Tuning Metallic Co0.85Se Quantum Dots/Carbon Hollow Polyhedrons with Tertiary Hierarchical Structure for High-Performance Potassium Ion Batteries

View ResearcherID and ORCID

Zhiwei Liu1, Kun Han1, Ping Li1, *, Wei (Alex) Wang2, *, Donglin He1, Qiwei Tan1, Leying Wang1, Yang Li3, Mingli Qin1, Xuanhui Qu1

Abstract | Support Info
icon-htmlFull Text Html
icon-pdf-smPDF w/ Links
icon-citExport Citation
Figures
+Show more

Nano-Micro Lett. (2019) 11: 96

First Online: 01 November 2019 (Article)

DOI:10.1007/s40820-019-0326-5

*Corresponding author. E-mail: ustbliping@126.com (Ping Li); wwang3@g.harvard.edu (Wei (Alex) Wang)

 

Abstract

 


Toc

Potassium-ion batteries (KIBs) are a potential candidate to lithium-ion batteries (LIBs) but possess unsatisfactory capacity and rate properties. Herein, the metallic cobalt selenide quantum dots (Co0.85Se-QDs) encapsulated in mesoporous carbon matrix were designed via a direct hydrothermal method. Specifically, the cobalt selenide/carbon composite (Co0.85Se-QDs/C) possesses tertiary hierarchical structure, which is the primary quantum dots, the secondary petals flake, and the tertiary hollow micro polyhedron framework. Co0.85Se-QDs are homogenously embedded into the carbon petals flake, which constitute the hollow polyhedral framework. This unique structure can take the advantages of both nanoscale and microscale features: Co0.85Se-QDs can expand in a multidimensional and ductile carbon matrix and reduce the K-intercalation stress in particle dimensions; the micro petals can restrain the agglomeration of active materials and promote the transportation of potassium ion and electron. In addition, the hollow carbon framework buffers volume expansion, maintains the structural integrity, and increases the electronic conductivity. Benefiting from this tertiary hierarchical structure, outstanding K-storage performance (402 mAh g-1 after 100 cycles at 50 mA g-1) is obtained when Co0.85Se-QDs/C used as KIBs anode. More importantly, the selenization process in this work is newly reported and can be generally extended to prepare other quantum dots encapsulated in edge-limited frameworks for excellent energy storage.


 

Keywords

Cobalt selenides; Quantum dots; Potassium-ion batteries; Tertiary hierarchical structure; Hollow dodecahedron

 

Full Text Html

1 Introduction

    Rapidly increasing demands for energy on a global scale give impetus to the application and development of new energy. Lithium-ion batteries (LIBs) as a promising secondary battery have been extensively used in the fields of vehicles and electronic devices due to its high capacity [1-3]. However, the rising cost and limited reserve of Li resources restrict the further practical applications of LIBs, which offers the potential opportunities for other rechargeable batteries, such as aluminum-ion, potassium-ion, sodium-ion, magnesium-ion, and dual-ion batteries [4-11]. Owing to the substantial reserves of potassium and sodium elements on earth, potassium-ion batteries (KIBs) and sodium-ion batteries (NIBs) have been widely studied in energy storage fields. But the commercial graphite could not be used as NIBs anode, and the reduction potential of Na is -2.71 V (vs SHE), lower than -3.04 V (vs SHE) of Li [12]. Whereas the reduction potential of K is -2.93 V (vs SHE), very close to that of Li, which offer a new thought for the next generation of energy storage battery systems [13-15]. Compared with NIBs, the heavy K-ions may be not very competitive due to the increase in weight, however, the total mass of the KIBs is not vital for large-scale energy storage because of the energy density is low priority [14].
    In recent years, the KIBs anode materials are mainly graphite, graphene, soft/hard carbon, tin-based composites, transition-metal oxides, sulfides, and phosphides [16-23]. Nevertheless, the low cycling capacity and rate capability make the researchers seek new anode materials. Many researchers focus on the transition-metal chalcogenide (sulfide, selenide, and telluride) due to the higher capacity than conventional intercalation electrode materials. Among them, metal selenides used as KIBs anodes possess an increased attention on account of their good thermal stabilities, favorable mechanical, and electrical conductivities [24, 25], which makes them to obtain better rate performance and electrochemical stability. Recently, cobalt selenides with different nanostructures have been reported and exhibit excellent performances in the energy storage fields [26]. Nevertheless, the fast capacity fading resulting from the structural failure in the initial several cycles is still the bottleneck for its practical application, so it is imperative to use carbon matrix to buffer the volume expansion of cobalt selenide nanocomposites in the discharge/charge cycle.
    Moreover, the miniaturization and dispersion of active materials on carbon support are also difficult issues to be solved. Although the active materials with tiny size (e.g., quantum dots (QDs)) have the ability to expand in a ductile and multidimensional surrounding [27], small-sized nanoparticles are prone to agglomeration and form inactive clusters, and thus improving the dispersion of active materials on carbon matrix is imperative [28]. Meanwhile, constructing 3D hierarchical network can profitably enhance the structural integrity and their electrochemical properties. The 3D hierarchical structure can effectively accommodate the mechanical stress and rapidly transfer ions, improving the rate performance and reducing the polarization. Therefore, controlling the uniform dispersion of nanoparticles in hierarchical structure becomes the focus of researches. Generally, the metal organic frameworks (MOFs) structure can meet the above requirements [29-31]. QDs, carbon matrix, and hierarchical structure can be obtained by further processing different MOFs. Lou et al. reported that the hierarchical structure of CoSe@carbon nanoboxes was synthesized through the template-engaged reaction [32], which manifests excellent electrochemical performance for LIBs. However, the conventional selenization process of the MOFs consumes a mass of energy and produces harmful gases. Hydrothermal method is simple to carry out at a lower temperature and reduces energy consumption. So far, no research was reported about the one-step modification of MOFs by hydrothermal selenization.
    In this work, we prepare the cobalt selenide quantum dots (Co0.85Se-QDs) encapsulated in mesoporous polyhedral carbon (C) matrix through one-step hydrothermal selenization for the first time. The shape-controllable Co0.85Se-QDs/C composite with petal-shaped shell exhibits good specific surface area and effectively buffers relative volume change, which endowing outstanding specific capacity, excellent rate performance, and favourable cycling stability. Thus, the Co0.85Se-QDs/C electrode shows an ultrahigh capacity of 402 mAh g-1 after 100 cycles at the current density of 50 mA g-1 with a good capacity retention of 99%. Besides, the reduction potential of the Co0.85Se-QDs/C electrode (0.5 V) overtops the plating voltage of K-metal (0.01 V), which can avoid the formation of metal dendrites and enhance their safety. The phase transition process was further investigated by the first-principles calculations.

