Recent Progress in the Fabrication, Properties, and Devices of Heterostructures Based on 2D Materials

View ResearcherID and ORCID

Yanping Liu1, #, *, Siyu Zhang1, #, Jun He1, Zhiming M. Wang2, *, Zongwen Liu3, *

Abstract
icon-htmlFull Text Html
icon-pdf-smPDF w/ Links
icon-citExport Citation
Figures
+Show more

Nano-Micro Lett. (2019) 11: 13

First Online: 18 February 2019 (Review)

DOI:10.1007/s40820-019-0245-5

*Corresponding author. E-mail: liuyanping@csu.edu.cn (Yanping Liu); zhmwang@gmail.com (Zhiming M. Wang); zongwen.liu@sydney.edu.au (Zongwen Liu)

 

Abstract

 


Toc

With a large number of researches being conducted on two-dimensional (2D) materials, their unique properties in optics, electrics, mechanics, and magnetics have attracted increasing attention. Accordingly, the idea of combining distinct functional 2D materials into heterostructures naturally emerged that provides unprecedented platforms for exploring new physics that are not accessible in a single 2D material or 3D heterostructures. Along with the rapid development of controllable, scalable and programmed synthesis techniques of high-quality 2D heterostructures, various heterostructure devices with extraordinary performance have been designed and fabricated, including tunneling transistors, photodetectors, and spintronic devices and so on. In this review, we present a summary of the latest progresses in fabrications, properties, and applications of different types of 2D heterostructures, followed by the discussions on present challenges and perspectives of further investigations.


 

Keywords

Two-dimensional (2D) materials; 2D heterostructures; Charge and magnetotransport; Electronic and optoelectronic devices

 

Full Text Html

1 Introduction

    Since the successful preparation of graphene in 2004 [1], the properties and applications of two-dimensional (2D) materials have attracted much attention. 2D materials can be divided into single-element 2D materials (such as graphene, black phosphorus (BP), silylene, germanene, etc.) and compound 2D materials (TMDs, h-BN, TMCs, III-V group elements compound semiconductor, etc.) [2]. Compared to bulk materials, layered 2D materials possess many peculiar properties that are strongly related to their number of layers. For example, the band structure at the Dirac point of a monolayer of graphene exhibits a linear dispersion relation, which is quite different from the parabolic band structure of double-layered grapheme [3]. And for black phosphorus (BP), the bandgap displays an evident redshift as the number of layers increases [4]. Besides, the direct-to-indirect band gap transition has been demonstrated in TMD semiconductors when it changes from single-layer to multi-layer [5]. 2D thin-layered materials have been considered as promising building blocks for the next-generation of electronic and optoelectronics devices due to their extraordinary properties. In particular, 2D atomically thin structures are immune from the short channel effect and their mechanical strength allows for integration into flexible and wearable circuits [6, 7].
  However, a number of issues limit the application of single 2D materials. Specifically, the direct deposition of metal electrodes on 2D semiconductors during device fabrication results in a high contact resistance due to the Schottky barrier [8-10]. Also, the intralayer excitons generated in single 2D semiconductor materials are hard to manipulate due to their short lifetime [11], which restricts their applications in exciton devices. Furthermore, h-BN and most insulated 2D materials are not suitable to be applied in devices alone, and BP is easily oxidized when exposed to air.
   Therefore, the idea of that 2D materials can be assembling 2D materials into heterostructures was put forward [12], and many novel properties of these heterostructures have been discovered [13-19]. Heterostructured 2D materials can be divided into two categories: the vertically stacked heterostructures and the epitaxial grown planar heterostructures. In this paper, we focus on the fabrication methods, the properties and the applications of 2D heterostructures in these two types.

2 Fabrications of 2D Heterostructures

2.1 Deterministic Transfer Method

    The layered 2D materials prepared through mechanical exfoliation and chemical vapor deposition can be transferred onto different substrates at a desired location. This usually requires a long working distance optical inspection system in combination with an XYZθ direction micro-manipulator for accurate placement, and certain polymer layers as a transfer medium. There are four types of polymer carriers: (I) PMMA/sacrifice layer [12, 20], (II) PDMS [21, 22], (III) thermoplastic polymer [23], and (IV) hybrid stamp composed of PDMS / PPC (or PC, PMMA) / h-BN [24]. The transfer processes are slightly different from each other as schematically illustrated in Fig. 1.

Fig. 1 The deterministic transfer method. The yellow, blue, green and red dashed lines correspond to the process of transfer using polymer carriers of types I to IV respectively, and in the end a bare heterostructure or a multilayer heterostructure covered by h-BN will be fabricated

Fig. 1 The deterministic transfer method. The yellow, blue, green and red dashed lines correspond to the process of transfer using polymer carriers of types I to IV respectively, and in the end a bare heterostructure or a multilayer heterostructure covered by h-BN will be fabricated

    Step 1: The polymer carriers are spin-coated layer by layer onto a Si / SiO2 substrate (mainly for type I transfer media) or a glass slide, and then mechanically exfoliate thin flakes of 2D nanostructures onto the carriers; Step 2: Mount the glass slide on the micro-manipulator directly or after the wet transfer process (mainly for type I carriers, the PMMA with flakes is attached to a glass slide when released from the Si/SiO2 substrate through desolating the sacrificial layer), and then align the flakes on the polymer carriers with the target material prepared on existing substrate into the desired location and orientation under microscope with micro-manipulate arms, and then the glass slide was lowered down until the two flakes make contact to form the van der Waals heterostructure; Step 3: Directly pick up the target flakes and combine with another layered material to form multi-heterostructure (for type IV carriers) or release the heterostructure by slowly lifting the glass slide and remove the residual polymer in acetone solution (for type ΙΙΙ and type IV transfer media, heating substrates are needed to release the stacking).

    The comparison between the different deterministic transfer methods is presented in Table 1 [25]. The cleanness is mainly determined by whether the interfaces in the heterostructure are exposed to the polymer. And the easiness and speed are dependent on the number of steps and specific procedures such as spin-coating, heating, and wet-transferring, which will increase the complexity and slow down the speed to some extent. The PDMS dry transfer is considered the easiest and quickest method, as the progress does not involve spin-coating, wet transfer or heating process. PDMS films have become commercialized commodities and their viscosity is strongly related to the speed when being peeled off [26]. Meanwhile, the pick-up method remains the best way to assemble multi-heterostructure with no residual polymer at interfaces. In conclusion, the deterministic transfer method has high flexibility in fabricating various heterostructures, but its drawbacks are obvious. It is inevitable to cause polymer residue at the interface or on the surface, and the 2D material samples may be destroyed or got wrinkled during the transfer process. Another challenge of the deterministic transfer method is the control of the stack orientation.

Table 1 Comparison between the different deterministic placement methods.

11 13 table1

2.2 Chemical Vapor Deposit (CVD) Growth

    CVD synthesis is a bottom-up strategy for the preparation of vertical 2D heterostructures and is able to realize the growth of planar multi-junction heterostructures. In order to obtain an atomically sharp heterojunction and a clean interface in vertically stacked heterostructures, as well as achieve scalable and controllable fabrication of both vertical and planar heterostructures, various approaches have been explored to realize CVD growth of heterostructures.

2.2.1 The One-Step CVD Method

    The schematic diagram of Fig. 2a shows the processes of this method, which is suitable for preparing heterostructures with the component materials containing the same elements. Yongji Gong et al. [27] successfully fabricated both vertical and planar MoS2/WS2 heterostructures by this one-step CVD method that demonstrated the in-plane epitaxial growth at a lower temperature of 650°C , as the provided energy was not enough for the nucleation of WS2 on the surface of MoS2, but at a higher temperature of 850 °C  vertically stacked structure could be formed as the van der Waals heterostructure was more thermodynamically stable.

Fig. 2 Chemical vapor deposit (CVD) growth. a The diagram of the synthesis of MoS2/WS2 heterostructures through one-step CVD method. S powder is placed at the upstream and a wafer with mixed powder of W and Te is put downstream. Reprinted with permission from Ref. [27]. b Multi-steps CVD growth of realized through direction-switchable carrier flow and cooling process. Reprinted with permission from Ref. [32]. c the modulable growth of 〖WS〗_2-〖WS〗_2(1-x)  〖Se〗_2x (0x1) monolayer lateral heterostructures using dual-heating quartz tube and d the optical picture and PL intensity mappings of heterostructures with different x. Reprinted with permission from Ref. [33]. e The principle of one-pot synthesis strategy and f the optical picture and PL intensity mappings of the hetero-superlattice indicating the sharp interlines. Reprinted with permission from Ref. [31]

Fig. 2 Chemical vapor deposit (CVD) growth. a The diagram of the synthesis of MoS2/WS2 heterostructures through one-step CVD method. S powder is placed at the upstream and a wafer with mixed powder of W and Te is put downstream. Reprinted with permission from Ref. [27]. b Multi-steps CVD growth of realized through direction-switchable carrier flow and cooling process. Reprinted with permission from Ref. [32]. c the modulable growth of 〖WS〗_2-〖WS〗_2(1-x) 〖Se〗_2x (0x1) monolayer lateral heterostructures using dual-heating quartz tube and d the optical picture and PL intensity mappings of heterostructures with different x. Reprinted with permission from Ref. [33]. e The principle of one-pot synthesis strategy and f the optical picture and PL intensity mappings of the hetero-superlattice indicating the sharp interlines. Reprinted with permission from Ref. [31]

2.2.2 The Two-Step CVD Method

    This is a more commonly adopted approach using the as-grown layered crystals as a substrate for the second layer. Such procedures were also adapted for both the vertically stacked and lateral heterostructures that are mainly affected by the rate of gas flow and the synthesis time. Li et al. [28] reported the growth of 2D GaSe/MoSe2 heterostructure by this two-step CVD method. Such MX/MX2 vertical heterostructures exhibit incommensurate superstructures because of the large lattice misfit between the two layers. In addition, the synthesis of a stacked TMD/hBN heterostructure was also realized by using the Ni–Ga alloy and Mo foil as the substrate without any intermediate operations. In such a case the Ni–Ga alloy promoted the formation of the h-BN honeycomb lattice while the Mo foil was a source of Mo [29].

2.2.3 The Multi-Steps CVD Method

    By switching the direction and modulating the components of gas flow [30-32], the multi-steps CVD method was developed (Fig. 2b). This approach makes the boundary of heterojunctions sharper and enables the sequential growth of the multi-junction heterostructure. Biyuan Zheng et al. [33] reported an efficient method to grow modulable -  monolayer planar heterostructure (Fig. 2c) with tunable band alignment (Fig. 2d). Using the dual heating furnace, the switching of the synthesis from a pure WS2 growth to a WS2(1-x)Se2x alloy formation can be controlled by changing the direction and the temperature of the Ar gas flow. The parameter x is modulated by the ratio of the mixed WS2/WSe2 powders.

    Moreover, the control of growth can also be realized by changing the components of the gas flow. Prasana K. Sahoo et al. [31] reported the one-pot synthesis strategy by placing two precursors (MoX2 and WX2 mixed powders) in the same boat at the heating zone, while the substrate was held at a lower temperature. The mechanism is vividly illustrated in Fig. 2e: under the N2 + H2O (g) gas flow, only the growth of MoX2 was promoted. When the gas flow was switched to the Ar + H2(5%) gas flow, only the growth of WX2 was allowed. Reversing the gas flow would terminate the current reaction. Figure 2f shows the optical images and the Raman intensity maps at 240 and 250 cm-1 revealing the well-defined spatial distribution and sharp interface of the MoSe2 and WSe2 domains in the multi-junction heterostructure. Compared with the one-step and the two-step CVD methods, the multi-step CVD method is more flexible and controllable that enables the possibility of creating spatial-selected optoelectronic devices due to the separation of electrons and holes into different materials.

3 Properties

3.1 Band Alignment

    The band alignment is the fundamental property of 2D heterostructures. Most charge transport behavior and illuminance properties are originated from the band structures, especially the band alignment. The band energy can be calculated in theory based on the first principles and measured through μ-XPS. Figure 3a [34] shows the band alignments of a monolayer semiconducting TMDs and monolayer SnS2 calculated by Perdew-Burke-Ernzerhof (PBE) with spin-orbit coupling (SOC). The results indicate that, for the monolayer TMDs in MX2 form, the energy of the conduction band minimum (CBM) and the valence band maximum (VBM) increase with the atomic number of X. Thus, when two different materials with sizable band gaps get combined into a heterostructure, there will be three types of I~III band alignments without considering the band bending at the interface, which are called straddling gap, staggered gap, and broken gap respectively. The type-I band alignment contributes to the fast recombination of electrons and holes, that allows them to be used in luminescent devices, such as light-emitting diodes (LEDs) [35, 36]. The type-II band alignment can facilitate the effective spatial separation of electrons and holes, prolonging the lifetime of interlayer excitons and making them a good candidate for the application in electron-hole separators and related optoelectronic devices. The type-III band alignment allows the band-to-band tunneling (BTBT) effect of carriers and enables the operation of the tunnel field effect transistors (TFET). Compared with the type II band alignment, the speed of the transportation of the electrons and holes in type-III heterostructures is much faster that results in a large number of electrons and holes separating into different layers of the material, so the heterojunction displays semi-metallic features generating a strong built-in electric field that makes the type-III heterostructures ideal for new generation thermal photovoltaic cells.

Fig. 3 Band alignment and band engineering methods. a Theoretical positions of VBM and CBM of VIB- and IVB-TMDs calculated by PBE-SOC. Reprinted with permission from Ref. [34]. b Schematic diagram of band bending at the interface, forming a notch on the accumulation side and a peak on the depletion side. c, d STM measurements of h-BN/graphene heterostructure stacked with the different rotation angle of 5° (c) and 0° (d). Reprinted with permission from Ref. [42]. e PL spectra of MoS2 monolayer and bilayers with different twist angles, where peak I is related to the direct transition at K-valley and peak II may be associated with the indirect band gap. Reprinted with permission from Ref. [42]. f The principle of photo-gating band alignment engineering. Reprinted with permission from Ref. [43]. g The band structure of a floating-gate device based on monolayer WS2.

Fig. 3 Band alignment and band engineering methods. a Theoretical positions of VBM and CBM of VIB- and IVB-TMDs calculated by PBE-SOC. Reprinted with permission from Ref. [34]. b Schematic diagram of band bending at the interface, forming a notch on the accumulation side and a peak on the depletion side. c, d STM measurements of h-BN/graphene heterostructure stacked with the different rotation angle of 5° (c) and 0° (d). Reprinted with permission from Ref. [42]. e PL spectra of MoS2 monolayer and bilayers with different twist angles, where peak I is related to the direct transition at K-valley and peak II may be associated with the indirect band gap. Reprinted with permission from Ref. [42]. f The principle of photo-gating band alignment engineering. Reprinted with permission from Ref. [43]. g The band structure of a floating-gate device based on monolayer WS2.

    Interestingly,when taking the band bending at the interface into consideration, the band structure of the heterostructures presents more novel properties. For example, when two semiconductors form a PN-junction with type-I band alignment (Fig. 3b), the VB and the CB on the different sides will bend in the opposite directions, forming a notch and a peak respectively. There is none symmetry in ΔEC and ΔEV values which will cause different potential barriers for electrons and holes.

    In addition, the band structure of a 2D heterostructure can be affected by many factors. Firstly, the quality of the interface is very important. For example, the interface defects and impurities can cause the defect or impurity energy level; and intrinsic metal-induced gap states (MIGS) or extrinsic disorder induced gap states (DIGS) at the interface would lead to the occurrence of Fermi-level pinning effect [37]. Pantelis Bampoulis et al. [38] demonstrated that the subsurface metal-like defects in MoS2/metal heterostructures could hugely decrease the Schottky barrier height (SBH) that attributed to strong Fermi-level pinning at the defects. On the other hand, a weak Fermi level pinning led to the SBH modulation by electrical gating [39], and a very weak Fermi level pinning has been observed at the graphene/TMD interfaces. A shift of about 120 mV was observed between the spectra of scanning tunneling spectroscopy (STS) of flakes residing on single-layer graphene (SLG) and bilayer graphene (BLG) substrates, which is equal to the difference in the work function of SLG and BLG. Secondly, the lattice constants of the materials and their stake orientation are also important factors. When two 2D materials with similar lattice constants form heterostructures, such as graphene/h-BN [40]  and SnS2/MoS2 [41], a periodic Moiré pattern will be formed. Figure 3c, d shows the STM measurements on graphene/h-BN heterostructure with a rotation smaller (Fig. 3d) and larger (Fig. 3c) than 1°. The later one displays a nearly same spatial periodic behavior exhibiting a much larger Moiré pattern due to the high Young modulus of graphene. Such deformation of lattice structure results in a much stronger van der Waals interaction and causes extra periodic potential in graphene that adjusts its band structure. Moreover, the indirect band gap varies appreciably with the stacking orientation [42]: the largest redshift for AA-(twist angle of 0 °) and AB-(twist angle of 60 °) stacked bilayers, and a significantly smaller but constant redshift for all other twist angles (Fig. 3e).

