer, showing the photoconductivity of the device [42-44]. The compact morphology of the MCs minimized the grain boundary and consequently diminished interfacial charge recombination. As shown in Fig. 2a, the photocurrent drastically increased with increasing excitation light intensity. In addition, the small dark current of the device (seen in Fig. S2) indicated the low carrier concentration of FAPbBr3 MCs [37]. The photoresponse was also reproducible under a periodic excitation of the light pulse, as demonstrated in Fig. S3.

Fig. 2 a Current–voltage characteristics measured under back-side excitation with varying light intensity. b Responsivity and corresponding current as a function of incident light power under back-side illumination. The detector was biased at 5 V. c EQE and detectivity under different light illuminations. d Response time measured by a monochromatic source of 495 nm under back-side illumination and rise time and fall time

Fig. 2 a Current–voltage characteristics measured under back-side excitation with varying light intensity. b Responsivity and corresponding current as a function of incident light power under back-side illumination. The detector was biased at 5 V. c EQE and detectivity under different light illuminations. d Response time measured by a monochromatic source of 495 nm under back-side illumination and rise time and fall time

    As shown in Fig. 2b, the photocurrent increased linearly with the incident power and the corresponding responsivity (R, defined as photocurrent/the incident light power) linearly decreased. The responsivity was 4000 A W−1 at 5 V (λ = 495 nm, probe intensity = 10 nW cm−2), which was two orders of magnitude higher than that of other FA-based perovskite photodetectors [7, 38, 45, 46]. Furthermore, the external quantum efficiency (EQE) calculated by Eq. 2 was as high as 1.05 × 106% (Fig. 2c):

10 3 43 gs2

    In addition, the detectivity D* of the device was 3.87 × 1014 Jones, as obtained from Eq. 3:

10 3 43 gs3

    This value of D* was higher than that of state-of-art MAPbI3 photodetectors (~1013 Jones) [46]. Moreover, the FAPbBr3 MC photodetector exhibited a rapid response with a rise time (τrise) of 0.67 ms and fall time (τfall) of 0.75 ms (Figs. 2d and S4), where τrise and τfall are defined as the time required for light response from 10% to 90% in the rising stage and from 90% to 10% in the falling stage, respectively.

Fig. 3 a Spectral-dependent photocurrent under front-side and back-side excitation at 1 mW cm−2 and a bias voltage of 5 V. b Photocurrent response measured using a series of bias voltages: 2, 3, 4, and 5 V, at an excitation of 495 nm. Normalized spectral-dependent photocurrent under different bias voltages under c back-side and d front-side excitation

Fig. 3 a Spectral-dependent photocurrent under front-side and back-side excitation at 1 mW cm−2 and a bias voltage of 5 V. b Photocurrent response measured using a series of bias voltages: 2, 3, 4, and 5 V, at an excitation of 495 nm. Normalized spectral-dependent photocurrent under different bias voltages under c back-side and d front-side excitation

    Previous research has revealed that the photoresponse to the excitation wavelength is different for front-side excitation and back-side excitation [46]. In back-side excitation, charge carriers are efficiently collected in the vicinity of the electrodes. However, in front-side excitation, it is more difficult for charge carriers generated by short-wavelength photons to penetrate the thick film to electrodes than that of long-wavelength photons with energy comparable to the bandgap [46]. In our case, the wavelength-dependent light response using front-side excitation resembled that using back-side excitation, indicating that our device was a broadband photodetector (Figs. 3a and S5). It was found that the thickness of the FAPbBr3 microcrystalline film of about 150 µm allowed most photons to be transmitted through the film to generate corresponding photocurrents. Once the film became sufficiently thick (>200 µm), it blocked the short-wavelength photons to the microcrystalline film to form a narrowband photodetector, which was also confirmed by Saidaminov and coworkers [46]. In addition, the generally lower photocurrent for front-side excitation could be attributed to the insufficient diffusion length of the photo-generated charges for the given film thickness, which hindered charge transportation to the bottom electrode [46]. Figure 3b shows the photocurrent variation for different bias voltages. As shown Figs. 3c, d, when the bias voltage was decreased, the photocurrents of the photons excited far above the absorption band edge degraded more.

Fig. 4 a Schematic showing two-photon absorption of 800 nm light and up-conversion to 567 nm PL. b Photocurrent and c responsivity dependence at an input light intensity of 800 nm and a bias of 5 V. d Fall time measured using pulsed light of 800 nm

Fig. 4 a Schematic showing two-photon absorption of 800 nm light and up-conversion to 567 nm PL. b Photocurrent and c responsivity dependence at an input light intensity of 800 nm and a bias of 5 V. d Fall time measured using pulsed light of 800 nm

    Perovskites have also attracted considerable attention as nonlinear semiconductor absorbers for optical limiting [47], ultrafast optical signal characterization [48], microscopy [49], and lithography [50]. Therefore, we characterized our device under two-photon excitation, where the photocurrent was generated by an 800-nm pulse laser with a photon energy much smaller than the bandgap of FAPbBr3 (2.18 eV). Figure 4a shows the PL mechanism of FAPbBr3 at 567 nm obtained under 800-nm two-photon absorption. Under 800-nm back-side illumination at a fixed bias of 5 V, the tendency of light current variation with respect to voltage (30–110 mW cm−2) is provided in Fig. 4b. Under ideal conditions, the photocurrent generated by two-photon absorption showed a square (n = 2) dependence on the input intensity [51]. However, our tested photocurrents (with 1 n 2 exhibited highly dependent on incidet power,  which was mainly attributed to the effect of trap-state’s sub-gap absorption [8, 52]. This tendency was consistent with that reported for near-infrared CsPbBr3 and MAPbBr3 photodetectors [8, 51]. Consequently, the responsivity of the two-photon pumped FAPbBr3 MC detector increased with increasing input intensity in the linear excitation region (Fig. 4c). The largest responsivity under 800-nm excitation (0.07 A W−1) was much higher than that previously reported for MAPbBr3 single crystals [51]. The fast response of our detector under two-photon excitation with a fast fall time (0.72 ms) was also shown in Fig. 4d. The result is similar to that observed under one-photon excitation (0.75 ms). The rapid pulse light with periodic changes was responsible for the missing rising stage.