2 Experimental

2.1 Synthesis of Co-based Polyhedron Precursor
    ZIF-67 polyhedron (denoted as Co polyhedron) precursor was synthesized on the basis of a previously reported literature with slight modification [33]. Cobalt nitrate hexahydrate powder (0.29 g) was added into methanol solution (25 mL) and kept stirring in a beaker for 10 min to form a pink solution. Afterwards, a mixture of 2-methylimidazole (0.328 g) and methanol solution (25 mL) was dropwise added into the former beaker under continuous stirring. When two solutions were mixed together, stirring was stopped. Finally, the purple precipitates were collected by centrifugation after aged at room temperature for 24 h, washed three times with absolute ethyl alcohol, and dried in a vacuum oven for further use.
2.2 Synthesis of Co0.85Se-QDs/C Composite
    In a typical route, Co polyhedron precursor (0.039 g), H2SeO3 (0.013-0.052 g), and hydrazine hydrate (N2H4·H2O) (0-20 mL) were mixed to form a mixture solution. Then the mixture solution was transferred into the Teflon-lined stainless-steel autoclaves and ultrasonic stirring for 15 min. The autoclave was sealed and retained at 140-220 °C for 24 h in a drying oven without any agitating and then allowed to gradually cool down to room temperature after heat treatment. The final sample was obtained by free sedimentation, washed with absolute ethyl alcohol and dried in a vacuum box at 65 °C for 4 h. Based on different amounts of hydrazine hydrate (20, 10, 2, and 0 mL), the as-prepared samples are named as Co0.85Se-QDs/C-20, Co0.85Se-QDs/C-10, Co0.85Se-QDs/C-2 and Co0.85Se-QDs/C-0, respectively.
2.3 Materials Characterizations
    The phase of all the materials were measured by the X-Ray powder diffraction (XRD) with Cu Kα radiation (Rigaku D/max-RB12 X-Ray diffractometer). The morphologies and surface elemental compositions of the samples were observed by field emission scanning electron microscopy (FESEM, JEOL, JSM-7001F). The transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HRTEM) images were observed by the transmission electron microscopy (JEOL, JEM-2010). The energy dispersive X-ray spectra (EDS) and scanning transmission electron microscopy (STEM) analyses were implemented by using a Hitachi HD2700C (200 kV). X-ray photoelectron spectra (XPS) were carried out with an ESCALAB 250 spectrometer (PerkinElmer) to explore the valence states of surface elements. The Raman spectra (Renishaw RM2000) with a wavelength of 532 nm was used to investigate the crystallization degree of carbon at room temperature. Differential scanning calorimetry (DSC) and thermogravimetric (TG) were tested using Seiko 6300 instrument. Brunauer-Emmett-Teller (BET) method was used to characterize the specific surface area of the samples.
2.4 Electrochemical Measurements
    Electrochemical measurements were carried out using the CR2023-type coin cells. The working electrode was the as-prepared Co0.85Se-QDs/C, and the K metal worked as both the reference and counter electrodes. The synthesized Co0.85Se-QDs/C were mixed with polyvinylidene fluoride (PVDF) in the weight ratio of 8:2. The coated foil was punched into pellets with a diameter of 10 mm, and the mass loading of the pellets is ~1.2 mg cm-2. A non-aqueous electrolyte solution consisted of 1 M KFSI and dimethyl ether (DME). The separator is the glass fiber (GF/D) from Whatman. The coin cells were assembled and disassembled in an argon atmosphere glovebox. The coin cells were galvanostatically discharged and charged using LAND-CT2011A battery-testing instrument under 25 °C, and the testing voltage performed range from 0.01 to 2.5 V. Cyclic voltammograms (CVs) scanned at 0.1 mV s-1 in a voltage window of 0.01-2.5 V were measured by an electrochemistry workstation (CHI660E).
2.5 Computational Section
    The first principle calculations were carried out using density functional theory (DFT) with the Perdew-Burke-Ernzerbof (PBE) form of generalized gradient approximation functional (GGA) [34]. The Vienna ab-initio simulation package (VASP) was employed [35-38]. The plane wave energy cutoff was set as 400 eV. The SCF energy (converged to 1.0 ×10-6 eV atom-1) and the Hellman-Feynman force (converged to 0.01eV Å-1) were set as the convergence criterion for geometry optimization. We chose the Co7Se8 closest to Co0.85Se as the initial structure for K doped/replacement reaction. The first Brillouin zone was sampled in the Monkhorst-Pack grid [39] with the 4×4×4 k-point mesh for the initial structures of Co7Se8 with 15 atoms for the potassium replacement reaction, and the same dense mesh for the reaction products (KxCo(7-x)Se8).
    As potassium reacted with the Co7Se8, refer to the following reaction (1):

Co7Se8 + xK → KxCo(7-x)Se8 + xCo              (1)

    Thus, the formation energy for reaction (1) is defined as:

Ef = Etot (KxCo(7-x)Se8) + xE (Co) – xE (K) - Etot (Co7Se8)    (2)
E (Co) = 1/2 Etot (Co)                     (3)
E (K) = 1/2 Etot (K)                      (4)

where Etot is the total energy of corresponding compounds, and Etot (K) and Etot (Co) are the total energy of bulk K and Co, respectively. x is the number of Co atoms replaced by K atoms. The negative (positive) Ef denotes the K replacement can be easily (hardly) occurred.

3 Results and Discussion

    The prepared process of the hierarchical Co0.85Se-QDs/C composite materials is schematically shown in Fig. 1. Firstly, the positively charged Co2+ and 2-methylimidazole aqueous solution were added to allow the heterogeneous nucleation and in-situ growth of Co-based zeolitic imidazolate framework (ZIF-67) crystal. The subsequent step was the selenization process by hydrothermal synthesis using hydrazine hydrate and seleniousacid as reductant and selenium source, respectively. During the hydrothermal process, the ZIF-67 as a precursor reacted with selenide ion to form cobalt sulfide QDs accompanied with the formation of mesoporous carbon polyhedra via the carbonization of the organic ligands. As a result, tertiary hierarchical Co0.85Se-QDs/C composite was obtained.

Fig. 1 Schematic illustration of the synthesis process for Co0.85Se-QDs/C composite

Fig. 1 Schematic illustration of the synthesis process for Co0.85Se-QDs/C composite

    The FESEM and TEM images of ZIF-67 show that the precursor consist of uniform polyhedral particles with size of ~1 um (Figs. 2a and S1). The XRD pattern of Co polyhedron precursor exhibits typical ZIF-67 characteristic (Fig. S2a). The FESEM images (Fig. 2b, c) show that Co0.85Se-QDs/C-20 composite has small divergent lamellas on the surface of hollow polyhedron. The TEM images (Fig. 2d, e) further demonstrate the hollow polyhedral structure with petal-shaped shell, which is in good agreement with the FESEM observations in Fig. 2c. H2SeO3 was reduced to Se and further transformed into selenide ion by hydrazine hydrate during the selenization process, reacting with Co polyhedron precursor to form Co0.85Se due to their thermodynamically stable and lower solubility [40]. The formation of hollow structure comes from the diffusion of Co2+ from interior to surface exceeded the diffusion of Se2−, which can be considered as the Kirkendal effect [41, 42].The lamellate shell (insert of Fig. 3e) is attributed to the structural collapse of Co precursor during the selenide reaction [43]. The lattice fringe of Co0.85Se-QDs in magnification could be clearly observed with the size of 0.269 nm (Fig. 2f), which coincides with the (101) plane of Co0.85Se. The Co0.85Se-QDs/C-20 composite consists of tertiary hierarchical structure, which is the primary Co0.85Se QDs (Fig. S2b), the secondary carbon-petal flake, and the tertiary hollow carbon polyhedron framework. The selected area electron diffraction (SAED) image (insert of Fig. 2f) confirms the polycrystalline crystal structure of Co0.85Se-QDs. Additionally, the elemental mapping by EDS testing (Fig. 2g-j) verifies the uniform distribution of the carbon, cobalt, and selenium in the Co0.85Se-QDs/C-20 composite.

Fig. 2 a SEM images of Co-based precursor. b, c SEM images and d, e TEM images of Co0.85Se-QDs/C-20. f High-resolution TEM image and SAED pattern of Co0.85Se-QDs/C-20. g STEM image of Co0.85Se-QDs/C-20 and h-j the corresponding elemental mappings of the C, Co, and Se elements

Fig. 2 a SEM images of Co-based precursor. b, c SEM images and d, e TEM images of Co0.85Se-QDs/C-20. f High-resolution TEM image and SAED pattern of Co0.85Se-QDs/C-20. g STEM image of Co0.85Se-QDs/C-20 and h-j the corresponding elemental mappings of the C, Co, and Se elements