    However, adjusting the band alignment through the above structural factors is complex and inflexible. The band structure of heterojunction can also be externally controlled by an electric field, magnetic field and light field [45]. The band engineering regulated by the gate voltage leads to the transitions in 2D heterostructures between band alignment of type I-III. Especially, graphene has a unique linear dispersion relationship with a finite DOS, thus the Fermi level and work function of graphene are gate modulable, making graphene widely used as the contact between the electrodes and the channel of the 2D material to reduce the contact resistance (Rc). What’s more, band structure can also be optically modulated to behave like a photogate, a phenomenon looking like the addition of a local gate (ΔVg) to the device when under illumination [46]. The band diagram of a photodetector with the WS2/MoS2 hetero-bilayer as a light absorption layer and the graphene as the electrode contact is shown in Fig. 3f [43]. Under illumination, the accumulation of holes at the region acts as a positive gate on the source graphene electrode, effectively raising the Fermi level of the graphene electrode and lowering the SBH. Figure 3g [44] shows a typical band structure of floating-gate devices with an Au floating-gate layer to form energy well to trap the charges.

3.2 Charge Transport Properties in 2D Heterostructures

    Different band alignments result in a variety of charge transport characteristics accompanied by the process of energy transfer. On the one hand, the single particle transportation, including interlayer tunneling effect and charge trapping phenomena, has been widely reported and novel devices based on those transportation mechanisms have been fabricated that exhibit low energy-assumption with high performance; on the other hand, the many-body transport and the separation of electron-hole pairs in 2D heterostructures have also been theoretically predicted and practically demonstrated [11], which enable the prospect of broad applications in optoelectronic field [47-51].  

3.2.1 Single Particle Transports

    The ultra-narrow channel length and atomically sharp interfaces can realize band-to-band tunneling (BTBT) effect by electrostatic gating to avoid deprivation of band-edge sharpness resulted from chemical doping [52]. As is shown in Fig. 4a-c [53], when applying a small Vg (Fig. 4b), the CBM of WSe2 is higher than the VBM of SnSe2. The electrons in SnSe2 cannot tunnel into WSe2, but diffusion of charges occurs at the interface, corresponding to channel current and high resistance state respectively when applied with a positive and negative bias voltage. This corresponds to the off state of the device. When keeping on increasing the Vg while the CBM of WSe2 is set below the VBM of SnSe2 (Fig. 4c), a tunneling window is opened, such that an interlayer tunneling can flow from SnSe2 to WSe2. In type I band alignment the layer with a wide bandgap will cause spatial confinement of electrons and holes in the “well” layer with a narrow bandgap [54] that causes a strong PL in a trapping layer and a quenched PL in the other (Fig. 4d).

Fig. 4 The single particle transport caused by different band structures. a-c The electronic modulation of BTBT in a TFET based on 2D SnSe2/WSe2 heterostructure. Reprinted with permission from Ref. [53]. d PL measurement of a stacked WSe2/MoTe2 heterostructure with proper annealing, where the blue, black and red line corresponding to the PL intensity of specific energy (eV) from the isolated WSe2 region, isolated MoTe2 region, and hetero stacked region respectively. Reprinted with permission from Ref. [54]. e-f The diagram of the charge transferring in p-MSB/WSe2 heterostructure under illumination. Reprinted with permission from Ref. [55]. g The band alignment, charge transportation and the distribution of the potential in the device. Reprinted with permission from Ref. [40]

Fig. 4 The single particle transport caused by different band structures. a-c The electronic modulation of BTBT in a TFET based on 2D SnSe2/WSe2 heterostructure. Reprinted with permission from Ref. [53]. d PL measurement of a stacked WSe2/MoTe2 heterostructure with proper annealing, where the blue, black and red line corresponding to the PL intensity of specific energy (eV) from the isolated WSe2 region, isolated MoTe2 region, and hetero stacked region respectively. Reprinted with permission from Ref. [54]. e-f The diagram of the charge transferring in p-MSB/WSe2 heterostructure under illumination. Reprinted with permission from Ref. [55]. g The band alignment, charge transportation and the distribution of the potential in the device. Reprinted with permission from Ref. [40]

    When take the band bending into consideration, the interfacial charge trapping can be seen in the PN junction of type II band alignment. Zhi Cai et al. [55] developed an electric-gating switchable photodetector based on p-MSB/WSe2 by epitaxial growth of 2D van-der-Waals, in which the p-MSB serves as a light absorber, while in the p-MSB/WSe2 heterostructure an interfacial energy barrier and a band bending between the lowest unoccupied molecular orbital of p-MSB and the CBM of WSe2 (Fig. 4e), enable unidirectional carrier injection. When a negative Vg is applied (Fig. 4f), the Fermi level of WSe2 shifts downwards, leading to an increase of the interfacial energy barrier that enhances the interfacial charge trapping process. It is believed the interface quality is the key to avoid the on-state current decreasing under such plasma treatment.

    Another way to obtain charge trapping is to place a floating-gate layer, which is usually sandwiched with the tunneling and blocking dielectric layers, between the channel and control gate as a charge trapping layer [44, 56-61]. Figure 4g [62] shows the charge transport in the floating-gate structure with graphene as the trapping layer and monolayer MoS2 as the channel. When a -6 V (+6 V) drain bias is applied, a large potential difference between the drain and graphene, and a nearly equal potential of the source electrode and graphene are generated. As a result, the electrons (and holes) are able to tunnel through the h-BN layer at the drain electrode side and are trapped in the floating-gate layer, so are unable to tunnel back to the source electrode or the MoS2 channel.

3.2.2 The Generation of Interlayer Excitons

    For the type II band alignment, the CBM and VBM are in different layers that lead to the spatial separation of electrons and holes. The ultrafast separation of electron-hole pairs could be detected by the pump-probe technique [49, 63, 64]. In the WS2/MoS2 heterostructure, after the MoS2 monolayer is directly pumped the photo-induced signal will appear instantaneously. The experimentally observed signal in the heterostructure shows a rising time that is shorter than 50 fs (Fig. 5a).

Fig. 5 The generation of interlayer excitons. a The transient absorption measurements of WS2 A-exciton resonance in the MoS2/WS2 heterostructure and B-exciton resonance in an isolated MoS2 monolayer. The dynamic evolution signal is obtained by convoluting the instrument response function (blue dashed line). b PL spectra detected from the 1-4 region of a vertically stacked WS2/MoS2 heterostructure, and number 1 and 2 corresponding to the MoS2 monolayer and number 3 and 4 regions are hetero stacked bilayer. Two additional peaks at 630 and 875 nm indicate the generation of interlayer excitons. Reprinted with permission from Ref. [27]. c The two processes of the interlayer excitons generation. Reprinted with permission from Ref. [63]

Fig. 5 The generation of interlayer excitons. a The transient absorption measurements of WS2 A-exciton resonance in the MoS2/WS2 heterostructure and B-exciton resonance in an isolated MoS2 monolayer. The dynamic evolution signal is obtained by convoluting the instrument response function (blue dashed line). b PL spectra detected from the 1-4 region of a vertically stacked WS2/MoS2 heterostructure, and number 1 and 2 corresponding to the MoS2 monolayer and number 3 and 4 regions are hetero stacked bilayer. Two additional peaks at 630 and 875 nm indicate the generation of interlayer excitons. Reprinted with permission from Ref. [27]. c The two processes of the interlayer excitons generation. Reprinted with permission from Ref. [63]

    The detailed charge separation processes in the heterostructure is presented in Fig. 5c [63]. After the excitation of the WS2(MoS2) monolayer, the electrons (holes) transferred from the CBM (VBM) of WS2 (MoS2) monolayer to the conduction (valence) bands just above (below) CBM (VBM) of the MoS2(WS2) monolayer within 50 fs, generating a hot interlayer excitons with a relatively long distance. The hot excitons then reorganized and dissipated the excess energy to form the tightly bound interlayer excitons within 800 fs. The existence of the final tightly bound interlayer excitons could be distinctly demonstrated in photoluminescence spectra [63, 65] as is shown in Fig. 5b [27]­. The photoluminescence signal was taken from number 1 and 2 regions corresponding to the A-exciton resonances in the monolayer MoS2. But the signals from the heterostructure regions displayed exciton resonances in MoS2 and WSe2, leading to an additional interlayer exciton peak. The exciton photoluminescence signals of MoS2 and WSe2 were quenched in the heterostructure due to the charge transfer process.

3.3 The Properties of Excitons in 2D Heterostructure

    The interlayer excitons hold the prolonged lifetime [51] and large binding energy which is strongly related to the distance between the two layers in vertical heterostructures. Simone Latini et al. [66] developed a QEH (quantum electrostatic heterostructure) model based on the MoS2/x-hBN/WSe2 vertical heterostructures (the parameter x is the number of hBN layers). The binding energy of the interlayer excitons is calculated up to 0.3 eV and decreases with the increasing parameter x, indicating a stable existence of the interlayer excitons at room temperature. But the weak oscillator strength and momentum-indirect nature make it challenging to directly observe the interlayer excitons by resonant optical excitation [67]. Figure 6a is the spectra of electroluminescence (red line) and photoluminescence (black line) for lateral p−n junctions based on a vertical MoSe2-WSe2 hetero-bilayer. The inset picture illustrates the electrode contacts of each layer. When applying a forward Vsd, the carriers would be injected in and recombine at the edge of the hetero-bilayer (orange arrows). It turned out that the photocurrent amplitude from the interlayer exciton was about 200 times smaller than that of the resonant excitation of the intralayer exciton.

Fig. 6 The properties of excitons in 2D heterostructures. a EL spectra of the MoSe2/WSe2 vertical heterostructure, a small intralayer signal at 1.62 eV was detected, and the inset illustrates the device structure (blue and green line represent the WSe2 and MoSe2 respectively). Reprinted with permission from Ref. [67]. b The optical selection rules in a MoX2/WX2 heterostructure with twist angle θ of 0° and 60° respectively. Reprinted with permission from Ref. [17]. c-d Time-resolved PL (d) of WSe2/MoSe2 heterostructure (c) after σ+ pulsed laser excitation, black dots and red dots corresponding to the co-polarized emission (σ+) and cross-polarized emission (σ-), and the blue line shows the degree of polarization, which is tunable by the gate voltage. Reprinted with permission from Ref. [68]. e The trions composed in different ways existing in the MoS2/WS2 bilayer. Reprinted with permission from Ref. [69]

Fig. 6 The properties of excitons in 2D heterostructures. a EL spectra of the MoSe2/WSe2 vertical heterostructure, a small intralayer signal at 1.62 eV was detected, and the inset illustrates the device structure (blue and green line represent the WSe2 and MoSe2 respectively). Reprinted with permission from Ref. [67]. b The optical selection rules in a MoX2/WX2 heterostructure with twist angle θ of 0° and 60° respectively. Reprinted with permission from Ref. [17]. c-d Time-resolved PL (d) of WSe2/MoSe2 heterostructure (c) after σ+ pulsed laser excitation, black dots and red dots corresponding to the co-polarized emission (σ+) and cross-polarized emission (σ-), and the blue line shows the degree of polarization, which is tunable by the gate voltage. Reprinted with permission from Ref. [68]. e The trions composed in different ways existing in the MoS2/WS2 bilayer. Reprinted with permission from Ref. [69]

    Interlayer excitons also have ideal valley-contrast physics. Fig. 6b [17] is the schematic of the interlayer exciton recombination in the K± valley in a MoS2/WSe2 heterostructur with the twist angle of 0° and 60°. After circularly polarized light excites intralayer excitons in the K+ valleys of MoS2 and K+ valleys of WSe2, a fast interlayer charge hopping forms the interlayer exciton in the K+ valley. The solid (dashed) arrows denote the dipole transition (interlayer hopping). Pasqual Rivera et al. [68] observed long valley lifetime and valley drift-diffusion of host interlayer excitons in MoSe2-WSe2 heterostructures with small twist angles (Fig. 6d). The valley polarization is greatest at +60 V and highly suppressed at −60 V. The valley polarization lifetime increases with Vg, reaching 39 ± 2 ns at +60 V, as determined by fitting a single exponential decay. The extraordinary valley-contract properties allow the possibility of the excitonic optoelectronic circuit to switch the valley functionalities and provide a platform for investigating excitonic superfluidity and condensation.

    In addition to intralayer and interlayer excitons, there is the theoretical existence of trions in 2D heterostructures. Figure 6e shows the different kinds of combinations of trions in a MoS2/WS2 heterostructure. Thorsten Deilmann et al. [69] calculated the interlayer excitation in a MoS2/WS2 heterostructure and predicted the existence of bound interlayer trions below the neutral interlayer. The binding energies is 18 and 28 meV for the positive and negative interlayer trions with both electrons/holes located on the same layer.

3.4 Magnetic Properties in 2D Heterostructures

    For the low-dimensional magnetic materials, the coercivity, saturation magnetization, Curie temperature (TC) and other magnetic parameters of the materials are related to the number of layers and grain size. Therefore, 2D materials usually present magnetic properties that differ from its bulk form. The application of 2D magnetic materials in heterostructures is of great significance for the study of spintronics, valleytronics, and electromagnetics [70]. The magnetic properties of 2D heterostructures are significant for the external ways to control (gate) the propagation of spin and valley (polarized) currents at room temperature. The massive theoretical calculations and experimental results indicate that by assembling 2D materials (graphene or TMDs) with ferromagnetic materials into a van der Waals heterostructure [71], a large magnetic exchange field can be generated at the interface and thus the regulation of the spin and valley pseudospin in 2D materials can be realized [72-74]. The existence of the magnetic exchange field can amplify the effect of the external magnetic field, which originates from the proximity effects of the heterojunction [75]. Figure 7a shows the sublattices of graphene on EuO represented with different colors and letters. Due to the existence of the EuO substrate, the two sublattices of isolated graphene break into six folders as shown in Fig. 7b. Such structural change resulting from the proximity effect will enhance the magnetic moment of surface Eu atoms, causing variable spin polarizations on the graphene sublattices with a calculated spin polarization of about 24% in average, and change the band structure of graphene. The recent research suggests that such magnetic exchange field (MEF) can be tuned over a range of 20T by small changes in the laser-excitation power [76]. Figure 7c shows the magnetization of CrI3 in a monolayer WSe2/multilayer CrI3 heterostructure probed via reflection magnetic circular dichroism (RMCD) as a function of the external magnetic field at different excitation light power. The RMCD exhibits a very similar power-dependent hysteresis loop behavior. Such opto-magnetic effect enables the power-switchable valley properties as illustrated in the PL spectra in Fig. 7d, where the polarization ρ (defined as (I+ - I-)/ (I+ - I-) , with  being the PL peak intensity excited by σ± polarized laser) flips in sign at certain external magnetic field with the increasing of the excitation power.

Fig. 7 Magnetic properties of 2D heterostructures. The broken lattice with six sublattices of graphene on the EuO (a) and the calculated spin polarization in graphene layer (b). Reprinted with permission from Ref. [75]. The RMCD (c) and polarization ρ (d) of WSe2/CrI3 heterostructure under sweeping external magnetic field and different excitation power. Reprinted with permission from Ref. [76]. e The transition of several PL peaks and the magnetic susceptibility along the out-of-plane direction (black) in FePS3 as the temperature increases. Reprinted with permission from Ref. [78]. The spin density and possible magnetic ground state (NM, FM, AFM) of XS2/VS2 heterostructures (f) and the dependence of band gap (g) and electrical field, and the calculated magnetic moment and relative energy is listed in the picture. Reprinted with permission from Ref. [79]. Schematic diagram of the device based on graphene/multilayer BP heterostructure (h) and the huge MR (i) compared with graphene on SiO2 substrate. Reprinted with permission from Ref. [80]

Fig. 7 Magnetic properties of 2D heterostructures. The broken lattice with six sublattices of graphene on the EuO (a) and the calculated spin polarization in graphene layer (b). Reprinted with permission from Ref. [75]. The RMCD (c) and polarization ρ (d) of WSe2/CrI3 heterostructure under sweeping external magnetic field and different excitation power. Reprinted with permission from Ref. [76]. e The transition of several PL peaks and the magnetic susceptibility along the out-of-plane direction (black) in FePS3 as the temperature increases. Reprinted with permission from Ref. [78]. The spin density and possible magnetic ground state (NM, FM, AFM) of XS2/VS2 heterostructures (f) and the dependence of band gap (g) and electrical field, and the calculated magnetic moment and relative energy is listed in the picture. Reprinted with permission from Ref. [79]. Schematic diagram of the device based on graphene/multilayer BP heterostructure (h) and the huge MR (i) compared with graphene on SiO2 substrate. Reprinted with permission from Ref. [80]

    The search of suitable 2D magnetic materials remains a challenge at the moment. The CrI3 mentioned above is layered magnetic material whose magnetic properties are strongly related to the number of layers [77]. Besides, a new class of magnetic heterostructure materials, called transition metal phosphorus trichalcogenides (TMPS, TM = V, Mn, Fe, Co, Ni, or Zn), could also be easily exfoliated and their magnetic ground state is strongly depended on the TM element. An Ising-type antiferromagnetic ordering from bulk to the monolayer has been reported for FePS3, a TMPS material. The Raman peaks (Fig. 7e) show a transition at the Neel temperature (TN) of 118 k [78].