    Moreover, the amplified spontaneous emission (ASE) behavior of the FAPbBr3 microcrystalline film was measured using 800-nm laser pulses with tunable intensities. The emission spectra (Fig. S6) with increasing light intensity exhibited an ASE threshold of 1.75 mJ cm−2, which was similar to the reported two-photon ASE threshold of MAPbBr3 photodetectors (2.2 mJ cm−2) [53].

4 Conclusion

    In summary, organolead trihalide perovskite FAPbBr3 MCs were synthesized and then deposited as a photodetector. The photodetector exhibited a good responsivity of up to 4000 A W−1 under back-side one-photon excitation with an EQE and detectivity of up to 1.05 × 106% and 3.87 × 1014 Jones, respectively. Besides, the two-photon responsivity under 800-nm excitation was 0.07 A W−1, which was four orders of magnitude higher than that reported for MAPbBr3 single crystals (10−6 A W−1). This deposited FAPbBr3 microcrystalline photodetector showed great potential for developing fast and sensitive photodetectors.

Acknowledgments

    We would like to acknowledge all funding sources, including grant numbers and funding agencies. We are grateful to the National Key R@D Program of China (Grant 2017YFA0204800) and the National Natural Science Foundation of China (Grant No: 21533010, 21321091, 21525315, 91333116 and 21173169) for their financial supports.