    To study the structural evolution and optimize the electrochemical performance, the morphology and particles size of Co0.85Se-QDs/C composite are changed by varying the preparation temperature in the selenization process. The as-prepared Co0.85Se-QDs/C samples are denoted as Co0.85Se-QDs/C-160, Co0.85Se-QDs/C-180, and Co0.85Se-QDs/C-220 synthesized under the temperatures of 160 °C, 180 °C, and 220 °C, respectively (Fig. S3). When the hydrothermal temperature is 160 °C, the Co0.85Se-QDs/C-160 still retains the partial unreacted ZIF-67 polyhedron with broadened XRD peaks due to the incomplete reaction (Figs. S3a, b and S4). With the temperature increases to 180 °C, the surface of Co0.85Se-QDs/C-180 gradually becomes petal-shaped shell (Fig. S3c, d), and XRD intensity of Co0.85Se phase is significantly increased and the diffraction peaks of CoSe2 phase are reduced. However, Co0.85Se-QDs/C-220 polyhedral particles are broken up when the hydrothermal temperature reaches to 220 °C, the (Fig. S3e, f) and the diffraction peaks of Co0.85Se, Co9Se8, and CoSe2 phase simultaneously appear in the XRD pattern. Thus, the optimized hydrothermal temperature of 200 °C is chosen in this work.
    The amount of selenite also has a significant effect on the phase and morphology of Co0.85Se-QDs/C composite. According to the additive amount of selenite from 0.026, 0.039, to 0.052 g, the obtained Co0.85Se-QDs/C composite are denoted as Co0.85Se-QDs/C-26, Co0.85Se-QDs/C-39 and Co0.85Se-QDs/C-52, respectively. With the increasing of H2SeO3, the morphology of Co0.85Se-QDs/C composite varies from nanosheets to porous spheres (Fig. S5). The diffraction peaks of Co0.85Se are gradually weakened, whereas CoSe2 phase is gradually strengthened in the XRD pattern (Fig. S6). This result indicates that different amounts of H2SeO3 in the hydrothermal selenization process can regulate the polyhedral morphology of the products.
    To further investigate the growth mechanism of Co0.85Se-QDs/C-20, the reductant is controlled to explain the structural evolution from Co-based polyhedron precursor to mesoporous and hollow Co0.85Se-QDs/C-20 composite (Figs. S7-S9).. When the addition amount of hydrazine hydrate is 10 mL, Co0.85Se-QDs/C-10 presents spherical morphology with rough surface (Fig. S7a). The Co0.85Se-QDs/C-10 exhibits similar hollow structure to Co0.85Se-QDs/C-20 (Fig. S7b). The HRTEM image of Co0.85Se-QDs/C-10 shows two different lattice fringes with spacings of 0.269 and 0.238 nm, corresponding to the (101) plane of Co0.85Se and the (211) plane of CoSe2, respectively (Fig. S7c). The SAED image further verify the coexistence of Co0.85Se and CoSe2 in Co0.85Se-QDs/C-10, which is in accordance with the XRD results (Fig. S10). When the addition amount of hydrazine hydrate decreases to 2 mL, the Co0.85Se-QDs/C-2 shows flake morphology decorated with agglomerated nanoparticles (Fig. S8a-c), and the HRTEM images display that Co0.85Se-QDs/C-2 contains monocrystalline Co(OH)2 phase and Co0.85Se phase (Fig. S8d, e). The SAED image (Fig. S8f) further shows the monocrystalline characteristic of Co(OH)2. Without the addition of hydrazine hydrate, the Co0.85Se-QDs/C-0 is composed of Co3O4, Co0.85Se, CoSe2, Co9Se8, Co(OH)2, and Se phases, which presents the dominating rod-like polycrystal of Co3O4 (Fig. S9). Using optimized ratio of reducing agent and oxidizer after selenization, pure-phased cobalt selenide with polyhedral structure can be obtained [44, 45]. When the amount of hydrazine hydrate is abundant, selenium and cobalt ions react to form a thin barrier layer of cobalt selenide in the polyhedron surface. The mechanism involved for the hollow architecture is attributed to the ion exchange reaction. As the amount of hydrazine hydrate decreases, only partial selenium ions are formed, and cobalt ions react with hydroxide to form flake cobalt hydroxide. The hydrothermal reaction completely destroys the polyhedron due to the direct effect of selenite to Co-based polyhedron precursor when hydrazine hydrate is not added, leading to the appearance of cobalt oxide nanowires.
    Figure 3a reveals the XRD curves of the as-synthesized Co0.85Se-QDs/C-20 at 200 °C for 24 h. All the strong diffraction peaks of the sample are assigned to the Co0.85Se phase with a hexagonal crystal structure (JCPDS 52-1008), which indicates the complete conversion of ZIF-67 to Co0.85Se-QDs/C-20. Moreover, the wide diffraction peaks of the Co0.85Se phase are related to large lattice strain and the ultrafine crystalline size [46], which further explains that amorphous carbon shells can prevent Co0.85Se nanoparticles from continuous growing in the hydrothermal process, leading to the formation of Co0.85Se QDs [47]. No reflection contacted with carbon in the XRD pattern is observed due to its amorphous nature. The chemical composition of Co0.85Se-QDs/C-20 is further detected by EDS spectrum (Fig. S11), confirming the presence of carbon, cobalt, and selenium elements. The element content of Co0.85Se-QDs/C-20 was summarized in Table S1. Figure 3b shows the Raman spectrum of the as-synthesized Co0.85Se-QDs/C-20. It can be clearly seen that the intensity of D-band around 1350 cm-1 (corresponded to disorder or defective carbon) is much stronger than that of the G-band around 1580 cm-1 (corresponded to graphitic carbon). And the relative intensity ratio of D to G-band (ID/IG) is 1.92, manifesting its low degree of graphitization. The diverse porosity of the Co0.85Se-QDs/C-20 is investigated by N2 adsorption/desorption tests (Fig. 3c). The Co0.85Se-QDs/C-20 presents a typical type IV curve, indicating the existence of mesoporous structure. The Brunauer-Emmett-Teller (BET) specific surface area of Co0.85Se-QDs/C-20 is 112 m2 g-1. The average pore size distribution of Co0.85Se-QDs/C-20 (insert of Fig. 3c) shows massive mesoporous in the range of 4~9 nm. TG-DSC curves of Co0.85Se-QDs/C-20 is carried out at 20~800 °C in air (Fig. S12). Based on the TG analysis, the carbon content in the composites is estimated to be approximately 15 wt%.

Fig. 3 Structural characterizations of the as-synthesized Co0.85Se-QDs/C-20. a XRD pattern. b Raman pattern. c N2 adsorption isotherm and pore-size distribution. Peak deconvolutions of the XPS spectra: d C 1s, e Co 2p, f Se 3d

Fig. 3 Structural characterizations of the as-synthesized Co0.85Se-QDs/C-20. a XRD pattern. b Raman pattern. c N2 adsorption isotherm and pore-size distribution. Peak deconvolutions of the XPS spectra: d C 1s, e Co 2p, f Se 3d

    XPS analysis was carried out to confirm the surface electronic state and the chemical composition of Co0.85Se-QDs/C-20 (Fig. 3d-f). The survey scan spectrum shows that the elemental components of the Co0.85Se-QDs/C-20 are mainly cobalt, carbon, oxygen, and selenium (Fig. S13). The spectra are calibrated by the standard C 1s signal located at 284.8 eV. As shown in Fig. 3c, the detected C peaks of C 1s spectrum divided into three peaks, corresponding to the C-C, C-O, and O-C=O bonds located at 284.6, 285.8, and 288.6 eV, respectively. The Co 2p spectrum are deconvoluted into four main peaks at the binding energies of 778.5, 780.8, 796.3, and 797.5 eV, corresponding to the Co-Se and Co-O of Co 2p3/2, Co-Co, and Co-O of Co 2p1/2, respectively. Besides, two small peaks of Co2+ centered at 782.6 and 798.8 eV can be corresponding to cobalt hydroxides. Furthermore, two shake-up satellites for a higher-energy Co 2p signal correspond to the antibonding orbital between selenium and cobalt atoms [48]. Among them, the weak Co-Co bonding of Co 2p1/2 stems from trace amounts of unreacted Co nanospheres during selenization, and the Co-O bonding could be attributed to the tiny amount of SeO2 generated during selenization and partial surface oxidation in air. As exhibited in Fig. 3f, the peaks at 55.5 and 54.6 eV could be assigned to Se 3d3/2 and Se 3d5/2, respectively, corresponding to the metal-Se interactions of the Co0.85Se-QDs/C-20. The peaks at 58~61 eV are ascribed to oxygen-selenium bonding existed in the sample surface and Co 3p [49]. The d-electron configuration of metal cations can effectively influence the physical characteristics of the metal dichalcogenides [50]. The Co 3d electrons of Co0.85Se make it view as a metallic conductor by adopting a low-spin configuration in the form of t2g6eg1 [51]. The metallic property can benefit the transportation of electrons through active electrodes, leading to an excellent rate performance.
    Electrochemical tests were used to evaluate the potassium storage performance of the Co0.85Se-QDs/C-20 electrode using the CR2032-type coin cells at 25 °C. The galvanostatic discharge/charge profiles of the Co0.85Se-QDs/C-20 electrode at 50 mA g-1 are presented in Fig. 4a. The initial discharge/charge capacities are 648 and 401 mAh g-1, respectively, which accords with the Columbic Efficiency (CE) of 61.8%. The observed capacity loss is due to the formation of the solid electrolyte interphase (SEI) layer on the surface of the electrodes [52], corresponding to the cycle voltammetry (CV) curves of the Co0.85Se-QDs/C-20 (Fig. S14). A plateau at around 0.9 V in the first discharge curve can be ascribed to the phase transformation from Co0.85Se to Co and K2Se [53], and a plateau at around 1.5 V in the first charge curve could be assigned to the inverse phase transformation. After several cycles, the capacity loss of the Co0.85Se-QDs/C-20 is nearly negligible, indicating a high discharge/charge reversibility. Meanwhile, the voltage plateau of the Co0.85Se-QDs/C-20 (0.5 V) is higher than the plating voltage of potassium metal (0.01 V), which can avoid the risk of dendrite formation.