    The TC of ferromagnetic materials in the above heterostructures is too low for them to be applied at room temperature. Current theoretical calculations have shown that XS2/VS2 heterostructures are ferromagnetic and are expected to have ultra-high TC [79]. Figure 7f is the optimized configurations, local magnetic arrangements, magnetic moments and energy relative to that of the ferromagnetic configuration for non-magnetic (NM), ferromagnetic (FM), and anti-ferromagnetic (AFM) states respectively. Clearly, the FM state is the most stable one for the two heterostructures. The XS2/VS2 heterostructures have the FM ground states in theory, and their TC can be calculated by the bellow equation:

11 13 gs

where γ is the dimension of the XS2/VS2 system,  is the Boltzmann constant, and EAFM and EFM are the energies of the unit-cell system with AFM and FM coupling respectively. The obtained very high Tc values are 485 K for the MoS2/VS2 heterostructure and 487 K for the WS2/VS2 heterostructure. Interestingly, a semiconductor-metal transition occurred under the modulating of the external electric field (Fig. 7g), indicating a potential for generating pure spin-polarized currents. Moreover, many other 2D magnetic materials have been studied experimentally or theoretically as shown in Table 2. Most of the 2D magnetic materials are in the form of MX (M=Cr, Co, V, Mo, Mn etc. X=C, O, S, Se or N) or MAX (M=Cr or Fe; A=Ge, Si, Al, Sn etc. X=Te), and most of them are semiconductors.

Table 2 The calculated or experimental properties of different 2D magnetic materials. Theoretically predicted materials are marked by (*). The ML, BL, TL, and HS are short for monolayer, bilayer and heterostructure respectively.

11 13 table2

    Furthermore, a magnetoresistance (MR) effect has been detected in some graphene-based heterostructures due to the interface state in the heterostructures. Yanpeng Liu et al. [80] fabricated a highly stable monolayer graphene/black phosphorus (Gra/BP) heterostructure device (Fig. 7h) that exhibits a giant MR (defined as ) of 775% (Fig. 7i), and the nonlocal MR more than10,000% in the Gra/BP device at room temperature due to an enhanced flavor Hall effect induced by the BP channel. Those experimental results provide valuable information for the study of magnetization dynamics in devices such as magnetoresistive random-access memories.

4 Applications in Devices

4.1 Electronic Devices
    2D materials have been extensively explored as channel materials for future electronic device applications because of their atomically thin channels that offer ideal electrostatic control to enhance the immunity to the short channel effects [89] and the deprivation of band-edge sharpness resulting from chemical doping. The electronic devices based on the band engineering of 2D heterostructures have been widely reported.
    Typically, the TFET usually uses an insulator thin layer of h-BN as the dielectric layer, as well as TMDs with large band gap. Using 2D materials to replace traditional metallic oxides effectively avoid pinholes, oxygen doping, and interlayer defects [90]. The TFET based on the SnSe2/WSe2 vertical heterostructure (Fig. 8a) was fabricated with a subthreshold swing of 80 mV dec-1 and ultrahigh ION/IOFF ratio over 106 (Fig. 8b), and such high performance can be realized simply by tuning the back-gate voltage to switch the BTBT effect [53].

Fig. 8 Electronic devices based on 2D heterostructure. Schematic diagram of programmable floating-gate memory based on MoS2/h-BN/graphene heterostructure (a), the hysteresis loop of Ids when Vds sweeps forward and backward (b) and the corresponding Ids when periodically repeat the four states by setting Vsd to -6, 0, and +6 V (c). Reprinted with permission from Ref. [62]. Transistor based on the BTBT in WSe2/SnSe2 heterostructure (d) and its channel current (e) as a function of Vg at certain Vd from 0.1 to 0.9V. Reprinted with permission from Ref. [53]

Fig. 8 Electronic devices based on 2D heterostructure. Schematic diagram of programmable floating-gate memory based on MoS2/h-BN/graphene heterostructure (a), the hysteresis loop of Ids when Vds sweeps forward and backward (b) and the corresponding Ids when periodically repeat the four states by setting Vsd to -6, 0, and +6 V (c). Reprinted with permission from Ref. [62]. Transistor based on the BTBT in WSe2/SnSe2 heterostructure (d) and its channel current (e) as a function of Vg at certain Vd from 0.1 to 0.9V. Reprinted with permission from Ref. [53]

    Likewise, memories based on the floating-gate structure are also important applications of 2D heterostructures, where the selection of the floating gate layer is crucial. To suppress the dark current in the device channel, gold nanoparticles (AuNPs) were selected to serve as the trapping layer [59]. Recently, researchers designed a programmable memory device based on a vertically stacked MoS2/h-BN/graphene heterostructure with graphene as the floating-gate [62] (Fig. 8c) which has ultrahigh on/off ratio and a high stretchability (>19%). With the dielectric layer of h-BN having an appropriate thickness, the on/off ratio over 109 has been obtained. Figure 8d shows the memory cycles realized by repeated voltage pulses as programming (i), reading (ii), erasing (iii) and reading (iv) operations. Such functions can also be demonstrated in the hysteresis behavior in the Ids-Vds plot (Fig. 8e) and are originated from the tunneling effect through h-BN and the asymmetric potential drop caused by the highly resistivity of MoS2. Moreover, Mengwei Si et al. [91]  integrated 2D ferroelectric insulator of CuInP2S6 on the top of MoS2 to build a nonvolatile memory device with a stable ferroelectric hysteresis loop in transfer characteristics.
4.2 Optoelectronic Devices
    2D materials are outstanding candidates for optoelectronic devices due to their unique properties, including the wide response spectrum range, excellent flexibility, and strong light-matter interaction [92, 93]. Similarly, due to the generation of interlayer excitons and flexible band engineering, 2D heterostructures have been widely applied in optoelectronics including photodetectors [94, 95], photovoltaic devices, and light source devices [96-102]. Many experiments have shown that the photodetectors based on 2D heterostructures can be applied in a broad range of spectrum from ultra-violet (UV) to near-infrared (NIR), the same range as that of the photodetectors based on bulk materials, but wider than that of a single 2D heterostructure. Table 3 lists the main parameters of the latest photodetectors based on 2D heterostructures. Actually, the photodetectors based on 2D heterostructures perform better due to the generation of the strong built-in electrical field in such atomically thin structures [103]. Also, researchers are keeping exploring multi ways to modulate devices and multi-structures to improve devices performance. It has been demonstrated that using graphene as the contact electrodes is an effective strategy to significantly increase the response speed (up to 5.5 ps Ref. [98]) of an atomically thin photodetector [96, 101, 102], because graphene, as a 2D material with ultrahigh carrier mobility, can minimize the lateral diffusion in the semiconductor [104]. Recently, Haijie Tan et al. [43] built WS2/MoS2 hetero-bilayer devices with layered graphene electrodes (Fig. 9a). By tuning the work function of graphene, the modification of the SBH at the interface of graphene and the TMD layer can be achieved. The lowering of the barrier as a result of the photogating effect would facilitate the re-injection of electrons into the TMD channel. Such devices displayed the highest photoresponsivity of up to 2,340 A W-1 and a large internal photoconductive gain over 3.7×104, with an estimated specific detectivity of 4×1011 Jones. Moreover, photodetectors based on MoS2-WS2 planar heterostructures [105] have also been reported to reach a detectivity of 4.36 × 1013 Jones. The p-n heterostructures are usually self-powered because the generated electron-hole pairs can get separated under built-in potential at zero bias. Compared with vertical heterostructures the fabrication of in-plain junctions is much controllable and scalable due to the difficulties of controlling the stacking orientation. The extraordinary flexibility of heterostructures enabled the researchers to design a curved image sensor array based on a MoS2-graphene heterostructure [106] which can be applied as a human eye-inspired soft implantable optoelectronic device for detecting optical signals through programmed electrical stimulation to optic nerves.

Fig. 9 2D heterostructures in optoelectronic applications. a Schematic diagram of TMD/TMD heterostructure with a graphene contact. Reprinted with permission from Ref. [43]. Schematic and optical picture of optoelectronic memory based on h-BN/WSe2 heterostructure (b) and the modulation of programming, reading and erasing state by Vg and incident illumination (c), and the wavelength-dependent PR (d). Reprinted with permission from Ref. [113]. Schematic and optical picture (e, f) of the multi-gate exciton device. The excitation region is marked by the red circle, and the recombination of the interlayer excitons occurs at the edge of the heterostructure. The modulation of exciton flux by Vg at room temperature is illustrated in diagram (g). Reprinted with permission from Ref. [114]

Fig. 9 2D heterostructures in optoelectronic applications. a Schematic diagram of TMD/TMD heterostructure with a graphene contact. Reprinted with permission from Ref. [43]. Schematic and optical picture of optoelectronic memory based on h-BN/WSe2 heterostructure (b) and the modulation of programming, reading and erasing state by Vg and incident illumination (c), and the wavelength-dependent PR (d). Reprinted with permission from Ref. [113]. Schematic and optical picture (e, f) of the multi-gate exciton device. The excitation region is marked by the red circle, and the recombination of the interlayer excitons occurs at the edge of the heterostructure. The modulation of exciton flux by Vg at room temperature is illustrated in diagram (g). Reprinted with permission from Ref. [114]

Table 3 The performances of 2D-heterostructure-based photodetectors

11 13 table3

    Moreover, the optoelectronic memories based on 2D heterostructures have been designed which can accumulate and release photo-generated carriers under an electric field and light irradiation. In addition, the introduction of 2D materials makes it possible to realize miniature, flexible and low-energy-consumption optoelectronic storage [106]. Recently Du Xiang et al. [113] successfully fabricated a multi-bit nonvolatile optoelectronic memory based on a stacked WSe2/hBN heterostructure as shown in Fig. 9b, which is also a filter-free color image sensor. The device can be programmed to read and erase by adjusting the gate voltage and the light pulse. The corresponding band alignment is shown in Fig. 9. The positive charges can be stored in h-BN even after removing the negative gate and switching off the light (Fig. 9c). The device has performed a retention time over 4.5×104 s and possesses over 128 (7 bit) storage states. Interestingly, the storage states at different wavelengths are highly distinct (Fig. 9d), indicating excellent wavelength distinguishing capability of the WSe2/hBN optoelectronic memory.
    In Addition, the reduced Coulomb screening in the atomically thin crystals led to a dramatic increase in the exciton binding energy, and therefore stabilized these excitons at room temperature. Recently, Dmitrii Unuchek et al. [114] reported excitonic devices made of MoS2/WSe2 van der Waals heterostructures encapsulated in hBN (Fig. 9e) demonstrating electrically controlled multi-gate transistor actions at room temperature. The interlayer exciton was excited in the heterostructure and the recombination was successfully observed at the edge of the heterostructure (Fig. 9g). The device was switched by adjusting the Vg1, reaching an on/off ratio of 100. Furthermore, under the modulation of the bias voltage, the excitons would drift (forward bias voltage) to the low potential or be limited in the potential hydrazine (reverse bias voltage), so the diffusion distance of the exciton could be adjusted to reach 5μm under a forward bias voltage.
4.3 Spintronic and Valleytronic Devices
    2D materials have excellent spin-valley properties, for example, graphene exhibits outstanding electrical, thermal, and mechanical properties. It also displays a very long spin diffusion length up to room temperature that facilitates the spin injection, manipulation, and detection in an integrated device leading to the realization of scalable and ultra-fast nonvolatile logic circuits with ultra-low energy dissipation. More recently, the spin valve effect in FM/2D-material/FM sandwich-like magnetic junction has been observed [115-118]. Particularly, in certain FM/G/FM junctions (FM=Ni, Co etc.), the lattice mismatch between graphene and FM is very small, and simultaneously, a spin filtering effect is theoretically permitted. As is shown in Fig. 10a [119], only the spin states at Dirac point in FM can be injected into graphene and the calculation indicates that only minority spins exist at the Dirac point. The introduction of 2D heterostructures in magnetic tunneling junctions can efficiently modulate the result of the spin filter due to the different spin polarizations at different interfaces. Muhammad Zahir Iqbal et al. [120] successfully observed the negative tunnel magnetoresistance (TMR) of -0.85% in a NiFe/G–hBN/Co magnetic junction under room temperature (Fig. 10b). However, the quality of the interfaces and the lattice orientation between different layers are very crucial.

Fig. 10 Spintronic and valleytronic applications of 2D heterostructures. a The calculated majority and minority spin states of Co (①-②) and Ni (③-④) and the Fermi surface of graphene (⑤), and the color bar indicates the number of Fermi surface sheets. Reprinted with permission from Ref. [119]. b TMR of the NiFe/Gra–hBN/Co magnetic junction at a different temperature. Reprinted with permission from Ref. [120]. WSe2 on the SiO2 substrate and the EuS substrate (c), and the valley splitting (d) and magnetization (e) in the WSe2/EuS structure under sweeping external vertical magnetic field at different temperatures. Reprinted with permission from Ref. [126]. Schematic diagram of MoS2/graphene heterostructure and the Hanle measurement (f, g) and the Hanle signal (h) detected after the laser excitation on the heterostructure region at a temperature of 10 k. Reprinted with permission from Ref. [127]

Fig. 10 Spintronic and valleytronic applications of 2D heterostructures. a The calculated majority and minority spin states of Co (①-②) and Ni (③-④) and the Fermi surface of graphene (⑤), and the color bar indicates the number of Fermi surface sheets. Reprinted with permission from Ref. [119]. b TMR of the NiFe/Gra–hBN/Co magnetic junction at a different temperature. Reprinted with permission from Ref. [120]. WSe2 on the SiO2 substrate and the EuS substrate (c), and the valley splitting (d) and magnetization (e) in the WSe2/EuS structure under sweeping external vertical magnetic field at different temperatures. Reprinted with permission from Ref. [126]. Schematic diagram of MoS2/graphene heterostructure and the Hanle measurement (f, g) and the Hanle signal (h) detected after the laser excitation on the heterostructure region at a temperature of 10 k. Reprinted with permission from Ref. [127]

    Besides, monolayer TMDs with a broken inversion symmetry own two degenerated inequivalent valleys that are related by time-reversal symmetry [121]. This property and the strong spin-orbit coupling are responsible for the unique physics in TMDs, especially the coupled spin and valley of freedom. With a direct band gap, TMDs offer the opportunity to excite carriers selectively within a particular valley with a specific valley pseudospin using circularly polarized light. Also, the valley Hall effects can be observed in a certain doped TMD sample [122, 123].
    However, the external control of valleytronic devices remains a challenge because the conditions of lifting the valley degeneracy by Zeeman splitting in a single 2D material are very demanding, that usually require strong magnetic field and low temperature [124], while tailoring graphene magnetic properties by structural engineering such as doping [10] and defects [125] inevitably increase the complexity in operations.
    Utilizing the interfacial magnetic exchange field (MEF) from a ferromagnetic substrate greatly enhanced valley splitting in monolayer TMDs has been found recently. Chuan Zhao et al. [126] successfully put the WSe2 monolayer on Si/SiO2 and on ferromagnetic EuS substrates. The magnetic field was perpendicular to the plane (Fig. 10c). In WSe2 on the SiO2 substrate, the ΔE was 1.5 meV at 7 T and 7 k. But in WSe2 on the EuS, the valley splitting reached 3.9 meV. Figures 10d, e show the measurements of the systematic field and temperature dependences of the splitting. With the field increased further, the rate of ΔEex increase got slower and then tended to saturation at high magnetic fields. Also, with the increasing of temperature, ΔEex decreased accordingly. Such behaviors are very similar to the field- and the temperature-dependent magnetization of EuS.
    Another thought of combining is to select another material whose properties can compensate for the setbacks of the material. Typically, for the graphene and TMDs in spintronics [128], the long-distance spin transport capability of graphene has been demonstrated at room temperature [129], but the lack of the SOC made it complicated to generate pure spin current. In contrast, spin/valley polarization can be efficiently generated in monolayer TMDs such as WS2 and MoS2 via external excitation field. Recently lateral spin or valley transport have been realized at room temperature by fabricating MoS2/few-layer graphene hybrid spin valves as shown in Fig. 10f. Yunqiu Kelly Luo et al. [127] fabricated the monolayer MoS2/few-layer-graphene hybrid spin valves and successfully injected the spin signal generated by circularly polarized light excitation on the TMD layer into the graphene layer. Figure 10g is the illustration of optical spin injection, lateral spin transport, and electrical spin detection in a monolayer MoS2/few-layer-graphene hybrid spin valve structure. Figure 10h shows the electrical spin signal VNL as a function of external magnetic field By under T=10 k. The spin signal can still be easily detected at room temperature but it’s about 5 times smaller due to the increased intervalley scattering which reduces the valley polarization in monolayer MoS2.