References

[1] W. Zhao, X. Xiong, Y. Han, L. Wen, Z. Zou et al., Fe-doped p-ZnO nanostructures/n-gan heterojunction for “blue-free” orange light-emitting diodes. Adv. Opt. Mater. 5(17), 1700146 (2017). https://doi.org/10.1002/adom.201700146
[2] G. Li, Z.K. Tan, D. Di, M.L. Lai, L. Jiang, J.H. Lim, R.H. Friend, N.C. Greenham. Efficient light-emitting diodes based on nanocrystalline perovskite in a dielectric polymer matrix. Nano Lett. 15(4), 2640-2644 (2015). https://doi.org/10.1021/acs.nanolett.5b00235
[3] W.S. Yang, J.H. Noh, N.J. Jeon, Y.C. Kim, S. Ryu, J. Seo, S.I. Seok, High-performance photovoltaic perovskite layers fabricated through intermolecular exchange. Science 348, 1234-1237 (2015). https://doi.org/10.1126/science.aaa9272
[4] Y. Wang, Y. Chen, W. Zhao, L. Ding, L. Wen et al., A self-powered fast-response ultraviolet detector of p-n homojunction assembled from two ZnO-based nanowires. Nano-Micro Lett. 9, 11 (2016). https://doi.org/10.1007/s40820-016-0112-6
[5] Z. Kang, Y. Ma, X. Tan, M. Zhu, Z. Zheng et al., MXene-silicon van der waals heterostructures for high-speed self-driven photodetectors. Adv. Electron. Mater. 3(9), 1700165 (2017). https://doi.org/10.1002/aelm.201700165
[6] X. Zhang, X. Han, J. Su, Q. Zhang, Y. Gao, Well vertically aligned ZnO nanowire arrays with an ultra-fast recovery time for UV photodetector. Appl. Phys. A 107(2), 255-260 (2012). https://doi.org/10.1007/s00339-012-6886-6
[7] S. Li, S. Tong, J. Yang, H. Xia, C. Zhang et al., High-performance formamidinium-based perovskite photodetectors fabricated via doctor-blading deposition in ambient condition. Org. Electron. 47, 102-107 (2017). https://doi.org/10.1016/j.orgel.2017.05.010
[8] B. Yang, F. Zhang, J. Chen, S. Yang, X. Xia, T. Pullerits, W. Deng, K. Han, Ultrasensitive and fast all-inorganic perovskite-based photodetector via fast carrier diffusion. Adv. Mater. 29, 1703758 (2017). https://doi.org/10.1002/adma.201703758
[9] X. Zhang, S. Yang, H. Zhou, J. Liang, H. Liu et al., Perovskite-erbium silicate nanosheet hybrid waveguide photodetectors at the near-infrared telecommunication band. Adv. Mater. 29(21), 1604431 (2017). https://doi.org/10.1002/adma.201604431
[10] D. Dong, H. Deng, C. Hu, H. Song, K. Qiao et al., Bandgap tunable Csx(CH3NH3)1-xPbI3 perovskite nanowires by aqueous solution synthesis for optoelectronic devices. Nanoscale 9(4), 1567-1574 (2017). https://doi.org/10.1039/C6NR06636D
[11] Q. Chen, N. De Marco, Y.M. Yang, T.B. Song, C.C. Chen, H. Zhao, Z. Hong, H. Zhou, Y. Yang, Under the spotlight: The organic-inorganic hybrid halide perovskite for optoelectronic applications. Nano Today 10(3), 355-396 (2015). https://doi.org/10.1016/j.nantod.2015.04.009
[12] J. Zhang, X. Yang, H. Deng, K. Qiao, U. Farooq et al., Low-dimensional halide perovskites and their advanced optoelectronic applications. Nano-Micro Lett. 9(3), 36 (2017). https://doi.org/10.1007/s40820-017-0137-5
[13] J.S. Manser, J.A. Christians, P.V. Kamat, Intriguing optoelectronic properties of metal halide perovskites. Chem. Rev. 116(21), 12956-13008 (2016). https://doi.org/10.1021/acs.chemrev.6b00136
[14] M.A. Green, A. Ho-Baillie, H.J. Snaith, The emergence of perovskite solar cells. Nat. Photonics 8(7), 506-514 (2014). https://doi.org/10.1038/nphoton.2014.134
[15] G. Xing, N. Mathews, S. Sun, S.S. Lim, Y.M. Lam, M. Grätzel, S. Mhaisalkar, T.C. Sum, Long-range balanced electron-and hole-transport lengths in organic-inorganic CH3NH3PbI3. Science 342(6156), 344-347 (2013). https://doi.org/10.1126/science.1243167
[16] W. Zhang, M. Saliba, D.T. Moore, S.K. Pathak, M.T. Hörantner et al., Ultrasmooth organic-inorganic perovskite thin-film formation and crystallization for efficient planar heterojunction solar cells. Nat. Commun. 6, 6142 (2015). https://doi.org/10.1038/ncomms7142
[17] C. Wehrenfennig, G.E. Eperon, M.B. Johnston, H.J. Snaith, L.M. Herz, High charge carrier mobilities and lifetimes in organolead trihalide perovskites. Adv. Mater. 26(10), 1584-1589 (2014). https://doi.org/10.1002/adma.201305172
[18] D. A. Valverde-Chávez, C.S. Ponseca, C.C. Stoumpos, A. Yartsev, M.G. Kanatzidis, V. Sundström, D.G. Cooke, Intrinsic femtosecond charge generation dynamics in single crystal CH3NH3PbI3. Energy Environ. Sci. 8(12), 3700-3707 (2015). https://doi.org/10.1039/C5EE02503F