Fig. 4 Electrochemical potassium storage performance of Co0.85Se-QDs/C composite. a The 2nd, 3rd, 5th, 10th, 50th, and 100th charge/discharge profiles of Co0.85Se-QDs/C-20 at 50 mA g-1 for KIBs (inset is the charge/discharge profiles of the first cycle). b Charge/discharge capacity and Coulombic efficiency of Co0.85Se-QDs/C-20 at 50 mA g-1. Comparison of c cycling stability and d rate performance under different current densities of the as-prepared Co0.85Se-QDs/C samples. e Long-term cycling stability and Coulombic efficiency at a high current density of 1 A g-1 over 500 cycles

Fig. 4 Electrochemical potassium storage performance of Co0.85Se-QDs/C composite. a The 2nd, 3rd, 5th, 10th, 50th, and 100th charge/discharge profiles of Co0.85Se-QDs/C-20 at 50 mA g-1 for KIBs (inset is the charge/discharge profiles of the first cycle). b Charge/discharge capacity and Coulombic efficiency of Co0.85Se-QDs/C-20 at 50 mA g-1. Comparison of c cycling stability and d rate performance under different current densities of the as-prepared Co0.85Se-QDs/C samples. e Long-term cycling stability and Coulombic efficiency at a high current density of 1 A g-1 over 500 cycles

    The cycle performance of the Co0.85Se-QDs/C-20 at 50 mA g-1 over 100 cycles is shown in Fig. 4b. During the initial cycle, the serious capacity fading can be mainly ascribed to the incomplete formation of SEI layer, which is consistent with the discharge/charge curves. After several cycles of cell activation, the slight capacity rise is ascribed to the activation process during reversible cycle process [54]. Moreover, a high capacity of 402 mAh g-1 with a relatively high efficiency around 99% is achieved even after 100 cycles, indicating the excellent cycling stability of Co0.85Se-QDs/C-20. Such high capacity is closely related to the hierarchical structure that is advantageous to potassium storage. The primary Co0.85Se QDs can fully react with potassium ions and maximize discharge/charge capacity for KIBs. The secondary carbon-petal provides stable transportation path for potassium ion and electron, which is favorable for potassiation/depotassiation. The tertiary hollow carbon polyhedron framework prevents the agglomeration of active materials, maintains structural integrity as well as boosts the electronic conductivity.
    For comparison, the cycling stabilities of Co0.85Se-QDs/C-10, Co0.85Se-QDs/C-2, and Co0.85Se-QDs/C-0 are also tested (Fig. 4c). They present a lower capacity than that of the Co0.85Se-QDs/C-20 under the same testing condition. After 100 cycles, Co0.85Se-QDs/C-10, Co0.85Se-QDs/C-2, and Co0.85Se-QDs/C-0 only achieve reversible capacities of 236, 166, and 87 mAh g-1, respectively, indicating poor electrochemical performance. The phenomenon could be attributed to the change of phase and structure influenced by the amount of hydrazine hydrate, which produces the side reactions and unstable SEI, causing the structural damage and capacity fading in the discharge/charge process. In addition, the capacity of the Co0.85Se-QDs/C-20 is higher than that of other reported selenide anode materials of KIBs (Table S2), demonstrating promising potential for application. Meanwhile, in order to investigate the influence of the crucial role of the electrolytes on potassium storage performance, we compare the cycling stability of Co0.85Se-QDs/C-20 in a voltage range of 0.01-2.5 V at 50 mA g-1 with selected four electrolytes of 0.8 M KPF6 in EC/DEC and 1 M KPF6 in diglyme (Fig. S15, S16). The Co0.85Se-QDs/C-20 composite shows high initial capacities of 714 and 736 mAh g-1, respectively, but the capacity rapid fading after 10 cycles is ascribed to side reaction in the discharge/charge process. The cycling performance of Co0.85Se-QDs/C-20 electrode used the KFSI in DME-based electrolytes is superior than that of the KPF6 in EC/DEC and diglyme-based electrolytes, indicating a better chemical stability with polysulfides of DME-based electrolytes, which could be attributed to the highly stable inorganic SEI layer formed on the surface of electrode by using KFSI in DME electrolytes [55, 56]. Therefore, we choose the KFSI in DME as electrolyte in this work.
    The rate performances of the Co0.85Se-QDs/C-20, Co0.85Se-QDs/C-10, Co0.85Se-QDs/C-2, and Co0.85Se-QDs/C-0 were evaluated at various current densities from 50 to 1000 mA g-1. As shown in Fig. 4c, the Co0.85Se-QDs/C-20 electrode shows reversible capacities of 402, 369, 337, 296, and 253 mAh g-1 at constant current rates of 50, 100, 200, 500, and 1000 mA g-1, respectively. Even at the ultrahigh current density of 2000 mA g-1, it can still deliver a high reversible capacity of 220 mAh g-1, which can be considered as a quick discharge/charge electrode material. After 60 cycles at various current densities, the capacity is resumed to 401 mAh g-1 when the current density returns to 50 mA g-1, indicating good stability and rate performance. For most of the cycles, the capacity of the Co0.85Se-QDs/C-20 is relatively stable at each rate and the Coulombic efficiency is above 99%. However, the capacities of the Co0.85Se-QDs/C-10, Co0.85Se-QDs/C-2, and Co0.85Se-QDs/C-0 decrease rapidly to 137, 86, and 45 mAh g-1 at the current density of 2000 mA g-1, respectively. When the current density is abruptly set back to 50 mA g-1, the capacities of Co0.85Se-QDs/C-2 and Co0.85Se-QDs/C-0 cannot return to its initial values, which is due to the impure phases and structural collapse. The galvanostatic discharge curves of the Co0.85Se-QDs/C-20 at different rates are shown in Fig. S17a. Remarkably, the potassiation plateau are steady, demonstrating high reversibility. The long-term cycling performance is further investigated by the extended charge and discharge experiments (Fig. 4e). The original polyhedron structure of the Co0.85Se-QDs/C-20 is still retained after 100 cycles, indicating the stable potassium storage performance (Fig. S17b). At a current density of 1A g-1, the Co0.85Se-QDs/C-20 electrode delivers a high initial reversible capacity of 280 mAh g-1 and stabilizes at around 228 mAh g-1 after 500 cycles. The excellent rate performance and long-term cycling performance could be ascribed to the high electronic conductivity and the stable hierarchical structure. In addition, a comparison of the electronic conductivity of the Co0.85Se-QDs/C-20 and pure Co0.85Se was carried out by four-probed method [57] (Table S3), and the Co0.85Se-QDs/C-20 shows a high electronic conductivity.
    The electrochemical dynamics of the Co0.85Se-QDs/C-20 electrode with potential pseudocapacitive behavior is studied. The CV curves at various scan rates from 0.1 to 2 mV s-1 are shown in Fig. S18a, displaying similar shapes with broad peaks during both cathodic and anodic processes. Based on the previous reports [58], the peak current (i) and the scan rate (υ) can follow the relationship of i = avb, where i is peak current, ν is scan rate, a and b are adjustable constants. Meanwhile, the b-value can be obtained by the slope of the log (i) vs. log (υ) plot. If b-value is close to 0.5, the charge storage is dominated by the ionic diffusion, whereas the b-value of 1 represents a capacitive response [59, 60]. The b-value of 0.77 for the Co0.85Se-QDs/C-20 electrode (Fig. S18b) indicates that the charge storage behavior is controlled by both the K ion diffusion and the pseudocapacitive effect. Furthermore, the ratio of pseudocapacitive contribution can be further quantitatively determined by separating the Equation of i = k1v + k2v1/2, where k1v and k2v1/2 represent the contribution of pseudocapacitance and ionic diffusion, respectively. Figure S18c shows the capacitive contributions of the Co0.85Se-QDs/C-20 electrode at 0.1, 0.2, 0.5, 1, and 2 mV s−1. The capacitive charge contribution rises with the scanning rate increases. The capacitive-controlled capacity makes up about 47.3% in the total charge storage at 0.1 mV s−1 (Fig. S18d), which indicates the significant role of the capacitive charge storage in the total capacity. These results show that the charge storage mechanism contains the ion diffusion and the additional pseudocapacitance contribution, leading to a high capacity and rate capability.
    The electrochemical impedance spectroscopy (EIS) was carried out to further research the electrochemical reaction process, and the corresponding Nyquist plots of the Co0.85Se-QDs/C-20, Co0.85Se-QDs/C-10, Co0.85Se-QDs/C-2, and Co0.85Se-QDs/C-0 electrodes in original cycle were measured (Fig. S19a). An equivalent circuit was used for fitting the electrochemical impedance spectra (insert of Fig. S19a). All of impedance spectra consist of a depressed semicircle in the high frequency range and a slope line in the low frequency range. The depressed semicircle corresponds to the electrode resistance (Rs) and the charge-transfer impedance (Rct), the slope line is related to the Warburg impedance (W). For the original state, the charge-transfer impedance of Co0.85Se-QDs/C-20 is lower than the other electrodes, portending the good ionic conductivity. The slope line in the low frequency range is almost vertical to the real axis in the imaginary part of the impedance, indicating its capacitor characteristic. The Nyquist plots of the Co0.85Se-QDs/C-20 electrode for different cycles are shown in Fig. S19b. The radius of the charge transfer part increases slightly in the subsequent cycle, indicating good reversibility.
    The reasons for the excellent electrochemical performance of the as-prepared Co0.85Se-QDs/C-20 are as follows: (i) The tertiary hierarchical structure can reduce the K-intercalation stress in particle dimensions, provide large surface area, prevent the agglomeration of active materials, facilitating the transportation of potassium ion and electron and maintaining the structural integrity. (ii) Because of the metallic property, the transportation of electrons in Co0.85Se is faster than other insulating anode materials. In addition, the present of carbon skeleton can effectively enhance the electric conductivity of the composite, improving the rate capability. (iii) The non-ignorable capacitive contribution has a significant influence on its high capacity and rate performance. These synergistic effects endow the Co0.85Se-QDs/C-20 with ultrahigh reversible capacity, excellent rate capability and cycling stability. Here we have to admit that the voltage plateau of K-ion full-cell comprising Co0.85Se-QDs/C composite as an anode will be a bit lower than the classical graphite anode owing to the high de-lithiation potential of Co0.85Se-QDs/C composite. However, the cyclic stability, rate capability, and specific capacity of Co0.85Se-QDs/C composite are better than the classical graphite anode.
    To further understand the potassium storage mechanism of the Co0.85Se, the first-principle calculations (Fig. 5) and ex-situ XRD measurements (Fig. S20) were employed to investigate the replacement process of K-ions into the Co7Se8 (closest to Co0.85Se) crystal structure. A positive formation energies (Ef) indicates an endothermic and unstable K substitution reaction while a negative Ein suggests an exothermic and stable reaction. Figure 5 shows the calculated Ef with respect to the number of K ions react with Co7Se8 and schematic molecular structures. The corresponding structure information and total energy of different compositions are shown in Table S4. The replacement reactions for the Co7Se8 can be explained as follows:

Co7Se8 + K+ + e- → K1Co6Se8 + Co, Ef = 1.12 eV                    (5)
Co7Se8 + 2 K+ + 2 e- → K2Co5Se8 + 2 Co, Ef = -1.18 eV             (6)
Co7Se8 + 3 K+ + 3 e- → K3Co4Se8 + 3 Co, Ef = -4.77 eV              (7)
Co7Se8 + 4 K+ + 4 e- → K4Co3Se8 + 4 Co, Ef = -3.32 eV             (8)

Fig. 5 Density functional theory (DFT) calculations. a The relationship between the formation energy and the number of K. b-f Schematic molecular structures of the formed compounds

Fig. 5 Density functional theory (DFT) calculations. a The relationship between the formation energy and the number of K. b-f Schematic molecular structures of the formed compounds

    It can be seen that the formation energies of reaction (6)-(8) are negative, suggesting that the three replacement reactions are favorable during cycling. Moreover, it is worth noting that the reaction (7) exhibits the largest negative formation energy, suggesting that the substitution reactions for K ions from Co7Se8 into Co and K3Co4Se8 are energetically favorable. This spontaneous substitution reaction can well explain the high capacity of the Co0.85Se-QDs/C-20 electrode, which is similar to the conversion reaction of Na ions in CoSe2. We believe that the proposed strategy and results may offer a positive impression for the development of high-performance KIBs

4 Conclusions

    In summary, we have successfully synthesized the Co0.85Se-QDs/C composite materials, which is used as an anode material for KIBs. This tertiary hierarchical structure togethering with the metallic nature of cobalt selenide QDs and its high mass loading and dispersity effectively achieves ultrahigh reversible capacity, good cycling stability, and excellent rate capability for high-performance KIBs. Co0.85Se-QDs/C-20 can deliver an ultrahigh capacity of 402 mAh g-1 at 50 mA g-1 after 100 cycles with the relatively high efficiency of approximately 99% by using the special KFSI in DME electrolyte. Even at a very high current density of 1 A g-1 over 500 cycles, the capacity can still maintain 228 mAh g-1. These results indicate that the Co0.85Se-QDs/C-20 could be a promising anode candidate for KIBs, and we expect that this synthetic route could guide the synthesis of edge-limited framework composites for energy storage and conversion.

Acknowledgements

    This work is financially supported by Beijing Natural Science Foundation (No. 2192034), China Postdoctoral Science Foundation (No. 2018M631335) and National Key R&D Program of China (No. 2018YFB0905600).

 