5 Summary and Outlook

    It is clear that remarkable progress has been achieved in the study of 2D heterostructures, such as the development in realizing controllable CVD growth of planar heterostructures, the distinctive properties of magnetism and spatially-separated excitons, as well as the various design and effective modulation of devices. These advances are fundamental bases for future scalable applications of 2D heterostructures. Additionally, 2D heterostructures can display unique physics phenomena due to the coupling effect and the electronic transport at the junction, offering an ideal platform for fundamental research in physics.
    Nevertheless, there are still great challenges in the research of 2D heterostructures. At the first, successful synthesis of vertical heterostructures by CVD has been rare and more often the stacked heterostructures were fabricated by artificial transfer that needed a proper annealing process, a procedure that could cause damage to the samples. Thus, the priority is to develop new strategies for scalable and controllable fabrication of 2D heterostructures with high-quality interfaces and certain stack orientation. While the CVD synthesis is an ideal method its gas system needs to be optimized to for better control of the reaction conditions. As for deterministic transfer method, in-depth studies on surface physical chemistries are needed for the invention of new types of transfer carriers. Secondly, new materials, such as layered magnetic materials with high TC, need to be created, which will enable a lot of new combinations of 2D heterostructures. Thirdly, to modulate the magnetic properties, band structure and charge transport characteristics of 2D heterostructures, conducting external electric field, optical field, magnetic field, strain treatment, together with the structural and surface engineering on the materials will be meaningful and helpful research points. What’s more, for the fabrication and design of devices, the selection of proper materials as the electrode contact for reducing the RC remains a tough task. The structural design of new devices to include floating-gate, multi-gate, and array structures is also very challenging.
    In order to further explore the properties and applications of 2D heterostructures, several opinions could be taken into consideration for future development. Firstly, the integration of layered ferromagnetic insulator and monolayer TMD will greatly enhance the valley splitting in TMD, so the synthesis of a layered ferromagnetic insulator material whose TC is over the room temperature could enable the development of valley-storage or valley-logical devices. Secondly, mix-dimension devices based on 0D-2D, 1D-2D or 3D-2D heterostructures are also an effective way to solve the current problems. By combining quantum dots, nanowire, nanoribbon or waveguide structures [130] with 2D sheets, more novel properties, such as interfacial disorders, will be realized. Finally, the fabrication strategy needs further improvement. For the CVD method, modulation of gas flow direction and temperature is a key factor for controlled reaction. For the transfer method, the development of a new transfer media layer and an automatic strategy is helpful to realize scalable fabrication and high yield. Hence, the heterostructures of 2D materials are promising for exploring new physics in 2D materials and realizing functional applications. The future of 2D heterostructures are full of massive novel possibilities.

Acknowledgments

    Yanping Liu would like to acknowledge Ye Yu for useful discussions. This work was supported by NSF of China (Grant No. 61775241) and partly by the Innovation-driven Project (Grant No. 2017CX019) and Youth Innovation Team (Grant No. 2019012) of CSU. Z. W. L. acknowledges the funding support from the Australian Research Council (ARC Discovery Projects, DP180102976).