[19] D.N. Dirin, I. Cherniukh, S. Yakunin, Y. Shynkarenko, M.V. Kovalenko, Solution-grown CsPbBr3 perovskite single crystals for photon detection. Chem. Mater. 28(23), 8470-8474 (2016). https://doi.org/10.1021/acs.chemmater.6b04298
[20] D. Shi, V. Adinolfi, R. Comin, M. Yuan, E. Alarousu et al., Low trap-state density and long carrier diffusion in organolead trihalide perovskite single crystals. Science 347(6221), 519-522 (2015). https://doi.org/10.1126/science.aaa2725
[21] M.I. Saidaminov, A.L. Abdelhady, B. Murali, E. Alarousu, V.M. Burlakov et al., High-quality bulk hybrid perovskite single crystals within minutes by inverse temperature crystallization. Nat. Commun. 6, 7586 (2015). https://doi.org/10.1038/ncomms8586
[22] Q. Dong, Y. Fang, Y. Shao, P. Mulligan, J. Qiu, L. Cao, J. Huang, Electron-hole diffusion lengths > 175 μm in solution-grown CH3NH3PbI3 single crystals. Science 347(6225), 967-970 (2015). https://doi.org/10.1126/science.aaa5760
[23] S.D. Stranks, G.E. Eperon, G. Grancini, C. Menelaou, M.J. Alcocer, T. Leijtens, L.M. Herz, A. Petrozza, H.J. Snaith, Electron-hole diffusion lengths exceeding 1 micrometer in an organometal trihalide perovskite absorber. Science 342(6156), 341-344 (2013). https://doi.org/10.1126/science.1243982
[24] M.I. Saidaminov, V. Adinolfi, R. Comin, A.L. Abdelhady, W. Peng et al., Planar-integrated single-crystalline perovskite photodetectors. Nat. Commun. 6, 8724 (2015). https://doi.org/10.1038/ncomms9724
[25] C. Bao, Z. Chen, Y. Fang, H. Wei, Y. Deng, X. Xiao, L. Li, J. Huang, Low-noise and large-linear-dynamic-range photodetectors based on hybrid-perovskite thin-single-crystals. Adv. Mater. 29(39), 1703209 (2017). https://doi.org/10.1002/adma.201703209
[26] J. Yang, T. Yu, K. Zhu, Q. Xu, High-gain and fast-response metal-semiconductor-metal structured organolead halide perovskite photodetectors. J. Phys. D Appl. Phys. 50(49), 495102 (2017). https://doi.org/10.1088/1361-6463/aa918c
[27] W. Hu, R. Wu, S. Yang, P. Fan, J. Yang, A. Pan, Solvent-induced crystallization for hybrid perovskite thin-film photodetector with high-performance and low working voltage. J. Phys. D Appl. Phys. 50(37), 375101 (2017). https://doi.org/10.1088/1361-6463/aa8059
[28] V. Adinolfi, O. Ouellette, M.I. Saidaminov, G. Walters, A.L. Abdelhady, O.M. Bakr, E.H. Sargent, Fast and sensitive solution-processed visible-blind perovskite uv photodetectors. Adv. Mater. 28(33), 7264-7268 (2016). https://doi.org/10.1002/adma.201601196
[29] G. Maculan, A.D. Sheikh, A.L. Abdelhady, M.I. Saidaminov, M.A. Haque et al., CH3NH3PbCl3 single crystals: Inverse temperature crystallization and visible-blind uv-photodetector. J. Phys. Chem. Lett. 6(19), 3781-3786 (2015). https://doi.org/10.1021/acs.jpclett.5b01666
[30] T.B. Song, Q. Chen, H. Zhou, C. Jiang, H.H. Wang, Y.M. Yang, Y. Liu, J. You, Y. Yang, Perovskite solar cells: Film formation and properties. J. Mater. Chem. A 3(17), 9032-9050 (2015). https://doi.org/10.1039/C4TA05246C
[31] X. Li, M.I. Dar, C. Yi, J. Luo, M. Tschumi, S.M. Zakeeruddin, M.K. Nazeeruddin, H. Han, M. Grätzel, Improved performance and stability of perovskite solar cells by crystal crosslinking with alkylphosphonic acid ω-ammonium chlorides. Nat. Chem. 7(9), 703-711 (2015). https://doi.org/10.1038/nchem.2324
[32] T.M. Koh, K. Fu, Y. Fang, S. Chen, T. Sum, N. Mathews, S.G. Mhaisalkar, P.P. Boix, T. Baikie, Formamidinium-containing metal-halide: An alternative material for near-IR absorption perovskite solar cells. J. Phys. Chem. C 118(30), 16458-16462 (2013). https://doi.org/10.1021/jp411112k
[33] G.E. Eperon, S.D. Stranks, C. Menelaou, M.B. Johnston, L.M. Herz, H.J. Snaith, Formamidinium lead trihalide: A broadly tunable perovskite for efficient planar heterojunction solar cells. Energy Environ. Sci. 7(3), 982-988 (2014). https://doi.org/10.1039/C3EE43822H
[34] T.J. Jacobsson, J.P. Correa-Baena, M. Pazoki, M. Saliba, K. Schenk, M. Grätzel, A. Hagfeldt, Exploration of the compositional space for mixed lead halogen perovskites for high efficiency solar cells. Energy Environ. Sci. 9(5), 1706-1724 (2016). https://doi.org/10.1039/C6EE00030D
[35] F.C. Hanusch, E. Wiesenmayer, E. Mankel, A. Binek, P. Angloher et al., Efficient planar heterojunction perovskite solar cells based on formamidinium lead bromide. J. Phys. Chem. Lett. 5(16), 2791-2795 (2014). https://doi.org/10.1021/jz501237m