References

[1] N. Liu, Z.D. Lu, J. Zhao, M.T. McDowell, H.W. Lee, W.T. Zhao, Y. Cui, A pomegranate-inspired nanoscale design for large-volume-change lithium battery anodes. Nat. Nanotechnol. 9, 187 (2014). https://doi.org/10.1038/nnano.2014.6
[2] S.H. Choi, T.W. Kwon, A. Coskun, J.W. Choi, Highly elastic binders integrating polyrotaxanes for silicon microparticle anodes in lithium ion batteries. Science 357, 279-283 (2017). https://doi.org/10.1126/science.aal4373
[3] M. Freire, N.V. Kosova, C. Jordy, D. Chateigner, O.I. Lebedev, A. Maignan, V. Pralong, An active Li-Mn-O compound for high energy density Li-ion batteries. Nat. Mater. 15, 173 (2016). https://doi.org/10.1038/nmat4479
[4] X.D. Xiang, K. Zhang, J. Chen, Recent advances and prospects of cathode materials for sodium-ion batteries. ChemInform 46, 5343-5364 (2015). https://doi.org/10.1002/chin.201544273
[5] Z.W. Liu, P. Li, G.Q. Suo, S. Gong, W. Wang et al., Zero-strain K0.6Mn1F2.7 hollow nanocubes for ultrastable potassium ion storage. Energy Environ. Sci. 11, 3033-3042 (2018). https://doi.org/10.1039/C8EE01611A
[6] L. Fan, R.F. Ma, J. Wang, H.G. Yang, B.A. Lu, An ultrafast and highly stable potassium-organic battery. Adv. Mater. 30, 1805486 (2018). https://doi.org/10.1002/adma.201805486
[7] K. Han, Z.W. Liu, P. Li, Q.Y. Yu, W.A. Wang et al., High throughput fabrication of 3D N-doped graphenic framework coupled with Fe3C@porous graphite carbon for ultrastable potassium ion storage. Energy Storage Mater. 22, 185-193 (2019). https://doi.org/10.1016/j.ensm.2019.01.016
[8] Y. Zhang, S.Q. Liu, Y.J. Ji, J.M. Ma, H.J. Yu, Emerging nonaqueous aluminum-ion batteries: challenges, status, and perspectives. Adv. Mater. 30, 1706310 (2018). https://doi.org/10.1002/adma.201706310
[9] X. Ji, J. Chen, F. Wang, W. Sun, Y.J. Ruan, L. Miao, J.J. Jiang, C.S. Wang, Water-activated VOPO4 for magnesium ion batteries. Nano Lett. 18, 6441-6448 (2018). https://doi.org/10.1021/acs.nanolett.8b02854 
[10] B.F. Ji, F. Zhang, X.H. Song, Y.B. Tang, A novel potassium-ion-based dual-ion battery. Adv. Mater. 29, 1700519 (2017). https://doi.org/10.1002/adma.201700519 
[11] B.F. Ji, F. Zhang, N.Z. Wu, Y.B. Tang, A dual-carbon battery based on potassium-ion electrolyte. Adv. Energy Mater. 7, 1700920 (2017). https://doi.org/10.1002/aenm.201700920
[12] W.C. Zhang, Z.B. Wu, J. Zhang, G.P. Liu, N.H. Yang et al., Unraveling the effect of salt chemistry on long-durability high-phosphorus-concentration anode for potassium ion batteries. Nano Energy 53, 967-974 (2018). https://doi.org/10.1016/j.nanoen.2018.09.058
[13] P. Li, X.B. Zheng, H.X. Yu, G.Q. Zhao, J. Shu, X. Xu, W.P. Sun, S.X. Dou, Electrochemical potassium/lithium-ion intercalation into TiSe2: Kinetics and mechanism. Energy Storage Mater. 16, 512-518 (2019). https://doi.org/10.1016/j.ensm.2018.09.014
[14] J.C. Pramudita, D. Sehrawat, D. Goonetilleke, N. Sharma, An initial review of the status of electrode materials for potassium-ion batteries. Adv. Energy Mater. 7, 1602911 (2017). https://doi.org/10.1002/aenm.201602911
[15] Y.H. Zhu, X. Yang, T. Sun, S. Wang, Y.L. Zhao, J.M. Yan, X.B. Zhang, Recent progresses and prospects of cathode materials for non‑aqueous potassium‑ion batteries. Electrochem. Energy Rev. 1, 548-566 (2018). https://doi.org/10.1007/s41918-018-0019-7
[16] Y. Xu, C.L. Zhang, M. Zhou, Q. Fu, C.X. Zhao, M.H. Wu, Y. Lei, Highly nitrogen doped carbon nanofibers with superior rate capability and cyclability for potassium ion batteries. Nat. Commun. 9, 1720 (2018). https://doi.org/10.1038/s41467-018-04190-z
[17] J.L. Yang, Z.C. Ju, Y. Jiang, Z. Xing, B.J. Xi, J.K. Feng, S.L. Xiong, Enhanced capacity and rate capability of nitrogen/oxygen dual-doped hard carbon in capacitive potassium-ion storage. Adv. Mater. 30, 1700104 (2018). https://doi.org/10.1002/adma.201700104
[18] B. Cao, Q. Zhang, H. Liu, B. Xu, S.L. Zhang et al., Graphitic carbon nanocage as a stable and high power anode for potassium-ion batteries. Adv. Energy Mater. 8, 1801149 (2018). https://doi.org/10.1002/aenm.201801149
[19] W. Luo, J.Y. Wan, B. Ozdemir, W.Z. Bao, Y.N. Chen et al., Potassium ion batteries with graphitic materials. Nano Lett. 15, 7671-7677 (2015). https://doi.org/10.1021/acs.nanolett.5b03667
[20] Z. Chen, D.G. Yin, M. Zhang, Sandwich-like MoS2@SnO2@C with high capacity and stability for sodium/potassium ion batteries. Small 14, 1703818 (2018). https://doi.org/10.1002/smll.201703818
[21] V. Lakshmi, Y. Chen, A.A. Mikhaylov, A.G. Medvedev et al., Nanocrystalline SnS2 coated onto reduced graphene oxide: demonstrating the feasibility of a non-graphitic anode with sulfide chemistry for potassium-ion batteries. Chem. Commun. 53, 8272-8275 (2017). https://doi.org/10.1039/c7cc03998k
[22] H. Gao, T.F. Zhou, Y. Zheng, Q. Zhang, Y.Q. Liu et al., CoS quantum dot nanoclusters for high-energy potassium-ion batteries. Adv. Funct. Mater. 27, 1702634 (2017). https://doi.org/10.1002/adfm.201702634
[23] Y.F. Dong, Z.S. Wu, S.H. Zheng, X.H. Wang, J.Q. Qin et al., Ti3C2 MXene-derived sodium/potassium titanate nanoribbons for high-performance sodium/potassium ion batteries with enhanced capacities. ACS Nano 11, 4792-4800 (2017). https://doi.org/10.1021/acsnano.7b01165
[24] W. Wang, B. Jiang, C. Qian, F. Lv, J.R. Feng et al., Pistachio-shuck-like MoSe2/C core/shell nanostructures for high-performance potassium-ion storage. Adv. Mater. 30, 1801812 (2018). https://doi.org/10.1002/adma.201801812
[25] C. Yang, J.R. Feng, F. Lv, J.H. Zhou, C.F. Lin et al., Metallic graphene-like VSe2 ultrathin nanosheets: superior potassium-ion storage and their working mechanism. Adv. Mater. 30, 1800036 (2018). https://doi.org/10.1002/adma.201800036
[26] X.F. Wang, D.Z. Kong, Z.X. Huang, Y. Wang, H.Y. Yang, Nontopotactic reaction in highly reversible sodium storage of ultrathin Co9Se8/rGO hybrid nanosheets. Small 13, 1603980 (2017). https://doi.org/10.1002/smll.201603980
[27] K.N. Zhao, L. Zhang, R. Xia, Y.F. Dong, W.W. Xu et al., SnO2 quantum dots@graphene oxide as a high-rate and long-life anode material for lithium-ion batteries. Small 12, 588 (2016). https://doi.org/10.1002/smll.201502183
[28] Y. Xiao, P. Cao, M. Sun, Core-shell bimetallic carbide nanoparticles confined in a three-dimensional N-doped carbon conductive network for efficient lithium storage. ACS Nano 8, 7846-7857 (2014). https://doi.org/10.1021/nn501390j
[29] J. Tang, R.R. Salunkhe, J. Liu, N.L. Torad, M. Imura, S.H. Furukawa, Y. Yamauchi, Thermal conversion of core-shell metal-organic frameworks: a new method for selectively functionalized nanoporous hybrid carbon. J. Am. Chem. Soc. 137, 1572 -1580 (2015). https://doi.org/10.1021/ja511539a
[30] P. Zhang, B.Y. Guan, L. Yu, X.W. Lou, A long-range acting dehydratase domain as the missing link for C17-dehydration in iso-migrastatin biosynthesis. Angew. Chem. Int. Ed. 129, 7247-7251 (2017). https://doi.org/10.1002/anie.201703588