References

[1] K.S. Novoselov, A.K. Geim, S.V. Morozov, D. Jiang, Y. Zhang, S.V. Dubonos, I.V. Grigorieva, A.A. Firsov, Electric field effect in atomically thin carbon films. Science 306(5696), 666-669 (2004). http://dx.doi.org/10.1126/science.1102896
[2] M. Osada, T. Sasaki, Two-dimensional dielectric nanosheets: novel nanoelectronics from nanocrystal building blocks. Adv. Mater. 24 (2), 210-228 (2012). http://dx.doi.org/10.1002/adma.201103241
[3] L.M. Malard, J. Nilsson, D.C. Elias, J.C. Brant, F. Plentz et al., Probing the electronic structure of bilayer graphene by Raman scattering. Phys. Rev. B 76(20), 201401 (2007). https://doi.org/10.1103/PhysRevB.76.201401
[4] V. Tran, R. Soklaski, Y.F. Liang, L. Yang, Layer-controlled band gap and anisotropic excitons in few-layer black phosphorus. Phys. Rev. B 89(23), 235319 (2014). https://doi.org/10.1103/PhysRevB.89.235319
[5] K.F. Mak, C. Lee, J. Hone, J. Shan, T.F. Heinz, Atomically Thin MoS2: A new direct-gap semiconductor. Phys. Rev. Lett. 105(13), 136805 (2010). https://doi.org/10.1103/PhysRevLett.105.136805
[6] L. Xie, M.Z. Liao, S.P. Wang, H. Yu, L.J. Du et al., Graphene-contacted ultrashort channel monolayer MoS2 transistors. Adv. Mater. 29(37), 1702522 (2017). https://doi.org/10.1002/adma.201702522
[7] Y.P. Liu, W.S. Lew, S. Goolaup, Z.X. Shen, L. Sun, T.J. Zhou, S.K. Wong, Observation of the semiconductor-metal transition behavior in monolayer graphene. Carbon 50(6), 2273-2279 (2012). https://doi.org/10.1016/j.carbon.2012.01.046
[8] A. Allain, J.H. Kang, K. Banerjee, A. Kis, Electrical contacts to two-dimensional semiconductors. Nat. Mater. 14(12), 1195-1205 (2015). https://doi.org/10.1038/nmat4452
[9] P.R.Y. Gangavarapu, P.C. Lokesh, K.N. Bhat, A.K. Naik, Towards barrier free contacts to n-type cntfets using graphene electrodes. 2016 Ieee Nanotechnology Materials and Devices Conference (Nmdc, 2016). https://doi.org/10.1109/NMDC.2016.7777064
[10] J. Du, C.X. Xia, W.Q. Xiong, X. Zhao, T.X. Wang, Y. Jia, Tuning the electronic structures and magnetism of two-dimensional porous C2N via transition metal embedding. Phys. Chem. Chem. Phys. 18(32), 22678-22686 (2016). https://doi.org/10.1039/C6CP03210A
[11] Y.P. Liu, S. Goolaup, W.S. Lew, I. Purnama, M.C. Sekhar, T.J. Zhou, S.K. Wong, Excitonic bandgap dependence on stacking configuration in four layer graphene. Appl. Phys. Lett. 103(16), 163108 (2013). https://doi.org/10.1063/1.4825263
[12] C.R. Dean, A.F. Young, I. Meric, C. Lee, L. Wang et al., Boron nitride substrates for high-quality graphene electronics. Nat. Nanotechnol. 5(10), 722-726 (2010). http://dx.doi.org/10.1038/nnano.2010.172
[13] W.J. Jie, Z.B. Yang, G.X. Bai, J.H. Hao, Luminescence in 2D materials and van der waals heterostructures. Adv. Opt. Mater. 6(10), 1701296 (2018). https://doi.org/10.1002/adom.201701296
[14] K.S. Novoselov, A. Mishchenko, A. Carvalho, A.H.C. Neto, 2D materials and van der Waals heterostructures. Science 353(6298), 9439 (2016). https://doi.org/10.1126/science.aac9439
[15] O.L. Sanchez, D. Ovchinnikov, S. Misra, A. Allain, A. Kis, Valley polarization by spin injection in a light-emitting van der waals heterojunction. Nano Lett. 16(9), 5792-5797 (2016). http://dx.doi.org/10.1021/acs.nanolett.6b02527.
[16] C.L. Tan, H. Zhang, Epitaxial growth of hetero-nanostructures based on ultrathin two-dimensional nanosheets. J. Am. Chem. Soc. 137(38), 12162-12174 (2015). http://dx.doi.org/10.1021/jacs.5b03590.
[17] H.Y. Yu, Y. Wang, Q.J. Tong, X.D. Xu, W. Yao, Anomalous light cones and valley optical selection rules of interlayer excitons in twisted heterobilayers. Phys. Rev. Lett. 115(18), 187002 (2015). https://doi.org/10.1103/PhysRevLett.115.187002
[18] F. Haque, T. Daeneke, K. Kalantar-zadeh, J. Ou, Two-dimensional transition metal oxide and chalcogenide-based photocatalysts. Nano-Micro Lett. 10, 23 (2018). https://doi.org/10.1007/s40820-017-0176-y
[19] X. Zhou, X.Z. Hu, J. Yu, S.Y. Liu, Z.W. Shu et al., 2D layered material-based van der waals heterostructures for optoelectronics. Adv. Funct. Mater. 28(14), 1706587 (2018). https://doi.org/10.1002/adfm.201706587
[20] J.A. Leon, N.C. Mamani, A. Rahim, L.E. Gomez, M.A.P.d. Silva, G. M. Gusev, Transferring few-layer graphene sheets on hexagonal boron nitride substrates for fabrication of graphene devices. Graphene 25-35, 48096 (2014). http://dx.doi.org/10.4236/graphene.2014.33005
[21] A. Castellanos-Gomez, M. Buscema, R. Molenaar, V. Singh, L. Janssen, H.S.J. van der Zant, G. A. Steele, Deterministic transfer of two-dimensional materials by all-dry viscoelastic stamping. 2D Mater. 1(1), 011002 (2014). 
[22] P. Pedrinazzi, J.M. Caridad, D.M.A. Mackenzie, F. Pizzocchero, L. Gammelgaard et al., High-quality graphene flakes exfoliated on a flat hydrophobic polymer. Appl. Phys. Lett. 112(3), 033101 (2018). https://doi.org/10.1063/1.5009168
[23] P.J. Zomer, S.P. Dash, N. Tombros, B. J. van Wees, A transfer technique for high mobility graphene devices on commercially available hexagonal boron nitride. Appl. Phys. Lett. 99(23), 232104 (2011). https://doi.org/10.1063/1.3665405
[24] J.I.J. Wang, Y.F. Yang, Y.A. Chen, K. Watanabe, T. Taniguchi, H.O. H. Churchill, P. Jarillo-Herrero, Electronic transport of encapsulated graphene and wse2 devices fabricated by pick-up of prepatterned hBN. Nano Lett. 15(3), 1898-1903 (2015). http://dx.doi.org/10.1021/nl504750f.
[25] R. Frisenda, E. Navarro-Moratalla, P. Gant, D.P. De Lara, P. Jarillo-Herrero, R.V. Gorbachev, A. Castellanos-Gomez, Recent progress in the assembly of nanodevices and van der Waals heterostructures by deterministic placement of 2D materials. Chem. Soc. Rev. 47(1), 53-68 (2018). http://dx.doi.org/10.1039/c7cs00556c
[26] M.A. Meitl, Z.T. Zhu, V. Kumar, K.J. Lee, X. Feng et al., Transfer printing by kinetic control of adhesion to an elastomeric stamp. Nat. Mater. 5(1), 33-38 (2006). http://dx.doi.org/10.1038/nmat1532
[27] Y.J. Gong, J.H. Lin, X.L. Wang, G. Shi, S.D. Lei et al., Vertical and in-plane heterostructures from WS2/MoS2 monolayers. Nat. Mater. 13(12), 1135-1142 (2014). http://dx.doi.org/10.1038/Nmat4091
[28] X.F. Li, M.W. Lin, J.H. Lin, B. Huang, A.A. Puretzky et al., Two-dimensional GaSe/MoSe2 misfit bilayer heterojunctions by van der Waals epitaxy. Sci. Adv. 2(4), 1501882 (2016). https://doi.org/10.1126/sciadv.1501882
[29] L. Fu, Y.Y. Sun, N. Wu, R.G. Mendes, L.F. Chen et al., Direct growth of MoS2/h-BN heterostructures via a sulfide-resistant alloy. Acs Nano 10(2), 2063-2070 (2016). http://dx.doi.org/10.1021/acsnano.5b06254
[30] B.Y. Zheng, C. Ma, D. Li, J.Y. Lan, Z. Zhang et al., Band alignment engineering in two-dimensional lateral heterostructures. J. Am. Chem. Soc. 140(36), 11193-11197 (2018). http://dx.doi.org/10.1021/jacs.8b07401
[31] P.K. Sahoo, S. Memaran, Y. Xin, L. Balicas, H.R. Gutierrez, One-pot growth of two-dimensional lateral heterostructures via sequential edge-epitaxy. Nature 553(7686), 63-67 (2018). http://dx.doi.org/10.1038/nature25155
[32] Z.W. Zhang, P. Chen, X.D. Duan, K.T. Zang, J. Luo, X.F. Duan, Robust epitaxial growth of two-dimensional heterostructures, multiheterostructures, and superlattices. Science 357(6353), 788-792 (2017). https://doi.org/10.1126/science.aan6814
[33] B. Zheng, C. Ma, D. Li, J. Lan, Z. Zhang et al., Band alignment engineering in two-dimensional lateral heterostructures. J. Am. Chem. Soc. 140(36), 11193-11197 (2018). http://dx.doi.org/10.1021/jacs.8b07401
[34] C. Gong, H.J. Zhang, W. Wang, L. Colombo, R.M. Wallace, K. Cho, Band alignment of two-dimensional transition metal dichalcogenides: Application in tunnel field effect transistors. Appl. Phys. Lett. 107(13), 053513 (2015). https://doi.org/10.1063/1.4932088
[35] F. Withers, O. Del Pozo-Zamudio, A. Mishchenko, A.P. Rooney, A. Gholinia et al., Light-emitting diodes by band-structure engineering in van der Waals heterostructures. Nature Mater. 14(3), 301-306 (2015). https://doi.org/10.1038/nmat4205
[36] W.G. Xu, W.W. Liu, J.F. Schmidt, W.J. Zhao, X. Lu et al., Correlated fluorescence blinking in two-dimensional semiconductor heterostructures. Nature 541(7635), 62-67 (2017). http://dx.doi.org/10.1038/nature20601
[37] Y. Hattori, T. Taniguchi, K. Watanabe, K. Nagashio, Determination of carrier polarity in fowler-nordheim tunneling and evidence of fermi level pinning at the hexagonal boron nitride/metal interface. ACS Appl. Mater. Interfaces 10(14), 11732-11738 (2018). https://doi.org/10.1021/acsami.7b18454
[38] P. Bampoulis, R. van Bremen, Q.R. Yao, B. Poelsema, H.J. W. Zandvliet, K. Sotthewes, Defect dominated charge transport and fermi level pinning in MoS2/metal contacts. ACS Appl. Mater. Interfaces 9(22), 19278-19286 (2017). http://dx.doi.org/10.1021/acsami.7b02739
[39] T. Le Quang, V. Cherkez, K. Nogajewski, M. Potemski, M.T. Dau, M. Jamet, P. Mallet, J. Y. Veuillen, Scanning tunneling spectroscopy of van der Waals graphene/semiconductor interfaces: absence of Fermi level pinning. 2D Mater. 4(3), 035019 (2017). http://iopscience.iop.org/article/10.1088/2053-1583/aa7b03
[40] C.R. Woods, L. Britnell, A. Eckmann, R.S. Ma, J.C. Lu, Commensurate-incommensurate transition in graphene on hexagonal boron nitride. Nature Phys. 10(6), 451-456 (2014). http://dx.doi.org/10.1038/Nphys2954
[41] B. Li, L. Huang, M.Z. Zhong, Y. Li, Y. Wang, J.B. Li, Z.M. Wei, Direct vapor phase growth and optoelectronic application of large band offset SnS2/MoS2 vertical bilayer heterostructures with high lattice mismatch. Adv. Electron. Mater. 2(11), 1600298 (2016). https://doi.org/10.1002/aelm.201600298
[42] K.H. Liu, L.M. Zhang, T. Cao, C.H. Jin, D.A. Qiu et al., Evolution of interlayer coupling in twisted molybdenum disulfide bilayers. Nat. Commun. 5, 4966 (2014). https://doi.org/10.1038/ncomms5966
[43] H.J. Tan, W.S. Xu, Y.W. Sheng, C.S. Lau, Y. Fan et al., Lateral graphene-contacted vertically stacked WS2/MoS2 hybrid photodetectors with large gain. Adv. Mater. 29(46), 1702917 (2017). https://doi.org/10.1002/adma.201702917
[44] F. Gong, W.J. Luo, J.L. Wang, P. Wang, H.H. Fang et al., High-sensitivity floating-gate phototransistors based on WS2 and MoS2. Adv. Funct. Mater. 26(33), 6084-6090 (2016). http://dx.doi.org/10.1002/adfm.201601346
[45] A. Dankert, S.P. Dash, Electrical gate control of spin current in van der Waals heterostructures at room temperature. Nat. Commun. 8, 16093 (2017). https://doi.org/10.1038/ncomms16093
[46] J.L. Wang, H.H. Fang, X.D. Wang, X.S. Chen, W. Lu, W.D. Hu, Recent progress on localized field enhanced two-dimensional material photodetectors from ultraviolet-visible to infrared. Small 13(35), 1700894 (2017). https://doi.org/10.1002/smll.201700894
[47] M.Z. Bellus, F. Ceballos, H.Y. Chiu, H. Zhao, Tightly bound trions in transition metal dichalcogenide heterostructures. ACS Nano 9(6), 6459-6464 (2015). http://dx.doi.org/10.1021/acsnano.5b02144
[48] L.B. Drissi, F.Z. Ramadan, N.B.J. Kanga, Optoelectronic properties in 2D GeC and SiC hybrids: DFT and many body effect calculations. Mater. Res. Express 5(1), 015061 (2018). http://iopscience.iop.org/article/10.1088/2053-1591/aaa862
[49] X.P. Hong, J. Kim, S.F. Shi, Y. Zhang, C.H. Jin et al., Ultrafast charge transfer in atomically thin MoS2/WS2 heterostructures. Nat. Nanotechnol. 9(9), 682-686 (2014). http://dx.doi.org/10.1038/Nnano.2014.167
[50] H.H. Hung, J.S. Wu, K. Sun, C.K. Chiu, Engineering of many-body Majorana states in a topological insulator/s-wave superconductor heterostructure. Sci. Rep. 7, 3499 (2017). https://doi.org/10.1038/s41598-017-02493-7
[51] P. Rivera, J.R. Schaibley, A.M. Jones, J.S. Ross, S F. Wu et al., Observation of long-lived interlayer excitons in monolayer MoSe2-WSe2 heterostructures. Nat. Commun. 6, 6242 (2015). https://doi.org/10.1038/ncomms7242
[52] M. Li, D. Esseni, G. Snider, D. Jena, H.G. Xing, Single particle transport in two-dimensional heterojunction interlayer tunneling field effect transistor. J. Appl. Phys. 115(7), 074508 (2014). https://doi.org/10.1063/1.4866076
[53] X. Yan, C.S. Liu, C. Li, W.Z. Bao, S.J. Ding, D.W. Zhang, P. Zhou, Tunable SnSe2/WSe2 Heterostructure Tunneling Field Effect Transistor. Small 13(34), 1701478 (2017). https://doi.org/10.1002/smll.201701478
[54] T. Yamaoka, H.E. Lim, S. Koirala, X.F. Wang, K. Shinokita et al., Efficient photocarrier transfer and effective photoluminescence enhancement in type i monolayer MoTe2/WSe2 heterostructure. Adv. Funct. Mater. 28(35), 1801021 (2018). https://doi.org/10.1002/adfm.201801021
[55] Z. Cai, M. Cao, Z.P. Jin, K.Y. Yi, X.S. Chen, D.C. Wei, Large photoelectric-gating effect of two-dimensional van-der-Waals organic/tungsten diselenide heterointerface. Npj 2D Mater. Appl. 2, 21 (2018). http://iopscience.iop.org/article/10.1088/2053-1591/aaa862
[56] S. Bertolazzi, D. Krasnozhon, A. Kis, Nonvolatile memory cells based on MoS2/graphene heterostructures. ACS Nano 7(4), 3246-3252 (2013). http://dx.doi.org/10.1021/nn3059136
[57] M.S. Choi, G.H. Lee, Y.J. Yu, D.Y. Lee, S.H. Lee, P. Kim, J. Hone, W.J. Yoo, Controlled charge trapping by molybdenum disulphide and graphene in ultrathin heterostructured memory devices. Nat. Commun. 4, 1624 (2013).https://www.nature.com/articles/ncomms2652
[58] Y. Zhang, Y.B. Yuan, J.S. Huang, Detecting 100 fW cm-2 light with trapped electron gated organic phototransistors. Adv. Mater. 29(5), 1603969 (2017). https://doi.org/10.1002/adma.201603969
[59] J.L. Wang, X.M. Zou, X.H. Xiao, L. Xu, C.L. Wang et al., Floating gate memory-based monolayer MoS2 transistor with metal nanocrystals embedded in the gate dielectrics. Small 11(2), 208-213 (2015). http://dx.doi.org/10.1002/smll.201401872
[60] Y.P. Liu, W.S. Lew, Z.W. Liu, Observation of anomalous resistance behavior in bilayer graphene. Nanoscale Res. Lett. 12, 48 (2017). https://doi.org/10.1186/s11671-016-1792-z
[61] Y.P. Liu, Z.W. Liu, W.S. Lew, Q.J. Wang, Temperature dependence of the electrical transport properties in few-layer graphene interconnects. Nanoscale Res. Lett. 8, 335 (2013). https://doi.org/10.1186/1556-276X-8-335
[62] Q.A. Vu, Y.S. Shin, Y.R. Kim, V.L. Nguyen, W.T. Kang et al., Two-terminal floating-gate memory with van der Waals heterostructures for ultrahigh on/off ratio. Nat. Commun. 7, 12725 (2016). https://doi.org/10.1038/ncomms12725
[63] H.L. Chen, X.W. Wen, J. Zhang, T.M. Wu, Y.J. Gong et al., Ultrafast formation of interlayer hot excitons in atomically thin MoS2/WS2 heterostructures. Nat. Commun. 7, 12512 (2016). https://doi.org/10.1038/ncomms12512
[64] X.W. Wen, H.L. Chen, T.M. Wu, Z.H. Yu et al., Ultrafast probes of electron-hole transitions between two atomic layers. Nat. Commun. 9, 1859 (2018). https://doi.org/10.1038/s41467-018-04291-9