[36] N. Pellet, P. Gao, G. Gregori, T.Y. Yang, M.K. Nazeeruddin, J. Maier, M. Grätzel, Mixed-organic-cation perovskite photovoltaics for enhanced solar-light harvesting. Angew. Chem. Int. Edit. 53(12), 3151-3157 (2014). https://doi.org/10.1002/anie.201309361
[37] A.A. Zhumekenov, M.I. Saidaminov, M.A. Haque, E. Alarousu, S.P. Sarmah et al., Formamidinium lead halide perovskite crystals with unprecedented long carrier dynamics and diffusion length. ACS Energy Lett. 1(1), 32-37 (2016). https://doi.org/10.1021/acsenergylett.6b00002
[38] D. Yu, F. Cao, Y. Shen, X. Liu, Y. Zhu, H. Zeng, Dimensionality and interface engineering of 2d homologous perovskites for boosted charge-carrier transport and photodetection performances. J. Phys. Chem. Lett. 8(12), 2565-2572 (2017). https://doi.org/10.1021/acs.jpclett.7b00993 
[39] M.I. Saidaminov, A.L. Abdelhady, G. Maculan, O.M. Bakr, Retrograde solubility of formamidinium and methylammonium lead halide perovskites enabling rapid single crystal growth. Chem. Commun. 51(100), 17658-17661 (2015). https://doi.org/10.1039/C5CC06916E
[40] N. Arora, M.I. Dar, M. Hezam, W. Tress, G. Jacopin et al., Photovoltaic and amplified spontaneous emission studies of high-quality formamidinium lead bromide perovskite films. Adv. Funct. Mater. 26(17), 2846-2854 (2016). https://doi.org/10.1002/adfm.201504977
[41] Q. Han, S.H. Bae, P. Sun, Y.T. Hsieh, Y.M. Yang et al., Single crystal formamidinium lead iodide (FAPbI3): Insight into the structural, optical, and electrical properties. Adv. Mater. 28(11), 2253-2258 (2016). https://doi.org/10.1002/adma.201505002
[42] R. Dong, Y. Fang, J. Chae, J. Dai, Z. Xiao et al., High-gain and low-driving-voltage photodetectors based on organolead triiodide perovskites. Adv. Mater. 27(11), 1912-1918 (2015). https://doi.org/10.1002/adma.201405116
[43] W. Hu, W. Huang, S. Yang, X. Wang, Z. Jiang et al., High-performance flexible photodetectors based on high-quality perovskite thin films by a vapor-solution method. Adv. Mater. 29(43), 1703256 (2017). https://doi.org/10.1002/adma.201703256
[44] M. Ahmadi, T. Wu, B. Hu, A review on organic-inorganic halide perovskite photodetectors: device engineering and fundamental physics. Adv. Mater. 29(41), 1605242 (2017). https://doi.org/10.1002/adma.201605242
[45] Y. Liu, J. Sun, Z. Yang, D. Yang, X. Ren, H. Xu, Z. Yang, S.F. Liu, 20-mm-large single-crystalline formamidinium-perovskite wafer for mass production of integrated photodetectors. Adv. Opt. Mater. 4(11), 1829-1837 (2016). https://doi.org/10.1002/adom.201600327
[46] M.I. Saidaminov, M. Haque, M. Savoie, A.L. Abdelhady, N. Cho et al., Perovskite photodetectors operating in both narrowband and broadband regimes. Adv. Mater. 28(37), 8144-8149 (2016). https://doi.org/10.1002/adma.201601235
[47] V. Liberman, M. Rothschild, O. Bakr, F. Stellacci, Optical limiting with complex plasmonic nanoparticles. J. Opt. 12(6), 065001 (2010). https://doi.org/10.1088/2040-8978/12/6/065001
[48] E. Chong, T. Watson, F. Festy, Autocorrelation measurement of femtosecond laser pulses based on two-photon absorption in gap photodiode. Appl. Phys. Lett. 105(6), 062111 (2014). https://doi.org/10.1063/1.4893423
[49] W.R. Zipfel, R.M. Williams, Nonlinear magic: Multiphoton microscopy in the biosciences. Nat. Biotechnol. 21(11), 1369-1377 (2003). https://doi.org/10.1038/nbt899
[50] W. Haske, V.W. Chen, J.M. Hales, W. Dong, S. Barlow, S.R. Marder, J.W. Perry, 65 nm feature sizes using visible wavelength 3-D multiphoton lithography. Opt. Express 15(6), 3426-3436 (2007). https://doi.org/10.1364/OE.15.003426
[51] G. Walters, B.R. Sutherland, S. Hoogland, D. Shi, R. Comin, D.P. Sellan, O.M. Bakr, E.H. Sargent, Two-photon absorption in organometallic bromide perovskites. ACS Nano 9(9), 9340-9346 (2015). https://doi.org/10.1021/acsnano.5b03308
[52] Q. Lin, A. Armin, P.L. Burn, P. Meredith, Near infrared photodetectors based on sub-gap absorption in organohalide perovskite single crystals. Laser Photonics Rev. 10(6), 1047-1053 (2016). https://doi.org/10.1002/lpor.201600215
[53] B. Yang, X. Mao, S. Yang, Y. Li, Y. Wang, M. Wang, W. Deng, K. Han, Low threshold two-photon-pumped amplified spontaneous emission in CH3NH3PbBr3 microdisks. ACS Appl. Mater. Interfaces 8(30), 19587-19592 (2016). https://doi.org/10.1021/acsami.6b04246