[31] Y.H. Zhu, J. Ciston, B. Zheng, X.H. Miao, C. Czarnik et al., Unravelling surface and interfacial structures of a metal–organic framework by transmission electron microscopy. Nat. Mater. 16, 532-536 (2017). https://doi.org/10.1038/nmat4852
[32] H. Hu, J.T. Zhang, B.Y. Guan, X.W. Lou, Unusual formation of CoSe@carbon nanoboxes, which have an inhomogeneous shell, for efficient lithium storage. Angew. Chem. Int. Ed. 55, 9514-9518 (2016). https://doi.org/10.1002/ange.201603852
[33] J. Shao, Z.M. Wan, H.M. Liu, H.Y. Zheng, T. Gao et al., Metal organic frameworks-derived Co3O4 hollow dodecahedrons with controllable interiors as outstanding anodes for Li storage. J. Mater. Chem. A 2, 12194-12200 (2014). https://doi.org/10.1039/C4TA01966K
[34] J.P. Perdew, K. Burke, M. Ernzerhof, Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865 (1996). https://doi.org/10.1103/PhysRevLett.77.3865
[35] J. Kürti, G. Kresse, H. Kuzmany, First-principles calculations of the radial breathing mode of single-wall carbon nanotubes. Phys. Rev. B 58, R8869 (1998). https://doi.org/10.1103/PhysRevB.58.R8869
[36] G. Kresse, J. Hafner, Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558 (1993). https://doi.org/10.1103/PhysRevB.47.558
[37] G. Kresse, J. Hafner, Ab initio molecular-dynamics simulation of the liquid-metal-amorphous-semiconductor transition in germanium. Phys. Rev. B 49, 14251 (1994). https://doi.org/10.1103/PhysRevB.49.14251
[38] G. Kresse, J. Furthmüller, Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169 (1996). https://doi.org/10.1103/physrevb.54.11169
[39] H.J. Monkhorst, J.D. Pack, Special points for Brillouin-zone integrations. Phys. Rev. B 13, 5188 (1976). https://doi.org/10.1103/PhysRevB.16.1746
[40] A. Banerjee, S. Bhatnagar, K.K. Upadhyay, P. Yadav, S. Ogale, Hollow Co0.85Se nanowire array on carbon fiber paper for high rate pseudocapacitor. ACS Appl. Mater. Interfaces 6, 18844-18852 (2014). https://doi.org/10.1021/am504333z
[41] D.S. Kong, H.T. Wang, J.J. Cha, M. Pasta, K.J. Koski, J. Yao, Y. Cui, Synthesis of MoS2 and MoSe2 films with vertically aligned layers. Nano Lett. 13, 1341-1347 (2013). https://doi.org/10.1021/nl400258t
[42] L. Yu, B.Y. Xia, X. Wang, X.W. Lou, General formation of M-MoS3 (M=Co, Ni) hollow structures with enhanced electrocatalytic activity for hydrogen evolution. Adv. Mater. 28, 92-97 (2016). https://doi.org/10.1002/adma.201504024
[43] Y. Hou, M. Qiu, T. Zhang, X.D. Zhuang, C.S. Kim, C. Yuan, X.L. Feng, Ternary porous cobalt phosphoselenide nanosheets: an efficient electrocatalyst for electrocatalytic and photoelectrochemical water splitting. Adv. Mater. 29, 1701589 (2017). https://doi.org/10.1002/adma.201701589
[44] Y.J. Xiong, J.M. McLellan, J.Y. Chen, Y.D. Yin, Z.Y. Li, Y.N. Xia, Kinetically controlled synthesis of triangular and hexagonal nanoplates of palladium and their SPR/SERS properties. J. Am. Chem. Soc. 127, 17118-17127 (2005). https://doi.org/10.1021/ja056498s
[45] J.F. Zhao, J.M. Song, C.C. Liu, B.H. Liu, H.L. Niu et al., Graphene-like cobalt selenide nanostructures: template-free solvothermal synthesis, characterization and wastewater treatment. CrystEngComm 13, 5681-5684 (2011). https://doi.org/10.1039/C1CE05323J
[46] Z.L. Chen, R.B. Wu, M. Liu, H. Wang, H.B. Xu et al., General synthesis of dual carbon-confined metal sulfides quantum dots toward high-performance anodes for sodium-ion batteries. Adv. Funct. Mater. 27, 1702046 (2017). https://doi.org/10.1002/adfm.201702046
[47] J. Liu, C. Wu, D.D. Xiao, P. Kopold, L. Gu, P.A. van Aken, J. Maier, Y. Yu, MOF-derived hollow Co9S8 nanoparticles embedded in graphitic carbon nanocages with superior Li-ion storage. Small 12, 2354-2364 (2016). https://doi.org/10.1002/smll.201503821
[48] S.K. Park, J.K. Kim, Y.C. Kang, Excellent sodium-ion storage performances of CoSe2 nanoparticles embedded within N-doped porous graphitic carbon nanocube/carbon nanotube composite. Chem. Eng. J. 328, 546-555 (2017). https://doi.org/10.1016/j.cej.2017.07.079
[49] Q. Liu, J.L. Shi, J.M. Hu, A.M. Asiri, Y.L. Luo, X.P. Sun, CoSe2 nanowires array as a 3D electrode for highly efficient electrochemical hydrogen evolution. ACS Appl. Mater. Interfaces 7, 3877-3881 (2015). https://doi.org/10.1021/am509185x
[50] Q.Y. Yu, B. Jiang, J. Hu, C.Y. Lao, Y.Z. Gao et al., Metallic octahedral CoSe2 threaded by N-doped carbon nanotubes: a flexible framework for high-performance potassium-ion batteries. Adv. Sci. 5, 1800782 (2018). https://doi.org/10.1002/advs.201800782
[51] D.S. Kong, H.T. Wang, Z.Y. Lu, Y. Cui, CoSe2 nanoparticles grown on carbon fiber paper: an efficient and stable electrocatalyst for hydrogen evolution reaction. J. Am. Chem. Soc. 136, 4897-4900 (2014). https://doi.org/10.1021/ja501497n
[52] W. Wang, J.H. Zhou, Z.P. Wang, L.Y. Zhao, P.H. Li et al., Short-range order in mesoporous carbon boosts potassium-ion battery performance. Adv. Energy Mater. 8, 1701648 (2018). https://doi.org/10.1002/aenm.201701648
[53] Y.C. Tang, Z.B. Zhao, X.J. Hao, Y.W. Wang, Y. Liu et al., Engineering hollow polyhedrons structured from carbon-coated CoSe2 nanospheres bridged by CNTs with boosted sodium storage performance. J. Mater. Chem. A 5, 13591-13600 (2017). https://doi.org/10.1039/C7TA02665J
[54] B.R. Jia, M.L. Qin, S.M. Li, Z.L. Zhang, H.F. Lu et al., Synthesis of mesoporous single crystal Co(OH)2 nanoplate and its topotactic conversion to dual-pore mesoporous single crystal Co3O4. ACS Appl. Mater. Interfaces 8, 15582-15590 (2016). https://doi.org/10.1021/acsami.6b02768
[55] N. Xiao, W.D. Mcculloch, Y. Wu, Reversible dendrite-free potassium plating and stripping electrochemistry for potassium secondary batteries. J. Am. Chem. Soc. 139, 9475-9478 (2017). https://doi.org/10.1021/jacs.7b04945
[56] L. Fan, S. Chen, R. Ma, J. Wang, L. Wang et al., Ultrastable potassium storage performance realized by highly effective solid electrolyte interphase layer. Small 14, 1801806 (2018). https://doi.org/10.1002/smll.201801806 
[57] Y. Huang, M. Xie, Z. Wang, Y. Jiang, G. Xiao et al., Fast sodium storage kinetics of lantern-like Ti0.25Sn0.75S2 connected via carbon nanotubes. Energy Storage Mater. 11, 100-111 (2018). https://doi.org/10.1016/j.ensm.2017.10.004
[58] K. Zhang, M.H. Park, L.M. Zhou, G.H. Lee, W.J. Li, Y.M. Kang, J. Chen, Urchin-like CoSe2 as a high-performance anode material for sodium-ion batteries. Adv. Funct. Mater. 26, 6728-6735 (2016). https://doi.org/10.1002/adfm.201602608
[59] J.B. Cook, H.S. Kim, Y. Yan, J.S. Ko, S. Robbennolt, B. Dunn, S.H. Tolbert, Mesoporous MoS2 as a transition metal dichalcogenide exhibiting pseudocapacitive Li and Na-ion charge storage. Adv. Energy Mater. 6, 1501937 (2016). https://doi.org/10.1002/aenm.201501937
[60] Na. Li, F. Zhang, Y.B. Tang, Hierarchical T-Nb2O5 nanostructure with hybrid mechanisms of intercalation and pseudocapacitance for potassium storage and high-performance potassium dual-ion batteries. J. Mater. Chem. A 6, 17889-17895 (2018). https://xs.scihub.ltd/10.1039/C8TA07