[65] A.T. Hanbicki, H.J. Chuang, M.R. Rosenberger, C.S. Hellberg, S.V. Sivaram, K.M. McCreary, I.I. Mazin, B. T. Jonker, Double indirect interlayer exciton in a MoSe2/WSe2 van der waals heterostructure. ACS Nano 12(5), 4719-4726 (2018). http://dx.doi.org/10.1021/acsnano.8b01369
[66] S. Latini, K.T. Winther, T. Olsen, K.S. Thygesen, Interlayer excitons and band alignment in MoS2/hBN/WSe2 van der waals heterostructures. Nano Lett. 17(2), 938-945 (2017). http://dx.doi.org/10.1021/acs.nanolett.6b04275
[67] J.S. Ross, P. Rivera, J. Schaibley, E. Lee-Wong, H.Y. Yu et al., Interlayer exciton optoelectronics in a 2D heterostructure p-n junction. Nano Lett. 17(2), 638-643 (2017). http://dx.doi.org/10.1021/acs.nanolett.6b03398
[68] P. Rivera, K.L. Seyler, H.Y. Yu, J.R. Schaibley, J.Q. Yan et al., Valley-polarized exciton dynamics in a 2D semiconductor heterostructure. Science 351(6274), 688-691 (2016). http://dx.doi.org/10.1126/science.aac7820
[69] T. Deilmann, K.S. Thygesen, Interlayer trions in the MoS2/WS2 van der Waals heterostructure. Nano Lett. 18(2), 1460-1465 (2018). http://dx.doi.org/10.1021/acs.nanolett.7b05224
[70] Y.P. Liu, W.S. Lew, L. Sun, Enhanced weak localization effect in few-layer graphene. Phys. Chem. Chem. Phys. 13(45), 20208-20214 (2011). https://doi.org/10.1039/c1cp22250c
[71] L. Y. Ping, G. Sarjoosing, M. Chandrasekhar, L. W. Siang, W. S. J. A. N. Kai, Effect of magnetic field on the electronic transport in trilayer graphene. ACS Nano 4(12), 7087-7092 (2010). https://doi.org/DOI: 10.1021/nn101296x
[72] J.S. Qi, X. Li, Q. Niu, J. Feng, Giant and tunable valley degeneracy splitting in MoTe2. Phys. Rev. B 92(12), 121403 (2015). https://doi.org/10.1103/PhysRevB.92.121403
[73] B.Z. Zhou, S.W. Ji, Z. Tian, W.J. Cheng, X.C. Wang, W.B. Mi, Proximity effect induced spin filtering and gap opening in graphene by half-metallic monolayer Cr2C ferromagnet. Carbon 132, 25-31 (2018). http://dx.doi.org/10.1016/j.carbon.2018.02.044
[74] P. Wei, S. Lee, F. Lemaitre, L. Pinel, D. Cutaia et al., Strong interfacial exchange field in the graphene/EuS heterostructure. Nat. Mater. 15(7), 711-716 (2016). http://dx.doi.org/10.1038/Nmat4603
[75] H.X. Yang, A. Hallal, D. Terrade, X. Waintal, S. Roche, M. Chshiev, Proximity effects induced in graphene by magnetic insulators: first-principles calculations on spin filtering and exchange-splitting gaps. Phys. Rev. Lett. 110(4), 046603 (2013). https://doi.org/10.1103/PhysRevLett.110.046603
[76] K.L. Seyler, D. Zhong, B. Huang, X.Y. Linpeng, N.P. Wilson et al., Valley manipulation by optically tuning the magnetic proximity effect in WSe2/CrI3 heterostructures. Nano Lett. 18(6), 3823-3828 (2018). http://dx.doi.org/10.1021/acs.nanolett.8b01105
[77] B. Huang, G. Clark, E. Navarro-Moratalla, D.R. Klein, R. Cheng, Layer-dependent ferromagnetism in a van der Waals crystal down to the monolayer limit. Nature 546(7657), 270-273 (2017). http://dx.doi.org/10.1038/nature22391
[78] J.U. Lee, S. Lee, J.H. Ryoo, S. Kang, T.Y. Kim et al., Ising-type magnetic ordering in atomically thin FePS3. Nano Lett. 16(12), 7433-7438 (2016). http://dx.doi.org/10.1021/acs.nanolett.6b03052
[79] J. Du, C.X. Xia, W.Q. Xiong, T.X. Wang, Y. Jia, J.B. Li, Two-dimensional transition-metal dichalcogenides-based ferromagnetic van der Waals heterostructures. Nanoscale 9 (44), 17585-17592 (2017). http://dx.doi.org/10.1039/c7nr06473j
[80] Y.P. Liu, I. Yudhistira, M. Yang, E. Laksono, Y.Z. Luo et al., Phonon-mediated colossal magnetoresistance in graphene/black phosphorus heterostructures. Nano Lett. 18(6), 3377-3383 (2018). http://dx.doi.org/10.1021/acs.nanolett.8b00155
[81] M. Bonilla, S. Kolekar, Y.J. Ma, H.C. Diaz, V. Kalappattil et al., Strong room-temperature ferromagnetism in VSe2 monolayers on van der Waals substrates. Nat. Nanotechnol. 13(4), 289-293 (2018). http://dx.doi.org/10.1038/s41565-018-0063-9
[82] Z.Y. Fei, B. Huang, P. Malinowski, W.B. Wang, T.C. Song et al., Two-dimensional itinerant ferromagnetism in atomically thin Fe3GeTe2. Nat Mater. 17(9), 778-782 (2018). http://dx.doi.org/10.1038/s41563-018-0149-7
[83] Y. Deng, Y. Yu, Y. Song, J. Zhang, N.Z. Wang et al., Gate-tunable room-temperature ferromagnetism in two-dimensional Fe3GeTe2. Nature 563, 94-99 (2018). http://dx.doi.org/10.1038/s41586-018-0626-9
[84] C. Si, J. Zhou, Z.M. Sun, Half-metallic ferromagnetism and surface functionalization-induced metal-insulator transition in graphene-like two-dimensional Cr2C crystals. ACS Appl. Mater. Interfaces 7(31), 17510-17515 (2015). http://dx.doi.org/10.1021/acsami.5b05401
[85] M. Kan, J. Zhou, Q. Sun, Y. Kawazoe, P. Jena, The intrinsic ferromagnetism in a MnO2 monolayer. J. Phys. Chem. Lett. 4(20), 3382-3386 (2013). http://dx.doi.org/10.1021/jz4017848
[86] Y. Zhang, J.M. Pang, M.G. Zhang, X. Gu, L. Huang, Two-dimensional Co2S2 monolayer with robust ferromagnetism. Sci. Rep. 7, 7 (2017). https://doi.org/10.1038/s41598-017-00035-9 [87] M. Ormaza, L. Fernandez, M. Ilyn, A. Magana, B. Xu et al., High temperature ferromagnetism in a GdAg2 monolayer. Nano Lett. 16(7), 4230-4235 (2016). http://dx.doi.org/10.1021/acs.nanolett.6b01197
[88] M. Kan, S. Adhikari, Q. Sun, Ferromagnetism in MnX2 ( X = S, Se) monolayers. Phys. Chem. Chem. Phys. 16(10), 4990-4994 (2014). http://dx.doi.org/10.1039/c3cp55146f
[89] Y.P. Liu, W.S. Lew, S. Goolaup, H.F. Liew, S.K. Wong, T.J. Zhou, Observation of oscillatory resistance behavior in coupled bernal and rhombohedral stacking graphene. ACS Nano 5(7), 5490-5498 (2011). https://doi.org/10.1021/nn200771e
[90] S. Roche, J. Aring;kerman, B. Beschoten, J.C. Charlier, M. Chshiev et al., Graphene spintronics: the European Flagship perspective. 2D Mater. 2(3), 030202 (2015). http://iopscience.iop.org/article/10.1088/2053-1583/2/3/030202
[91] M.W. Si, P.Y. Liao, G. Qiu, Y.Q. Duan, P.D.D. Ye, Ferroelectric field-effect transistors based on MoS2 and CuInP2S6 two-dimensional van der Waals heterostructure. ACS Nano 12(7), 6700-6705 (2018). http://dx.doi.org/10.1021/acsnano.8b01810
[92] Y.P. Liu, K. Tom, X.W. Zhang, S. Lou, Y. Liu, J. Yao, Alloying effect on bright-dark exciton states in ternary monolayer MoxW1-xSe2. New J. Phys. 19, 073018 (2017). http://iopscience.iop.org/article/10.1088/1367-2630/aa6d39
[93] Y.P. Liu, Q.L. Xia, J. He, Z.W. Liu, Direct observation of high photoresponsivity in pure graphene photodetectors. Nanoscale Res. Lett. 12, 93 (2017). https://doi.org/10.1186/s11671-017-1827-0
[94] Y.P. Liu, K. Tom, X. Wang, C.M. Huang, H.T. Yuan et al., Dynamic control of optical response in layered metal chalcogenide nanoplates. Nano Lett. 16(1), 488-496 (2016). https://doi.org/10.1021/acs.nanolett.5b04140
[95] X.C. Yu, Z.G. Dong, Y.P. Liu, T. Liu, J. Tao et al., A high performance, visible to mid-infrared photodetector based on graphene nanoribbons passivated with HfO2. Nanoscale 8(1), 327-332 (2016). https://doi.org/10.1039/C5NR06869J
[96] W.G. Luo, Y.F. Cao, P.G. Hu, K.M. Cai, Q. Feng et al., Gate tuning of high-performance inse-based photodetectors using graphene electrodes. Adv. Opt. Mater. 3(10), 1418-1423 (2015). https://doi.org/10.1002/adom.201500190
[97] Q. Lv, F. Yan, X. Wei, K. Wang, High-performance, self-driven photodetector based on graphene sandwiched GaSe/WS2 heterojunction. 6(2), 1700490 (2018). http://dx.doi.org/doi:10.1002/adom.201700490
[98] M. Massicotte, P. Schmidt, F. Vialla, K.G. Schadler, A. Reserbat-Plantey et al., Picosecond photoresponse in van der Waals heterostructures. Nat. Nanotechnol. 11(1), 42-46 (2016).
[99] X. Wang, L. Huang, Y. Peng, N. Huo, K. Wu et al., Enhanced rectification, transport property and photocurrent generation of multilayer ReSe2/MoS2 p–n heterojunctions. 9(2), 507-516 (2016). http://dx.doi.org/10.1007/s12274-015-0932-6
[100] X. Wei, F.G. Yan, Q.S. Lv, C. Shen, K.Y. Wang, Fast gate-tunable photodetection in the graphene sandwiched WSe2/GaSe heterojunctions. Nanoscale 9(24), 8388-8392 (2017). https://doi.org/10.1039/C7NR03124F
[101] F.G. Yan, L.X. Zhao, A.L. Patane, P.A. Hu, X. Wei et al., Fast, multicolor photodetection with graphene-contacted p-GaSe/n-InSe van der Waals heterostructures. Nanotechnology 28, 27 (2017). https://doi.org/10.1088/1361-6528/aa749e
[102] K. Zhang, X. Fang, Y.L. Wang, Y. Wan, Q.J. Song et al., Ultrasensitive near-infrared photodetectors based on a graphene-MoTe2-graphene vertical van der Waals heterostructure. ACS Appl. Mater.Interfaces 9(6), 5392-5398 (2017). https://doi.org/10.1021/acsami.6b14483
[103] X. Wei, F.G. Yan, C. Shen, Q.S. Lv, K. Y. Wang, Photodetectors based on junctions of two-dimensional transition metal dichalcogenides. Chinese Phys. B. 26(3), 038504 (2017). https://doi.org/10.1088/1674-1056/26/3/038504
[104] C.H. Lee, G.H. Lee, A.M. van der Zande, W.C. Chen, Y.L. Li et al., Atomically thin p-n junctions with van der Waals heterointerfaces. Nat. Nanotechnol. 9(9), 676-681 (2014). https://doi.org/10.1038/nnano.2014.150
[105] W.H. Wu, Q. Zhang, X. Zhou, L. Li, J.W. Su, F.K. Wang, T.Y. Zhai, Self-powered photovoltaic photodetector established on lateral monolayer MoS2-WS2 heterostructures. Nano Energy 51, 45-53 (2018). http://dx.doi.org/10.1016/j.nanoen.2018.06.049
[106] C. Choi, M.K. Choi, S.Y. Liu, M.S. Kim, O.K. Park et al., Human eye-inspired soft optoelectronic device using high-density MoS2-graphene curved image sensor array. Nat. Commun. 8, 1664 (2017). https://doi.org/10.1038/s41467-017-01824-6
[107] F. Wang, Z.X. Wang, K. Xu, F.M. Wang, Q.S. Wang, Y. Huang, L. Yin, J. He, Tunable GaTe-MoS2 van der Waals p-n junctions with novel optoelectronic performance. Nano Lett. 15(11), 7558-7566 (2015). http://dx.doi.org/10.1021/acs.nanolett.5b03291
[108] M.S. Long, E.F. Liu, P. Wang, A.Y. Gao, H. Xia et al., Broadband photovoltaic detectors based on an atomically thin heterostructure. Nano Lett. 16(4), 2254-2259 (2016). http://dx.doi.org/10.1021/acs.nanolett.5b04538
[109] K. Roy, M. Padmanabhan, S. Goswami, T.P. Sai, G. Ramalingam, S. Raghavan, A. Ghosh, Graphene-MoS2 hybrid structures for multifunctional photoresponsive memory devices. Nature Nanotechnology. 8(11), 826-830 (2013). http://dx.doi.org/10.1038/Nnano.2013.206
[110] S.J. Zheng, E.X. Wu, Z.H. Feng, R. Zhang, Y. Xie et al., Acoustically enhanced photodetection by a black phosphorus-MoS2 van der Waals heterojunction p-n diode. Nanoscale 10(21), 10148-10153 (2018). http://dx.doi.org/10.1039/c8nr02022a
[111] Q.M. Wang, Z.Y. Yang, Graphene photodetector with polydiacetylenes acting as both transfer-supporting and light-absorbing layers: Flexible, broadband, ultrahigh photoresponsivity and detectivity. Carbon 138, 90-97 (2018). http://dx.doi.org/10.1016/j.carbon.2018.05.054
[112] Y.J. Liu, C. Liu, X.M. Wang, L. He, X.G. Wan et al., Photoresponsivity of an all-semimetal heterostructure based on graphene and WTe2. Sci. Rep. 8, 12840 (2018). https://doi.org/10.1038/s41598-018-29717-8
[113] D. Xiang, T. Liu, J.L. Xu, J.Y. Tan, Z.H. Hu et al., Two-dimensional multibit optoelectronic memory with broadband spectrum distinction. Nat. Commun. 9, 2966 (2018). https://doi.org/10.1038/s41467-018-05397-w
[114] D. Unuchek, A. Ciarrocchi, A. Avsar, K. Watanabe, T. Taniguchi, A. Kis, Room-temperature electrical control of exciton flux in a van der Waals heterostructure. Nature 560(7718), 340-344 (2018). http://dx.doi.org/10.1038/s41586-018-0357-y
[115] B. Dlubak, M.-B. Martin, R.S. Weatherup, H. Yang, C. Deranlot et al., Graphene-passivated nickel as an oxidation-resistant electrode for spintronics. ACS Nano 6(12), 10930-10934 (2012). http://dx.doi.org/10.1021/nn304424x
[116] M.Z. Iqbal, M.W. Iqbal, S. Siddique, M.F. Khan, S.M. Ramay, Room temperature spin valve effect in NiFe/WS2/Co junctions. Sci. Rep. 6, 21038 (2016). http://dx.doi.org/10.1038/srep21038
[117] Z. Wang, D. Sapkota, T. Taniguchi, K. Watanabe, D. Mandrus, A.F. Morpurgo, Tunneling spin valves based on Fe3GeTe2/hBN/Fe3GeTe2 van der Waals heterostructures. Nano Lett. 18(7), 4303-4308 (2018). http://dx.doi.org/10.1021/acs.nanolett.8b01278
[118] H. Zhang, M. Ye, Y. Wang, R. Quhe, Y. Pan et al., Magnetoresistance in Co/2D MoS2/Co and Ni/2D MoS2/Ni junctions. Phys. Chem. Chem. Phys. 18(24), 16367-16376 (2016). http://dx.doi.org/10.1039/C6CP01866A
[119] V.M. Karpan, G. Giovannetti, P.A. Khomyakov, M. Talanana, A.A. Starikov et al., Graphite and graphene as perfect spin filters. Phys. Rev. Lett. 99(17), 176602 (2007). http://dx.doi.org/10.1103/PhysRevLett.99.176602
[120] M.Z. Iqbal, S. Siddique, G. Hussain, M.W. Iqbal, Room temperature spin valve effect in the NiFe/Gr–hBN/Co magnetic tunnel junction. J. Mater. Chem. C 4(37), 8711-8715 (2016). http://dx.doi.org/10.1039/C6TC03425J
[121] D. Xiao, G.B. Liu, W.X. Feng, X.D. Xu, W. Yao, Coupled spin and valley physics in monolayers of MoS2 and other group-VI dichalcogenides. Phys. Rev. Lett. 108(19), 196802 (2012). https://doi.org/10.1103/PhysRevLett.108.196802
[122] J. Lee, K.F. Mak, J. Shan, Electrical control of the valley Hall effect in bilayer MoS2 transistors. Nat. Nanotechnol. 11(5), 421-425 (2016). http://dx.doi.org/10.1038/nnano.2015.337
[123] K.F. Mak, K.L. McGill, J. Park, P.L. McEuen, The valley Hall effect in MoS2 transistors. Science 344(6191), 1489-1492 (2014). http://dx.doi.org/10.1126/science.1250140
[124] A.V. Stier, K.M. McCreary, B.T. Jonker, J. Kono, S.A. Crooker, Exciton diamagnetic shifts and valley Zeeman effects in monolayer WS2 and MoS2 to 65 Tesla. Nat. Commun. 7, 10643 (2016). https://doi.org/10.1038/ncomms10643
[125] L. Cai, J.F. He, Q.H. Liu, T. Yao, L. Chen et al., Vacancy-induced ferromagnetism of MoS2 Nanosheets. J. Am. Chem. Soc. 137(7), 2622-2627 (2015). https://doi.org/10.1021/ja5120908
[126] C. Zhao, T. Norden, P.Y. Zhang, P.Q. Zhao, Y.C. Cheng et al., Enhanced valley splitting in monolayer WSe2 due to magnetic exchange field. Nat. Nanotechnol. 12(8), 757-762 (2017). http://dx.doi.org/10.1038/Nnano.2017.68
[127] Y.K. Luo, J.S. Xu, T.C. Zhu, G.Z. Wu, E.J. McCormick et al., Opto-valleytronic spin injection in monolayer MoS2/few-layer graphene hybrid spin valves. Nano Lett. 17(6), 3877-3883 (2017). http://dx.doi.org/10.1021/acs.nanolett.7b01393
[128] Y.P. Liu, H. Idzuchi, Y. Fukuma, O. Rousseau, Y. Otani, W.S. Lew, Spin injection properties in trilayer graphene lateral spin valves. Appl. Phys. Lett. 102(3), 033105 (2013). https://doi.org/10.1063/1.4776699
[129] M.V. Kamalakar, C. Groenveld, A. Dankert, S.P. Dash, Long distance spin communication in chemical vapour deposited graphene. Nat. Commun. 6, 6766 (2015). https://doi.org/10.1038/ncomms7766
[130] F.G. Yan, Z.M. Wei, X. Wei, Q.S. Lv, W.K. Zhu, K.Y. Wang, Toward high-performance photodetectors based on 2D materials: Strategy on methods. Small Methods 2(5), 1700394 (2018). https://doi.org/10.1002/smtd.201700349