References

[1] W. Zhao, X. Xiong, Y. Han, L. Wen, Z. Zou et al., Fe-doped p-ZnO nanostructures/n-gan heterojunction for “blue-free” orange light-emitting diodes. Adv. Opt. Mater. 5(17), 1700146 (2017). https://doi.org/10.1002/adom.201700146
[2] G. Li, Z.K. Tan, D. Di, M.L. Lai, L. Jiang, J.H. Lim, R.H. Friend, N.C. Greenham. Efficient light-emitting diodes based on nanocrystalline perovskite in a dielectric polymer matrix. Nano Lett. 15(4), 2640-2644 (2015). https://doi.org/10.1021/acs.nanolett.5b00235
[3] W.S. Yang, J.H. Noh, N.J. Jeon, Y.C. Kim, S. Ryu, J. Seo, S.I. Seok, High-performance photovoltaic perovskite layers fabricated through intermolecular exchange. Science 348, 1234-1237 (2015). https://doi.org/10.1126/science.aaa9272
[4] Y. Wang, Y. Chen, W. Zhao, L. Ding, L. Wen et al., A self-powered fast-response ultraviolet detector of p-n homojunction assembled from two ZnO-based nanowires. Nano-Micro Lett. 9, 11 (2016). https://doi.org/10.1007/s40820-016-0112-6
[5] Z. Kang, Y. Ma, X. Tan, M. Zhu, Z. Zheng et al., MXene-silicon van der waals heterostructures for high-speed self-driven photodetectors. Adv. Electron. Mater. 3(9), 1700165 (2017). https://doi.org/10.1002/aelm.201700165
[6] X. Zhang, X. Han, J. Su, Q. Zhang, Y. Gao, Well vertically aligned ZnO nanowire arrays with an ultra-fast recovery time for UV photodetector. Appl. Phys. A 107(2), 255-260 (2012). https://doi.org/10.1007/s00339-012-6886-6
[7] S. Li, S. Tong, J. Yang, H. Xia, C. Zhang et al., High-performance formamidinium-based perovskite photodetectors fabricated via doctor-blading deposition in ambient condition. Org. Electron. 47, 102-107 (2017). https://doi.org/10.1016/j.orgel.2017.05.010
[8] B. Yang, F. Zhang, J. Chen, S. Yang, X. Xia, T. Pullerits, W. Deng, K. Han, Ultrasensitive and fast all-inorganic perovskite-based photodetector via fast carrier diffusion. Adv. Mater. 29, 1703758 (2017). https://doi.org/10.1002/adma.201703758
[9] X. Zhang, S. Yang, H. Zhou, J. Liang, H. Liu et al., Perovskite-erbium silicate nanosheet hybrid waveguide photodetectors at the near-infrared telecommunication band. Adv. Mater. 29(21), 1604431 (2017). https://doi.org/10.1002/adma.201604431
[10] D. Dong, H. Deng, C. Hu, H. Song, K. Qiao et al., Bandgap tunable Csx(CH3NH3)1-xPbI3 perovskite nanowires by aqueous solution synthesis for optoelectronic devices. Nanoscale 9(4), 1567-1574 (2017). https://doi.org/10.1039/C6NR06636D
[11] Q. Chen, N. De Marco, Y.M. Yang, T.B. Song, C.C. Chen, H. Zhao, Z. Hong, H. Zhou, Y. Yang, Under the spotlight: The organic-inorganic hybrid halide perovskite for optoelectronic applications. Nano Today 10(3), 355-396 (2015). https://doi.org/10.1016/j.nantod.2015.04.009
[12] J. Zhang, X. Yang, H. Deng, K. Qiao, U. Farooq et al., Low-dimensional halide perovskites and their advanced optoelectronic applications. Nano-Micro Lett. 9(3), 36 (2017). https://doi.org/10.1007/s40820-017-0137-5
[13] J.S. Manser, J.A. Christians, P.V. Kamat, Intriguing optoelectronic properties of metal halide perovskites. Chem. Rev. 116(21), 12956-13008 (2016). https://doi.org/10.1021/acs.chemrev.6b00136
[14] M.A. Green, A. Ho-Baillie, H.J. Snaith, The emergence of perovskite solar cells. Nat. Photonics 8(7), 506-514 (2014). https://doi.org/10.1038/nphoton.2014.134
[15] G. Xing, N. Mathews, S. Sun, S.S. Lim, Y.M. Lam, M. Grätzel, S. Mhaisalkar, T.C. Sum, Long-range balanced electron-and hole-transport lengths in organic-inorganic CH3NH3PbI3. Science 342(6156), 344-347 (2013). https://doi.org/10.1126/science.1243167
[16] W. Zhang, M. Saliba, D.T. Moore, S.K. Pathak, M.T. Hörantner et al., Ultrasmooth organic-inorganic perovskite thin-film formation and crystallization for efficient planar heterojunction solar cells. Nat. Commun. 6, 6142 (2015). https://doi.org/10.1038/ncomms7142
[17] C. Wehrenfennig, G.E. Eperon, M.B. Johnston, H.J. Snaith, L.M. Herz, High charge carrier mobilities and lifetimes in organolead trihalide perovskites. Adv. Mater. 26(10), 1584-1589 (2014). https://doi.org/10.1002/adma.201305172
[18] D. A. Valverde-Chávez, C.S. Ponseca, C.C. Stoumpos, A. Yartsev, M.G. Kanatzidis, V. Sundström, D.G. Cooke, Intrinsic femtosecond charge generation dynamics in single crystal CH3NH3PbI3. Energy Environ. Sci. 8(12), 3700-3707 (2015). https://doi.org/10.1039/C5EE02503F
[19] D.N. Dirin, I. Cherniukh, S. Yakunin, Y. Shynkarenko, M.V. Kovalenko, Solution-grown CsPbBr3 perovskite single crystals for photon detection. Chem. Mater. 28(23), 8470-8474 (2016). https://doi.org/10.1021/acs.chemmater.6b04298
[20] D. Shi, V. Adinolfi, R. Comin, M. Yuan, E. Alarousu et al., Low trap-state density and long carrier diffusion in organolead trihalide perovskite single crystals. Science 347(6221), 519-522 (2015). https://doi.org/10.1126/science.aaa2725
[21] M.I. Saidaminov, A.L. Abdelhady, B. Murali, E. Alarousu, V.M. Burlakov et al., High-quality bulk hybrid perovskite single crystals within minutes by inverse temperature crystallization. Nat. Commun. 6, 7586 (2015). https://doi.org/10.1038/ncomms8586
[22] Q. Dong, Y. Fang, Y. Shao, P. Mulligan, J. Qiu, L. Cao, J. Huang, Electron-hole diffusion lengths > 175 μm in solution-grown CH3NH3PbI3 single crystals. Science 347(6225), 967-970 (2015). https://doi.org/10.1126/science.aaa5760
[23] S.D. Stranks, G.E. Eperon, G. Grancini, C. Menelaou, M.J. Alcocer, T. Leijtens, L.M. Herz, A. Petrozza, H.J. Snaith, Electron-hole diffusion lengths exceeding 1 micrometer in an organometal trihalide perovskite absorber. Science 342(6156), 341-344 (2013). https://doi.org/10.1126/science.1243982
[24] M.I. Saidaminov, V. Adinolfi, R. Comin, A.L. Abdelhady, W. Peng et al., Planar-integrated single-crystalline perovskite photodetectors. Nat. Commun. 6, 8724 (2015). https://doi.org/10.1038/ncomms9724
[25] C. Bao, Z. Chen, Y. Fang, H. Wei, Y. Deng, X. Xiao, L. Li, J. Huang, Low-noise and large-linear-dynamic-range photodetectors based on hybrid-perovskite thin-single-crystals. Adv. Mater. 29(39), 1703209 (2017). https://doi.org/10.1002/adma.201703209
[26] J. Yang, T. Yu, K. Zhu, Q. Xu, High-gain and fast-response metal-semiconductor-metal structured organolead halide perovskite photodetectors. J. Phys. D Appl. Phys. 50(49), 495102 (2017). https://doi.org/10.1088/1361-6463/aa918c
[27] W. Hu, R. Wu, S. Yang, P. Fan, J. Yang, A. Pan, Solvent-induced crystallization for hybrid perovskite thin-film photodetector with high-performance and low working voltage. J. Phys. D Appl. Phys. 50(37), 375101 (2017). https://doi.org/10.1088/1361-6463/aa8059
[28] V. Adinolfi, O. Ouellette, M.I. Saidaminov, G. Walters, A.L. Abdelhady, O.M. Bakr, E.H. Sargent, Fast and sensitive solution-processed visible-blind perovskite uv photodetectors. Adv. Mater. 28(33), 7264-7268 (2016). https://doi.org/10.1002/adma.201601196
[29] G. Maculan, A.D. Sheikh, A.L. Abdelhady, M.I. Saidaminov, M.A. Haque et al., CH3NH3PbCl3 single crystals: Inverse temperature crystallization and visible-blind uv-photodetector. J. Phys. Chem. Lett. 6(19), 3781-3786 (2015). https://doi.org/10.1021/acs.jpclett.5b01666
[30] T.B. Song, Q. Chen, H. Zhou, C. Jiang, H.H. Wang, Y.M. Yang, Y. Liu, J. You, Y. Yang, Perovskite solar cells: Film formation and properties. J. Mater. Chem. A 3(17), 9032-9050 (2015). https://doi.org/10.1039/C4TA05246C
[31] X. Li, M.I. Dar, C. Yi, J. Luo, M. Tschumi, S.M. Zakeeruddin, M.K. Nazeeruddin, H. Han, M. Grätzel, Improved performance and stability of perovskite solar cells by crystal crosslinking with alkylphosphonic acid ω-ammonium chlorides. Nat. Chem. 7(9), 703-711 (2015). https://doi.org/10.1038/nchem.2324
[32] T.M. Koh, K. Fu, Y. Fang, S. Chen, T. Sum, N. Mathews, S.G. Mhaisalkar, P.P. Boix, T. Baikie, Formamidinium-containing metal-halide: An alternative material for near-IR absorption perovskite solar cells. J. Phys. Chem. C 118(30), 16458-16462 (2013). https://doi.org/10.1021/jp411112k
[33] G.E. Eperon, S.D. Stranks, C. Menelaou, M.B. Johnston, L.M. Herz, H.J. Snaith, Formamidinium lead trihalide: A broadly tunable perovskite for efficient planar heterojunction solar cells. Energy Environ. Sci. 7(3), 982-988 (2014). https://doi.org/10.1039/C3EE43822H
[34] T.J. Jacobsson, J.P. Correa-Baena, M. Pazoki, M. Saliba, K. Schenk, M. Grätzel, A. Hagfeldt, Exploration of the compositional space for mixed lead halogen perovskites for high efficiency solar cells. Energy Environ. Sci. 9(5), 1706-1724 (2016). https://doi.org/10.1039/C6EE00030D
[35] F.C. Hanusch, E. Wiesenmayer, E. Mankel, A. Binek, P. Angloher et al., Efficient planar heterojunction perovskite solar cells based on formamidinium lead bromide. J. Phys. Chem. Lett. 5(16), 2791-2795 (2014). https://doi.org/10.1021/jz501237m
[36] N. Pellet, P. Gao, G. Gregori, T.Y. Yang, M.K. Nazeeruddin, J. Maier, M. Grätzel, Mixed-organic-cation perovskite photovoltaics for enhanced solar-light harvesting. Angew. Chem. Int. Edit. 53(12), 3151-3157 (2014). https://doi.org/10.1002/anie.201309361
[37] A.A. Zhumekenov, M.I. Saidaminov, M.A. Haque, E. Alarousu, S.P. Sarmah et al., Formamidinium lead halide perovskite crystals with unprecedented long carrier dynamics and diffusion length. ACS Energy Lett. 1(1), 32-37 (2016). https://doi.org/10.1021/acsenergylett.6b00002
[38] D. Yu, F. Cao, Y. Shen, X. Liu, Y. Zhu, H. Zeng, Dimensionality and interface engineering of 2d homologous perovskites for boosted charge-carrier transport and photodetection performances. J. Phys. Chem. Lett. 8(12), 2565-2572 (2017). https://doi.org/10.1021/acs.jpclett.7b00993
[39] M.I. Saidaminov, A.L. Abdelhady, G. Maculan, O.M. Bakr, Retrograde solubility of formamidinium and methylammonium lead halide perovskites enabling rapid single crystal growth. Chem. Commun. 51(100), 17658-17661 (2015). https://doi.org/10.1039/C5CC06916E
[40] N. Arora, M.I. Dar, M. Hezam, W. Tress, G. Jacopin et al., Photovoltaic and amplified spontaneous emission studies of high-quality formamidinium lead bromide perovskite films. Adv. Funct. Mater. 26(17), 2846-2854 (2016). https://doi.org/10.1002/adfm.201504977
[41] Q. Han, S.H. Bae, P. Sun, Y.T. Hsieh, Y.M. Yang et al., Single crystal formamidinium lead iodide (FAPbI3): Insight into the structural, optical, and electrical properties. Adv. Mater. 28(11), 2253-2258 (2016). https://doi.org/10.1002/adma.201505002
[42] R. Dong, Y. Fang, J. Chae, J. Dai, Z. Xiao et al., High-gain and low-driving-voltage photodetectors based on organolead triiodide perovskites. Adv. Mater. 27(11), 1912-1918 (2015). https://doi.org/10.1002/adma.201405116
[43] W. Hu, W. Huang, S. Yang, X. Wang, Z. Jiang et al., High-performance flexible photodetectors based on high-quality perovskite thin films by a vapor-solution method. Adv. Mater. 29(43), 1703256 (2017). https://doi.org/10.1002/adma.201703256
[44] M. Ahmadi, T. Wu, B. Hu, A review on organic-inorganic halide perovskite photodetectors: device engineering and fundamental physics. Adv. Mater. 29(41), 1605242 (2017). https://doi.org/10.1002/adma.201605242
[45] Y. Liu, J. Sun, Z. Yang, D. Yang, X. Ren, H. Xu, Z. Yang, S.F. Liu, 20-mm-large single-crystalline formamidinium-perovskite wafer for mass production of integrated photodetectors. Adv. Opt. Mater. 4(11), 1829-1837 (2016). https://doi.org/10.1002/adom.201600327
[46] M.I. Saidaminov, M. Haque, M. Savoie, A.L. Abdelhady, N. Cho et al., Perovskite photodetectors operating in both narrowband and broadband regimes. Adv. Mater. 28(37), 8144-8149 (2016). https://doi.org/10.1002/adma.201601235
[47] V. Liberman, M. Rothschild, O. Bakr, F. Stellacci, Optical limiting with complex plasmonic nanoparticles. J. Opt. 12(6), 065001 (2010). https://doi.org/10.1088/2040-8978/12/6/065001
[48] E. Chong, T. Watson, F. Festy, Autocorrelation measurement of femtosecond laser pulses based on two-photon absorption in gap photodiode. Appl. Phys. Lett. 105(6), 062111 (2014). https://doi.org/10.1063/1.4893423
[49] W.R. Zipfel, R.M. Williams, Nonlinear magic: Multiphoton microscopy in the biosciences. Nat. Biotechnol. 21(11), 1369-1377 (2003). https://doi.org/10.1038/nbt899
[50] W. Haske, V.W. Chen, J.M. Hales, W. Dong, S. Barlow, S.R. Marder, J.W. Perry, 65 nm feature sizes using visible wavelength 3-D multiphoton lithography. Opt. Express 15(6), 3426-3436 (2007). https://doi.org/10.1364/OE.15.003426
[51] G. Walters, B.R. Sutherland, S. Hoogland, D. Shi, R. Comin, D.P. Sellan, O.M. Bakr, E.H. Sargent, Two-photon absorption in organometallic bromide perovskites. ACS Nano 9(9), 9340-9346 (2015). https://doi.org/10.1021/acsnano.5b03308
[52] Q. Lin, A. Armin, P.L. Burn, P. Meredith, Near infrared photodetectors based on sub-gap absorption in organohalide perovskite single crystals. Laser Photonics Rev. 10(6), 1047-1053 (2016). https://doi.org/10.1002/lpor.201600215
[53] B. Yang, X. Mao, S. Yang, Y. Li, Y. Wang, M. Wang, W. Deng, K. Han, Low threshold two-photon-pumped amplified spontaneous emission in CH3NH3PbBr3 microdisks. ACS Appl. Mater. Interfaces 8(30), 19587-19592 (2016). https://doi.org/10.1021/acsami.6b04246