References

[1] K.S. Novoselov, A.K. Geim, S.V. Morozov, D. Jiang, Y. Zhang, S.V. Dubonos, I.V. Grigorieva, A.A. Firsov, Electric field effect in atomically thin carbon films. Science 306(5696), 666-669 (2004). http://dx.doi.org/10.1126/science.1102896
[2] M. Osada, T. Sasaki, Two-dimensional dielectric nanosheets: novel nanoelectronics from nanocrystal building blocks. Adv. Mater. 24 (2), 210-228 (2012). http://dx.doi.org/10.1002/adma.201103241
[3] L.M. Malard, J. Nilsson, D.C. Elias, J.C. Brant, F. Plentz et al., Probing the electronic structure of bilayer graphene by Raman scattering. Phys. Rev. B 76(20), 201401 (2007). https://doi.org/10.1103/PhysRevB.76.201401
[4] V. Tran, R. Soklaski, Y.F. Liang, L. Yang, Layer-controlled band gap and anisotropic excitons in few-layer black phosphorus. Phys. Rev. B 89(23), 235319 (2014). https://doi.org/10.1103/PhysRevB.89.235319
[5] K.F. Mak, C. Lee, J. Hone, J. Shan, T.F. Heinz, Atomically Thin MoS2: A new direct-gap semiconductor. Phys. Rev. Lett. 105(13), 136805 (2010). https://doi.org/10.1103/PhysRevLett.105.136805
[6] L. Xie, M.Z. Liao, S.P. Wang, H. Yu, L.J. Du et al., Graphene-contacted ultrashort channel monolayer MoS2 transistors. Adv. Mater. 29(37), 1702522 (2017). https://doi.org/10.1002/adma.201702522
[7] Y.P. Liu, W.S. Lew, S. Goolaup, Z.X. Shen, L. Sun, T.J. Zhou, S.K. Wong, Observation of the semiconductor-metal transition behavior in monolayer graphene. Carbon 50(6), 2273-2279 (2012). https://doi.org/10.1016/j.carbon.2012.01.046
[8] A. Allain, J.H. Kang, K. Banerjee, A. Kis, Electrical contacts to two-dimensional semiconductors. Nat. Mater. 14(12), 1195-1205 (2015). https://doi.org/10.1038/nmat4452
[9] P.R.Y. Gangavarapu, P.C. Lokesh, K.N. Bhat, A.K. Naik, Towards barrier free contacts to n-type cntfets using graphene electrodes. 2016 Ieee Nanotechnology Materials and Devices Conference (Nmdc, 2016). https://doi.org/10.1109/NMDC.2016.7777064
[10] J. Du, C.X. Xia, W.Q. Xiong, X. Zhao, T.X. Wang, Y. Jia, Tuning the electronic structures and magnetism of two-dimensional porous C2N via transition metal embedding. Phys. Chem. Chem. Phys. 18(32), 22678-22686 (2016). https://doi.org/10.1039/C6CP03210A
[11] Y.P. Liu, S. Goolaup, W.S. Lew, I. Purnama, M.C. Sekhar, T.J. Zhou, S.K. Wong, Excitonic bandgap dependence on stacking configuration in four layer graphene. Appl. Phys. Lett. 103(16), 163108 (2013). https://doi.org/10.1063/1.4825263
[12] C.R. Dean, A.F. Young, I. Meric, C. Lee, L. Wang et al., Boron nitride substrates for high-quality graphene electronics. Nat. Nanotechnol. 5(10), 722-726 (2010). http://dx.doi.org/10.1038/nnano.2010.172
[13] W.J. Jie, Z.B. Yang, G.X. Bai, J.H. Hao, Luminescence in 2D materials and van der waals heterostructures. Adv. Opt. Mater. 6(10), 1701296 (2018). https://doi.org/10.1002/adom.201701296
[14] K.S. Novoselov, A. Mishchenko, A. Carvalho, A.H.C. Neto, 2D materials and van der Waals heterostructures. Science 353(6298), 9439 (2016). https://doi.org/10.1126/science.aac9439
[15] O.L. Sanchez, D. Ovchinnikov, S. Misra, A. Allain, A. Kis, Valley polarization by spin injection in a light-emitting van der waals heterojunction. Nano Lett. 16(9), 5792-5797 (2016). http://dx.doi.org/10.1021/acs.nanolett.6b02527.
[16] C.L. Tan, H. Zhang, Epitaxial growth of hetero-nanostructures based on ultrathin two-dimensional nanosheets. J. Am. Chem. Soc. 137(38), 12162-12174 (2015). http://dx.doi.org/10.1021/jacs.5b03590.
[17] H.Y. Yu, Y. Wang, Q.J. Tong, X.D. Xu, W. Yao, Anomalous light cones and valley optical selection rules of interlayer excitons in twisted heterobilayers. Phys. Rev. Lett. 115(18), 187002 (2015). https://doi.org/10.1103/PhysRevLett.115.187002
[18] F. Haque, T. Daeneke, K. Kalantar-zadeh, J. Ou, Two-dimensional transition metal oxide and chalcogenide-based photocatalysts. Nano-Micro Lett. 10, 23 (2018). https://doi.org/10.1007/s40820-017-0176-y
[19] X. Zhou, X.Z. Hu, J. Yu, S.Y. Liu, Z.W. Shu et al., 2D layered material-based van der waals heterostructures for optoelectronics. Adv. Funct. Mater. 28(14), 1706587 (2018). https://doi.org/10.1002/adfm.201706587
[20] J.A. Leon, N.C. Mamani, A. Rahim, L.E. Gomez, M.A.P.d. Silva, G. M. Gusev, Transferring few-layer graphene sheets on hexagonal boron nitride substrates for fabrication of graphene devices. Graphene 25-35, 48096 (2014). http://dx.doi.org/10.4236/graphene.2014.33005
[21] A. Castellanos-Gomez, M. Buscema, R. Molenaar, V. Singh, L. Janssen, H.S.J. van der Zant, G. A. Steele, Deterministic transfer of two-dimensional materials by all-dry viscoelastic stamping. 2D Mater. 1(1), 011002 (2014).
[22] P. Pedrinazzi, J.M. Caridad, D.M.A. Mackenzie, F. Pizzocchero, L. Gammelgaard et al., High-quality graphene flakes exfoliated on a flat hydrophobic polymer. Appl. Phys. Lett. 112(3), 033101 (2018). https://doi.org/10.1063/1.5009168
[23] P.J. Zomer, S.P. Dash, N. Tombros, B. J. van Wees, A transfer technique for high mobility graphene devices on commercially available hexagonal boron nitride. Appl. Phys. Lett. 99(23), 232104 (2011). https://doi.org/10.1063/1.3665405
[24] J.I.J. Wang, Y.F. Yang, Y.A. Chen, K. Watanabe, T. Taniguchi, H.O. H. Churchill, P. Jarillo-Herrero, Electronic transport of encapsulated graphene and wse2 devices fabricated by pick-up of prepatterned hBN. Nano Lett. 15(3), 1898-1903 (2015). http://dx.doi.org/10.1021/nl504750f.
[25] R. Frisenda, E. Navarro-Moratalla, P. Gant, D.P. De Lara, P. Jarillo-Herrero, R.V. Gorbachev, A. Castellanos-Gomez, Recent progress in the assembly of nanodevices and van der Waals heterostructures by deterministic placement of 2D materials. Chem. Soc. Rev. 47(1), 53-68 (2018). http://dx.doi.org/10.1039/c7cs00556c
[26] M.A. Meitl, Z.T. Zhu, V. Kumar, K.J. Lee, X. Feng et al., Transfer printing by kinetic control of adhesion to an elastomeric stamp. Nat. Mater. 5(1), 33-38 (2006). http://dx.doi.org/10.1038/nmat1532
[27] Y.J. Gong, J.H. Lin, X.L. Wang, G. Shi, S.D. Lei et al., Vertical and in-plane heterostructures from WS2/MoS2 monolayers. Nat. Mater. 13(12), 1135-1142 (2014). http://dx.doi.org/10.1038/Nmat4091
[28] X.F. Li, M.W. Lin, J.H. Lin, B. Huang, A.A. Puretzky et al., Two-dimensional GaSe/MoSe2 misfit bilayer heterojunctions by van der Waals epitaxy. Sci. Adv. 2(4), 1501882 (2016). https://doi.org/10.1126/sciadv.1501882
[29] L. Fu, Y.Y. Sun, N. Wu, R.G. Mendes, L.F. Chen et al., Direct growth of MoS2/h-BN heterostructures via a sulfide-resistant alloy. Acs Nano 10(2), 2063-2070 (2016). http://dx.doi.org/10.1021/acsnano.5b06254
[30] B.Y. Zheng, C. Ma, D. Li, J.Y. Lan, Z. Zhang et al., Band alignment engineering in two-dimensional lateral heterostructures. J. Am. Chem. Soc. 140(36), 11193-11197 (2018). http://dx.doi.org/10.1021/jacs.8b07401
[31] P.K. Sahoo, S. Memaran, Y. Xin, L. Balicas, H.R. Gutierrez, One-pot growth of two-dimensional lateral heterostructures via sequential edge-epitaxy. Nature 553(7686), 63-67 (2018). http://dx.doi.org/10.1038/nature25155
[32] Z.W. Zhang, P. Chen, X.D. Duan, K.T. Zang, J. Luo, X.F. Duan, Robust epitaxial growth of two-dimensional heterostructures, multiheterostructures, and superlattices. Science 357(6353), 788-792 (2017). https://doi.org/10.1126/science.aan6814
[33] B. Zheng, C. Ma, D. Li, J. Lan, Z. Zhang et al., Band alignment engineering in two-dimensional lateral heterostructures. J. Am. Chem. Soc. 140(36), 11193-11197 (2018). http://dx.doi.org/10.1021/jacs.8b07401
[34] C. Gong, H.J. Zhang, W. Wang, L. Colombo, R.M. Wallace, K. Cho, Band alignment of two-dimensional transition metal dichalcogenides: Application in tunnel field effect transistors. Appl. Phys. Lett. 107(13), 053513 (2015). https://doi.org/10.1063/1.4932088
[35] F. Withers, O. Del Pozo-Zamudio, A. Mishchenko, A.P. Rooney, A. Gholinia et al., Light-emitting diodes by band-structure engineering in van der Waals heterostructures. Nature Mater. 14(3), 301-306 (2015). https://doi.org/10.1038/nmat4205
[36] W.G. Xu, W.W. Liu, J.F. Schmidt, W.J. Zhao, X. Lu et al., Correlated fluorescence blinking in two-dimensional semiconductor heterostructures. Nature 541(7635), 62-67 (2017). http://dx.doi.org/10.1038/nature20601
[37] Y. Hattori, T. Taniguchi, K. Watanabe, K. Nagashio, Determination of carrier polarity in fowler-nordheim tunneling and evidence of fermi level pinning at the hexagonal boron nitride/metal interface. ACS Appl. Mater. Interfaces 10(14), 11732-11738 (2018). https://doi.org/10.1021/acsami.7b18454
[38] P. Bampoulis, R. van Bremen, Q.R. Yao, B. Poelsema, H.J. W. Zandvliet, K. Sotthewes, Defect dominated charge transport and fermi level pinning in MoS2/metal contacts. ACS Appl. Mater. Interfaces 9(22), 19278-19286 (2017). http://dx.doi.org/10.1021/acsami.7b02739
[39] T. Le Quang, V. Cherkez, K. Nogajewski, M. Potemski, M.T. Dau, M. Jamet, P. Mallet, J. Y. Veuillen, Scanning tunneling spectroscopy of van der Waals graphene/semiconductor interfaces: absence of Fermi level pinning. 2D Mater. 4(3), 035019 (2017). http://iopscience.iop.org/article/10.1088/2053-1583/aa7b03
[40] C.R. Woods, L. Britnell, A. Eckmann, R.S. Ma, J.C. Lu, Commensurate-incommensurate transition in graphene on hexagonal boron nitride. Nature Phys. 10(6), 451-456 (2014). http://dx.doi.org/10.1038/Nphys2954
[41] B. Li, L. Huang, M.Z. Zhong, Y. Li, Y. Wang, J.B. Li, Z.M. Wei, Direct vapor phase growth and optoelectronic application of large band offset SnS2/MoS2 vertical bilayer heterostructures with high lattice mismatch. Adv. Electron. Mater. 2(11), 1600298 (2016). https://doi.org/10.1002/aelm.201600298
[42] K.H. Liu, L.M. Zhang, T. Cao, C.H. Jin, D.A. Qiu et al., Evolution of interlayer coupling in twisted molybdenum disulfide bilayers. Nat. Commun. 5, 4966 (2014). https://doi.org/10.1038/ncomms5966
[43] H.J. Tan, W.S. Xu, Y.W. Sheng, C.S. Lau, Y. Fan et al., Lateral graphene-contacted vertically stacked WS2/MoS2 hybrid photodetectors with large gain. Adv. Mater. 29(46), 1702917 (2017). https://doi.org/10.1002/adma.201702917
[44] F. Gong, W.J. Luo, J.L. Wang, P. Wang, H.H. Fang et al., High-sensitivity floating-gate phototransistors based on WS2 and MoS2. Adv. Funct. Mater. 26(33), 6084-6090 (2016). http://dx.doi.org/10.1002/adfm.201601346
[45] A. Dankert, S.P. Dash, Electrical gate control of spin current in van der Waals heterostructures at room temperature. Nat. Commun. 8, 16093 (2017). https://doi.org/10.1038/ncomms16093
[46] J.L. Wang, H.H. Fang, X.D. Wang, X.S. Chen, W. Lu, W.D. Hu, Recent progress on localized field enhanced two-dimensional material photodetectors from ultraviolet-visible to infrared. Small 13(35), 1700894 (2017). https://doi.org/10.1002/smll.201700894
[47] M.Z. Bellus, F. Ceballos, H.Y. Chiu, H. Zhao, Tightly bound trions in transition metal dichalcogenide heterostructures. ACS Nano 9(6), 6459-6464 (2015). http://dx.doi.org/10.1021/acsnano.5b02144
[48] L.B. Drissi, F.Z. Ramadan, N.B.J. Kanga, Optoelectronic properties in 2D GeC and SiC hybrids: DFT and many body effect calculations. Mater. Res. Express 5(1), 015061 (2018). http://iopscience.iop.org/article/10.1088/2053-1591/aaa862
[49] X.P. Hong, J. Kim, S.F. Shi, Y. Zhang, C.H. Jin et al., Ultrafast charge transfer in atomically thin MoS2/WS2 heterostructures. Nat. Nanotechnol. 9(9), 682-686 (2014). http://dx.doi.org/10.1038/Nnano.2014.167
[50] H.H. Hung, J.S. Wu, K. Sun, C.K. Chiu, Engineering of many-body Majorana states in a topological insulator/s-wave superconductor heterostructure. Sci. Rep. 7, 3499 (2017). https://doi.org/10.1038/s41598-017-02493-7
[51] P. Rivera, J.R. Schaibley, A.M. Jones, J.S. Ross, S F. Wu et al., Observation of long-lived interlayer excitons in monolayer MoSe2-WSe2 heterostructures. Nat. Commun. 6, 6242 (2015). https://doi.org/10.1038/ncomms7242
[52] M. Li, D. Esseni, G. Snider, D. Jena, H.G. Xing, Single particle transport in two-dimensional heterojunction interlayer tunneling field effect transistor. J. Appl. Phys. 115(7), 074508 (2014). https://doi.org/10.1063/1.4866076
[53] X. Yan, C.S. Liu, C. Li, W.Z. Bao, S.J. Ding, D.W. Zhang, P. Zhou, Tunable SnSe2/WSe2 Heterostructure Tunneling Field Effect Transistor. Small 13(34), 1701478 (2017). https://doi.org/10.1002/smll.201701478
[54] T. Yamaoka, H.E. Lim, S. Koirala, X.F. Wang, K. Shinokita et al., Efficient photocarrier transfer and effective photoluminescence enhancement in type i monolayer MoTe2/WSe2 heterostructure. Adv. Funct. Mater. 28(35), 1801021 (2018). https://doi.org/10.1002/adfm.201801021
[55] Z. Cai, M. Cao, Z.P. Jin, K.Y. Yi, X.S. Chen, D.C. Wei, Large photoelectric-gating effect of two-dimensional van-der-Waals organic/tungsten diselenide heterointerface. Npj 2D Mater. Appl. 2, 21 (2018). http://iopscience.iop.org/article/10.1088/2053-1591/aaa862
[56] S. Bertolazzi, D. Krasnozhon, A. Kis, Nonvolatile memory cells based on MoS2/graphene heterostructures. ACS Nano 7(4), 3246-3252 (2013). http://dx.doi.org/10.1021/nn3059136
[57] M.S. Choi, G.H. Lee, Y.J. Yu, D.Y. Lee, S.H. Lee, P. Kim, J. Hone, W.J. Yoo, Controlled charge trapping by molybdenum disulphide and graphene in ultrathin heterostructured memory devices. Nat. Commun. 4, 1624 (2013). https://www.nature.com/articles/ncomms2652
[58] Y. Zhang, Y.B. Yuan, J.S. Huang, Detecting 100 fW cm-2 light with trapped electron gated organic phototransistors. Adv. Mater. 29(5), 1603969 (2017). https://doi.org/10.1002/adma.201603969
[59] J.L. Wang, X.M. Zou, X.H. Xiao, L. Xu, C.L. Wang et al., Floating gate memory-based monolayer MoS2 transistor with metal nanocrystals embedded in the gate dielectrics. Small 11(2), 208-213 (2015). http://dx.doi.org/10.1002/smll.201401872
[60] Y.P. Liu, W.S. Lew, Z.W. Liu, Observation of anomalous resistance behavior in bilayer graphene. Nanoscale Res. Lett. 12, 48 (2017). https://doi.org/10.1186/s11671-016-1792-z
[61] Y.P. Liu, Z.W. Liu, W.S. Lew, Q.J. Wang, Temperature dependence of the electrical transport properties in few-layer graphene interconnects. Nanoscale Res. Lett. 8, 335 (2013). https://doi.org/10.1186/1556-276X-8-335
[62] Q.A. Vu, Y.S. Shin, Y.R. Kim, V.L. Nguyen, W.T. Kang et al., Two-terminal floating-gate memory with van der Waals heterostructures for ultrahigh on/off ratio. Nat. Commun. 7, 12725 (2016). https://doi.org/10.1038/ncomms12725
[63] H.L. Chen, X.W. Wen, J. Zhang, T.M. Wu, Y.J. Gong et al., Ultrafast formation of interlayer hot excitons in atomically thin MoS2/WS2 heterostructures. Nat. Commun. 7, 12512 (2016). https://doi.org/10.1038/ncomms12512
[64] X.W. Wen, H.L. Chen, T.M. Wu, Z.H. Yu et al., Ultrafast probes of electron-hole transitions between two atomic layers. Nat. Commun. 9, 1859 (2018). https://doi.org/10.1038/s41467-018-04291-9
[65] A.T. Hanbicki, H.J. Chuang, M.R. Rosenberger, C.S. Hellberg, S.V. Sivaram, K.M. McCreary, I.I. Mazin, B. T. Jonker, Double indirect interlayer exciton in a MoSe2/WSe2 van der waals heterostructure. ACS Nano 12(5), 4719-4726 (2018). http://dx.doi.org/10.1021/acsnano.8b01369
[66] S. Latini, K.T. Winther, T. Olsen, K.S. Thygesen, Interlayer excitons and band alignment in MoS2/hBN/WSe2 van der waals heterostructures. Nano Lett. 17(2), 938-945 (2017). http://dx.doi.org/10.1021/acs.nanolett.6b04275
[67] J.S. Ross, P. Rivera, J. Schaibley, E. Lee-Wong, H.Y. Yu et al., Interlayer exciton optoelectronics in a 2D heterostructure p-n junction. Nano Lett. 17(2), 638-643 (2017). http://dx.doi.org/10.1021/acs.nanolett.6b03398
[68] P. Rivera, K.L. Seyler, H.Y. Yu, J.R. Schaibley, J.Q. Yan et al., Valley-polarized exciton dynamics in a 2D semiconductor heterostructure. Science 351(6274), 688-691 (2016). http://dx.doi.org/10.1126/science.aac7820
[69] T. Deilmann, K.S. Thygesen, Interlayer trions in the MoS2/WS2 van der Waals heterostructure. Nano Lett. 18(2), 1460-1465 (2018). http://dx.doi.org/10.1021/acs.nanolett.7b05224
[70] Y.P. Liu, W.S. Lew, L. Sun, Enhanced weak localization effect in few-layer graphene. Phys. Chem. Chem. Phys. 13(45), 20208-20214 (2011). https://doi.org/10.1039/c1cp22250c
[71] L. Y. Ping, G. Sarjoosing, M. Chandrasekhar, L. W. Siang, W. S. J. A. N. Kai, Effect of magnetic field on the electronic transport in trilayer graphene. ACS Nano 4(12), 7087-7092 (2010). https://doi.org/DOI: 10.1021/nn101296x
[72] J.S. Qi, X. Li, Q. Niu, J. Feng, Giant and tunable valley degeneracy splitting in MoTe2. Phys. Rev. B 92(12), 121403 (2015). https://doi.org/10.1103/PhysRevB.92.121403
[73] B.Z. Zhou, S.W. Ji, Z. Tian, W.J. Cheng, X.C. Wang, W.B. Mi, Proximity effect induced spin filtering and gap opening in graphene by half-metallic monolayer Cr2C ferromagnet. Carbon 132, 25-31 (2018). http://dx.doi.org/10.1016/j.carbon.2018.02.044
[74] P. Wei, S. Lee, F. Lemaitre, L. Pinel, D. Cutaia et al., Strong interfacial exchange field in the graphene/EuS heterostructure. Nat. Mater. 15(7), 711-716 (2016). http://dx.doi.org/10.1038/Nmat4603
[75] H.X. Yang, A. Hallal, D. Terrade, X. Waintal, S. Roche, M. Chshiev, Proximity effects induced in graphene by magnetic insulators: first-principles calculations on spin filtering and exchange-splitting gaps. Phys. Rev. Lett. 110(4), 046603 (2013). https://doi.org/10.1103/PhysRevLett.110.046603
[76] K.L. Seyler, D. Zhong, B. Huang, X.Y. Linpeng, N.P. Wilson et al., Valley manipulation by optically tuning the magnetic proximity effect in WSe2/CrI3 heterostructures. Nano Lett. 18(6), 3823-3828 (2018). http://dx.doi.org/10.1021/acs.nanolett.8b01105
[77] B. Huang, G. Clark, E. Navarro-Moratalla, D.R. Klein, R. Cheng, Layer-dependent ferromagnetism in a van der Waals crystal down to the monolayer limit. Nature 546(7657), 270-273 (2017). http://dx.doi.org/10.1038/nature22391
[78] J.U. Lee, S. Lee, J.H. Ryoo, S. Kang, T.Y. Kim et al., Ising-type magnetic ordering in atomically thin FePS3. Nano Lett. 16(12), 7433-7438 (2016). http://dx.doi.org/10.1021/acs.nanolett.6b03052
[79] J. Du, C.X. Xia, W.Q. Xiong, T.X. Wang, Y. Jia, J.B. Li, Two-dimensional transition-metal dichalcogenides-based ferromagnetic van der Waals heterostructures. Nanoscale 9 (44), 17585-17592 (2017). http://dx.doi.org/10.1039/c7nr06473j
[80] Y.P. Liu, I. Yudhistira, M. Yang, E. Laksono, Y.Z. Luo et al., Phonon-mediated colossal magnetoresistance in graphene/black phosphorus heterostructures. Nano Lett. 18(6), 3377-3383 (2018). http://dx.doi.org/10.1021/acs.nanolett.8b00155
[81] M. Bonilla, S. Kolekar, Y.J. Ma, H.C. Diaz, V. Kalappattil et al., Strong room-temperature ferromagnetism in VSe2 monolayers on van der Waals substrates. Nat. Nanotechnol. 13(4), 289-293 (2018). http://dx.doi.org/10.1038/s41565-018-0063-9
[82] Z.Y. Fei, B. Huang, P. Malinowski, W.B. Wang, T.C. Song et al., Two-dimensional itinerant ferromagnetism in atomically thin Fe3GeTe2. Nat Mater. 17(9), 778-782 (2018). http://dx.doi.org/10.1038/s41563-018-0149-7
[83] Y. Deng, Y. Yu, Y. Song, J. Zhang, N.Z. Wang et al., Gate-tunable room-temperature ferromagnetism in two-dimensional Fe3GeTe2. Nature 563, 94-99 (2018). http://dx.doi.org/10.1038/s41586-018-0626-9
[84] C. Si, J. Zhou, Z.M. Sun, Half-metallic ferromagnetism and surface functionalization-induced metal-insulator transition in graphene-like two-dimensional Cr2C crystals. ACS Appl. Mater. Interfaces 7(31), 17510-17515 (2015). http://dx.doi.org/10.1021/acsami.5b05401
[85] M. Kan, J. Zhou, Q. Sun, Y. Kawazoe, P. Jena, The intrinsic ferromagnetism in a MnO2 monolayer. J. Phys. Chem. Lett. 4(20), 3382-3386 (2013). http://dx.doi.org/10.1021/jz4017848
[86] Y. Zhang, J.M. Pang, M.G. Zhang, X. Gu, L. Huang, Two-dimensional Co2S2 monolayer with robust ferromagnetism. Sci. Rep. 7, 7 (2017). https://doi.org/10.1038/s41598-017-00035-9
[87] M. Ormaza, L. Fernandez, M. Ilyn, A. Magana, B. Xu et al., High temperature ferromagnetism in a GdAg2 monolayer. Nano Lett. 16(7), 4230-4235 (2016). http://dx.doi.org/10.1021/acs.nanolett.6b01197
[88] M. Kan, S. Adhikari, Q. Sun, Ferromagnetism in MnX2 ( X = S, Se) monolayers. Phys. Chem. Chem. Phys. 16(10), 4990-4994 (2014). http://dx.doi.org/10.1039/c3cp55146f
[89] Y.P. Liu, W.S. Lew, S. Goolaup, H.F. Liew, S.K. Wong, T.J. Zhou, Observation of oscillatory resistance behavior in coupled bernal and rhombohedral stacking graphene. ACS Nano 5(7), 5490-5498 (2011). https://doi.org/10.1021/nn200771e
[90] S. Roche, J. Aring;kerman, B. Beschoten, J.C. Charlier, M. Chshiev et al., Graphene spintronics: the European Flagship perspective. 2D Mater. 2(3), 030202 (2015). http://iopscience.iop.org/article/10.1088/2053-1583/2/3/030202
[91] M.W. Si, P.Y. Liao, G. Qiu, Y.Q. Duan, P.D.D. Ye, Ferroelectric field-effect transistors based on MoS2 and CuInP2S6 two-dimensional van der Waals heterostructure. ACS Nano 12(7), 6700-6705 (2018). http://dx.doi.org/10.1021/acsnano.8b01810
[92] Y.P. Liu, K. Tom, X.W. Zhang, S. Lou, Y. Liu, J. Yao, Alloying effect on bright-dark exciton states in ternary monolayer MoxW1-xSe2. New J. Phys. 19, 073018 (2017). http://iopscience.iop.org/article/10.1088/1367-2630/aa6d39
[93] Y.P. Liu, Q.L. Xia, J. He, Z.W. Liu, Direct observation of high photoresponsivity in pure graphene photodetectors. Nanoscale Res. Lett. 12, 93 (2017). https://doi.org/10.1186/s11671-017-1827-0
[94] Y.P. Liu, K. Tom, X. Wang, C.M. Huang, H.T. Yuan et al., Dynamic control of optical response in layered metal chalcogenide nanoplates. Nano Lett. 16(1), 488-496 (2016). https://doi.org/10.1021/acs.nanolett.5b04140
[95] X.C. Yu, Z.G. Dong, Y.P. Liu, T. Liu, J. Tao et al., A high performance, visible to mid-infrared photodetector based on graphene nanoribbons passivated with HfO2. Nanoscale 8(1), 327-332 (2016). https://doi.org/10.1039/C5NR06869J
[96] W.G. Luo, Y.F. Cao, P.G. Hu, K.M. Cai, Q. Feng et al., Gate tuning of high-performance inse-based photodetectors using graphene electrodes. Adv. Opt. Mater. 3(10), 1418-1423 (2015). https://doi.org/10.1002/adom.201500190
[97] Q. Lv, F. Yan, X. Wei, K. Wang, High-performance, self-driven photodetector based on graphene sandwiched GaSe/WS2 heterojunction. 6(2), 1700490 (2018). http://dx.doi.org/doi:10.1002/adom.201700490
[98] M. Massicotte, P. Schmidt, F. Vialla, K.G. Schadler, A. Reserbat-Plantey et al., Picosecond photoresponse in van der Waals heterostructures. Nat. Nanotechnol. 11(1), 42-46 (2016).
[99] X. Wang, L. Huang, Y. Peng, N. Huo, K. Wu et al., Enhanced rectification, transport property and photocurrent generation of multilayer ReSe2/MoS2 p–n heterojunctions. 9(2), 507-516 (2016). http://dx.doi.org/10.1007/s12274-015-0932-6
[100] X. Wei, F.G. Yan, Q.S. Lv, C. Shen, K.Y. Wang, Fast gate-tunable photodetection in the graphene sandwiched WSe2/GaSe heterojunctions. Nanoscale 9(24), 8388-8392 (2017). https://doi.org/10.1039/C7NR03124F
[101] F.G. Yan, L.X. Zhao, A.L. Patane, P.A. Hu, X. Wei et al., Fast, multicolor photodetection with graphene-contacted p-GaSe/n-InSe van der Waals heterostructures. Nanotechnology 28, 27 (2017). https://doi.org/10.1088/1361-6528/aa749e
[102] K. Zhang, X. Fang, Y.L. Wang, Y. Wan, Q.J. Song et al., Ultrasensitive near-infrared photodetectors based on a graphene-MoTe2-graphene vertical van der Waals heterostructure. ACS Appl. Mater.Interfaces 9(6), 5392-5398 (2017). https://doi.org/10.1021/acsami.6b14483
[103] X. Wei, F.G. Yan, C. Shen, Q.S. Lv, K. Y. Wang, Photodetectors based on junctions of two-dimensional transition metal dichalcogenides. Chinese Phys. B. 26(3), 038504 (2017). https://doi.org/10.1088/1674-1056/26/3/038504
[104] C.H. Lee, G.H. Lee, A.M. van der Zande, W.C. Chen, Y.L. Li et al., Atomically thin p-n junctions with van der Waals heterointerfaces. Nat. Nanotechnol. 9(9), 676-681 (2014). https://doi.org/10.1038/nnano.2014.150
[105] W.H. Wu, Q. Zhang, X. Zhou, L. Li, J.W. Su, F.K. Wang, T.Y. Zhai, Self-powered photovoltaic photodetector established on lateral monolayer MoS2-WS2 heterostructures. Nano Energy 51, 45-53 (2018). http://dx.doi.org/10.1016/j.nanoen.2018.06.049
[106] C. Choi, M.K. Choi, S.Y. Liu, M.S. Kim, O.K. Park et al., Human eye-inspired soft optoelectronic device using high-density MoS2-graphene curved image sensor array. Nat. Commun. 8, 1664 (2017). https://doi.org/10.1038/s41467-017-01824-6
[107] F. Wang, Z.X. Wang, K. Xu, F.M. Wang, Q.S. Wang, Y. Huang, L. Yin, J. He, Tunable GaTe-MoS2 van der Waals p-n junctions with novel optoelectronic performance. Nano Lett. 15(11), 7558-7566 (2015). http://dx.doi.org/10.1021/acs.nanolett.5b03291
[108] M.S. Long, E.F. Liu, P. Wang, A.Y. Gao, H. Xia et al., Broadband photovoltaic detectors based on an atomically thin heterostructure. Nano Lett. 16(4), 2254-2259 (2016). http://dx.doi.org/10.1021/acs.nanolett.5b04538
[109] K. Roy, M. Padmanabhan, S. Goswami, T.P. Sai, G. Ramalingam, S. Raghavan, A. Ghosh, Graphene-MoS2 hybrid structures for multifunctional photoresponsive memory devices. Nature Nanotechnology. 8(11), 826-830 (2013). http://dx.doi.org/10.1038/Nnano.2013.206
[110] S.J. Zheng, E.X. Wu, Z.H. Feng, R. Zhang, Y. Xie et al., Acoustically enhanced photodetection by a black phosphorus-MoS2 van der Waals heterojunction p-n diode. Nanoscale 10(21), 10148-10153 (2018). http://dx.doi.org/10.1039/c8nr02022a
[111] Q.M. Wang, Z.Y. Yang, Graphene photodetector with polydiacetylenes acting as both transfer-supporting and light-absorbing layers: Flexible, broadband, ultrahigh photoresponsivity and detectivity. Carbon 138, 90-97 (2018). http://dx.doi.org/10.1016/j.carbon.2018.05.054
[112] Y.J. Liu, C. Liu, X.M. Wang, L. He, X.G. Wan et al., Photoresponsivity of an all-semimetal heterostructure based on graphene and WTe2. Sci. Rep. 8, 12840 (2018). https://doi.org/10.1038/s41598-018-29717-8
[113] D. Xiang, T. Liu, J.L. Xu, J.Y. Tan, Z.H. Hu et al., Two-dimensional multibit optoelectronic memory with broadband spectrum distinction. Nat. Commun. 9, 2966 (2018). https://doi.org/10.1038/s41467-018-05397-w
[114] D. Unuchek, A. Ciarrocchi, A. Avsar, K. Watanabe, T. Taniguchi, A. Kis, Room-temperature electrical control of exciton flux in a van der Waals heterostructure. Nature 560(7718), 340-344 (2018). http://dx.doi.org/10.1038/s41586-018-0357-y
[115] B. Dlubak, M.-B. Martin, R.S. Weatherup, H. Yang, C. Deranlot et al., Graphene-passivated nickel as an oxidation-resistant electrode for spintronics. ACS Nano 6(12), 10930-10934 (2012). http://dx.doi.org/10.1021/nn304424x
[116] M.Z. Iqbal, M.W. Iqbal, S. Siddique, M.F. Khan, S.M. Ramay, Room temperature spin valve effect in NiFe/WS2/Co junctions. Sci. Rep. 6, 21038 (2016). http://dx.doi.org/10.1038/srep21038
[117] Z. Wang, D. Sapkota, T. Taniguchi, K. Watanabe, D. Mandrus, A.F. Morpurgo, Tunneling spin valves based on Fe3GeTe2/hBN/Fe3GeTe2 van der Waals heterostructures. Nano Lett. 18(7), 4303-4308 (2018). http://dx.doi.org/10.1021/acs.nanolett.8b01278
[118] H. Zhang, M. Ye, Y. Wang, R. Quhe, Y. Pan et al., Magnetoresistance in Co/2D MoS2/Co and Ni/2D MoS2/Ni junctions. Phys. Chem. Chem. Phys. 18(24), 16367-16376 (2016). http://dx.doi.org/10.1039/C6CP01866A
[119] V.M. Karpan, G. Giovannetti, P.A. Khomyakov, M. Talanana, A.A. Starikov et al., Graphite and graphene as perfect spin filters. Phys. Rev. Lett. 99(17), 176602 (2007). http://dx.doi.org/10.1103/PhysRevLett.99.176602
[120] M.Z. Iqbal, S. Siddique, G. Hussain, M.W. Iqbal, Room temperature spin valve effect in the NiFe/Gr–hBN/Co magnetic tunnel junction. J. Mater. Chem. C 4(37), 8711-8715 (2016). http://dx.doi.org/10.1039/C6TC03425J
[121] D. Xiao, G.B. Liu, W.X. Feng, X.D. Xu, W. Yao, Coupled spin and valley physics in monolayers of MoS2 and other group-VI dichalcogenides. Phys. Rev. Lett. 108(19), 196802 (2012). https://doi.org/10.1103/PhysRevLett.108.196802
[122] J. Lee, K.F. Mak, J. Shan, Electrical control of the valley Hall effect in bilayer MoS2 transistors. Nat. Nanotechnol. 11(5), 421-425 (2016). http://dx.doi.org/10.1038/nnano.2015.337
[123] K.F. Mak, K.L. McGill, J. Park, P.L. McEuen, The valley Hall effect in MoS2 transistors. Science 344(6191), 1489-1492 (2014). http://dx.doi.org/10.1126/science.1250140
[124] A.V. Stier, K.M. McCreary, B.T. Jonker, J. Kono, S.A. Crooker, Exciton diamagnetic shifts and valley Zeeman effects in monolayer WS2 and MoS2 to 65 Tesla. Nat. Commun. 7, 10643 (2016). https://doi.org/10.1038/ncomms10643
[125] L. Cai, J.F. He, Q.H. Liu, T. Yao, L. Chen et al., Vacancy-induced ferromagnetism of MoS2 Nanosheets. J. Am. Chem. Soc. 137(7), 2622-2627 (2015). https://doi.org/10.1021/ja5120908
[126] C. Zhao, T. Norden, P.Y. Zhang, P.Q. Zhao, Y.C. Cheng et al., Enhanced valley splitting in monolayer WSe2 due to magnetic exchange field. Nat. Nanotechnol. 12(8), 757-762 (2017). http://dx.doi.org/10.1038/Nnano.2017.68
[127] Y.K. Luo, J.S. Xu, T.C. Zhu, G.Z. Wu, E.J. McCormick et al., Opto-valleytronic spin injection in monolayer MoS2/few-layer graphene hybrid spin valves. Nano Lett. 17(6), 3877-3883 (2017). http://dx.doi.org/10.1021/acs.nanolett.7b01393
[128] Y.P. Liu, H. Idzuchi, Y. Fukuma, O. Rousseau, Y. Otani, W.S. Lew, Spin injection properties in trilayer graphene lateral spin valves. Appl. Phys. Lett. 102(3), 033105 (2013). https://doi.org/10.1063/1.4776699
[129] M.V. Kamalakar, C. Groenveld, A. Dankert, S.P. Dash, Long distance spin communication in chemical vapour deposited graphene. Nat. Commun. 6, 6766 (2015). https://doi.org/10.1038/ncomms7766
[130] F.G. Yan, Z.M. Wei, X. Wei, Q.S. Lv, W.K. Zhu, K.Y. Wang, Toward high-performance photodetectors based on 2D materials: Strategy on methods. Small Methods 2(5), 1700394 (2018). https://doi.org/10.1002/smtd.201700349