Citation Information

Fengying Zhang, Bin Yang, Kaibo Zheng, Songqiu Yang, Yajuan Li, Weiqiao Deng, Rongxing He, Formamidinium Lead Bromide Perovskite Microcrystals for Sensitive and Fast Photodetectors. Nano-Micro Lett.(2018) 10: 43. https://doi.org/10.1007/s40820-018-0196-2

History

Received: 23 January 2018 / Accepted: 5 March 2018


Additional Info

  • Type of Publishing: JOUR - Journal
  • Title: Formamidinium Lead Bromide Perovskite Microcrystals for Sensitive and Fast Photodetectors
  • Author: Fengying Zhang, Bin Yang, Kaibo Zheng, Songqiu Yang, Yajuan Li, Weiqiao Deng, Rongxing He
  • Year: 2018
  • Volume: 10
  • Issue: 3
  • Journal Name: Nano-Micro Letters
  • ISSN: 2150-5551
  • URL: http://dx.doi.org/10.1007/s40820-018-0196-2
  • Abstract: Because of the good thermal stability and superior carrier transport characteristics of formamidinium lead trihalide perovskite HC(NH2)2PbX3 (FAPbX3), it has been considered to be a better optoelectronic material than conventional CH3NH3PbX3 (MAPbX3). Herein, we fabricated a FAPbBr3 microcrystal-based photodetector that exhibited a good responsivity of 4000 A W−1 and external quantum efficiency up to 106% under one-photon excitation, corresponding to the detectivity greater than 1014 Jones. The responsivity is two orders of magnitude higher than that of previously reported formamidinium (FA) perovskite photodetectors. Furthermore, the FAPbBr3 photodetector’s responsivity to two-photon absorption with an 800-nm excitation source can reach 0.07 A W-1, which is four orders of magnitude higher than that of its MAPbBr3 counterparts. The response time of this photodetector is less than 1 ms. This study provides solid evidence that FAPbBr3 can be an excellent candidate for highly sensitive and fast photodetectors.
  • Publish Date: Monday, 05 March 2018
  • Start Page: 43
  • DOI: 10.1007/s40820-018-0196-2