Citation Information

Yanping Liu, Siyu Zhang, Jun He, Zhiming M. Wang, Zongwen Liu, Recent Progress in the Fabrication, Properties, and Devices of Heterostructures Based on 2D Materials. Nano-Micro Lett.(2019) 11: 13. https://doi.org/10.1007/s40820-019-0245-5

History

Received: 13 December 2018 / Accepted: 28 January 2019 / Published online: 18 February 2019


Additional Info

  • Type of Publishing: JOUR - Journal
  • Title: Recent Progress in the Fabrication, Properties, and Devices of Heterostructures Based on 2D Materials
  • Author: Yanping Liu, Siyu Zhang, Jun He, Zhiming M. Wang, Zongwen Liu
  • Year: 2019
  • Volume: 11
  • Journal Name: Nano-Micro Letters
  • ISSN: 2150-5551
  • URL: http://dx.doi.org/10.1007/s40820-019-0245-5
  • Abstract: With a large number of researches being conducted on two-dimensional (2D) materials, their unique properties in optics, electrics, mechanics, and magnetics have attracted increasing attention. Accordingly, the idea of combining distinct functional 2D materials into heterostructures naturally emerged that provides unprecedented platforms for exploring new physics that are not accessible in a single 2D material or 3D heterostructures. Along with the rapid development of controllable, scalable and programmed synthesis techniques of high-quality 2D heterostructures, various heterostructure devices with extraordinary performance have been designed and fabricated, including tunneling transistors, photodetectors, and spintronic devices and so on. In this review, we present a summary of the latest progresses in fabrications, properties, and applications of different types of 2D heterostructures, followed by the discussions on present challenges and perspectives of further investigations.
  • Publish Date: Monday, 18 February 2019
  • Start Page: 13
  • DOI: 10.1007/s40820-019-0245-5