References

[1] N. Liu, Z.D. Lu, J. Zhao, M.T. McDowell, H.W. Lee, W.T. Zhao, Y. Cui, A pomegranate-inspired nanoscale design for large-volume-change lithium battery anodes. Nat. Nanotechnol. 9, 187 (2014). https://doi.org/10.1038/nnano.2014.6
[2] S.H. Choi, T.W. Kwon, A. Coskun, J.W. Choi, Highly elastic binders integrating polyrotaxanes for silicon microparticle anodes in lithium ion batteries. Science 357, 279-283 (2017). https://doi.org/10.1126/science.aal4373
[3] M. Freire, N.V. Kosova, C. Jordy, D. Chateigner, O.I. Lebedev, A. Maignan, V. Pralong, An active Li-Mn-O compound for high energy density Li-ion batteries. Nat. Mater. 15, 173 (2016). https://doi.org/10.1038/nmat4479
[4] X.D. Xiang, K. Zhang, J. Chen, Recent advances and prospects of cathode materials for sodium-ion batteries. ChemInform 46, 5343-5364 (2015). https://doi.org/10.1002/chin.201544273
[5] Z.W. Liu, P. Li, G.Q. Suo, S. Gong, W. Wang et al., Zero-strain K0.6Mn1F2.7 hollow nanocubes for ultrastable potassium ion storage. Energy Environ. Sci. 11, 3033-3042 (2018). https://doi.org/10.1039/C8EE01611A
[6] L. Fan, R.F. Ma, J. Wang, H.G. Yang, B.A. Lu, An ultrafast and highly stable potassium-organic battery. Adv. Mater. 30, 1805486 (2018). https://doi.org/10.1002/adma.201805486
[7] K. Han, Z.W. Liu, P. Li, Q.Y. Yu, W.A. Wang et al., High throughput fabrication of 3D N-doped graphenic framework coupled with Fe3C@porous graphite carbon for ultrastable potassium ion storage. Energy Storage Mater. 22, 185-193 (2019). https://doi.org/10.1016/j.ensm.2019.01.016
[8] Y. Zhang, S.Q. Liu, Y.J. Ji, J.M. Ma, H.J. Yu, Emerging nonaqueous aluminum-ion batteries: challenges, status, and perspectives. Adv. Mater. 30, 1706310 (2018). https://doi.org/10.1002/adma.201706310
[9] X. Ji, J. Chen, F. Wang, W. Sun, Y.J. Ruan, L. Miao, J.J. Jiang, C.S. Wang, Water-activated VOPO4 for magnesium ion batteries. Nano Lett. 18, 6441-6448 (2018). https://doi.org/10.1021/acs.nanolett.8b02854
[10] B.F. Ji, F. Zhang, X.H. Song, Y.B. Tang, A novel potassium-ion-based dual-ion battery. Adv. Mater. 29, 1700519 (2017). https://doi.org/10.1002/adma.201700519
[11] B.F. Ji, F. Zhang, N.Z. Wu, Y.B. Tang, A dual-carbon battery based on potassium-ion electrolyte. Adv. Energy Mater. 7, 1700920 (2017). https://doi.org/10.1002/aenm.201700920
[12] W.C. Zhang, Z.B. Wu, J. Zhang, G.P. Liu, N.H. Yang et al., Unraveling the effect of salt chemistry on long-durability high-phosphorus-concentration anode for potassium ion batteries. Nano Energy 53, 967-974 (2018). https://doi.org/10.1016/j.nanoen.2018.09.058
[13] P. Li, X.B. Zheng, H.X. Yu, G.Q. Zhao, J. Shu, X. Xu, W.P. Sun, S.X. Dou, Electrochemical potassium/lithium-ion intercalation into TiSe2: Kinetics and mechanism. Energy Storage Mater. 16, 512-518 (2019). https://doi.org/10.1016/j.ensm.2018.09.014
[14] J.C. Pramudita, D. Sehrawat, D. Goonetilleke, N. Sharma, An initial review of the status of electrode materials for potassium-ion batteries. Adv. Energy Mater. 7, 1602911 (2017). https://doi.org/10.1002/aenm.201602911
[15] Y.H. Zhu, X. Yang, T. Sun, S. Wang, Y.L. Zhao, J.M. Yan, X.B. Zhang, Recent progresses and prospects of cathode materials for non‑aqueous potassium‑ion batteries. Electrochem. Energy Rev. 1, 548-566 (2018). https://doi.org/10.1007/s41918-018-0019-7
[16] Y. Xu, C.L. Zhang, M. Zhou, Q. Fu, C.X. Zhao, M.H. Wu, Y. Lei, Highly nitrogen doped carbon nanofibers with superior rate capability and cyclability for potassium ion batteries. Nat. Commun. 9, 1720 (2018). https://doi.org/10.1038/s41467-018-04190-z
[17] J.L. Yang, Z.C. Ju, Y. Jiang, Z. Xing, B.J. Xi, J.K. Feng, S.L. Xiong, Enhanced capacity and rate capability of nitrogen/oxygen dual-doped hard carbon in capacitive potassium-ion storage. Adv. Mater. 30, 1700104 (2018). https://doi.org/10.1002/adma.201700104
[18] B. Cao, Q. Zhang, H. Liu, B. Xu, S.L. Zhang et al., Graphitic carbon nanocage as a stable and high power anode for potassium-ion batteries. Adv. Energy Mater. 8, 1801149 (2018). https://doi.org/10.1002/aenm.201801149
[19] W. Luo, J.Y. Wan, B. Ozdemir, W.Z. Bao, Y.N. Chen et al., Potassium ion batteries with graphitic materials. Nano Lett. 15, 7671-7677 (2015). https://doi.org/10.1021/acs.nanolett.5b03667
[20] Z. Chen, D.G. Yin, M. Zhang, Sandwich-like MoS2@SnO2@C with high capacity and stability for sodium/potassium ion batteries. Small 14, 1703818 (2018). https://doi.org/10.1002/smll.201703818
[21] V. Lakshmi, Y. Chen, A.A. Mikhaylov, A.G. Medvedev et al., Nanocrystalline SnS2 coated onto reduced graphene oxide: demonstrating the feasibility of a non-graphitic anode with sulfide chemistry for potassium-ion batteries. Chem. Commun. 53, 8272-8275 (2017). https://doi.org/10.1039/c7cc03998k
[22] H. Gao, T.F. Zhou, Y. Zheng, Q. Zhang, Y.Q. Liu et al., CoS quantum dot nanoclusters for high-energy potassium-ion batteries. Adv. Funct. Mater. 27, 1702634 (2017). https://doi.org/10.1002/adfm.201702634
[23] Y.F. Dong, Z.S. Wu, S.H. Zheng, X.H. Wang, J.Q. Qin et al., Ti3C2 MXene-derived sodium/potassium titanate nanoribbons for high-performance sodium/potassium ion batteries with enhanced capacities. ACS Nano 11, 4792-4800 (2017). https://doi.org/10.1021/acsnano.7b01165
[24] W. Wang, B. Jiang, C. Qian, F. Lv, J.R. Feng et al., Pistachio-shuck-like MoSe2/C core/shell nanostructures for high-performance potassium-ion storage. Adv. Mater. 30, 1801812 (2018). https://doi.org/10.1002/adma.201801812
[25] C. Yang, J.R. Feng, F. Lv, J.H. Zhou, C.F. Lin et al., Metallic graphene-like VSe2 ultrathin nanosheets: superior potassium-ion storage and their working mechanism. Adv. Mater. 30, 1800036 (2018). https://doi.org/10.1002/adma.201800036
[26] X.F. Wang, D.Z. Kong, Z.X. Huang, Y. Wang, H.Y. Yang, Nontopotactic reaction in highly reversible sodium storage of ultrathin Co9Se8/rGO hybrid nanosheets. Small 13, 1603980 (2017). https://doi.org/10.1002/smll.201603980
[27] K.N. Zhao, L. Zhang, R. Xia, Y.F. Dong, W.W. Xu et al., SnO2 quantum dots@graphene oxide as a high-rate and long-life anode material for lithium-ion batteries. Small 12, 588 (2016). https://doi.org/10.1002/smll.201502183
[28] Y. Xiao, P. Cao, M. Sun, Core-shell bimetallic carbide nanoparticles confined in a three-dimensional N-doped carbon conductive network for efficient lithium storage. ACS Nano 8, 7846-7857 (2014). https://doi.org/10.1021/nn501390j
[29] J. Tang, R.R. Salunkhe, J. Liu, N.L. Torad, M. Imura, S.H. Furukawa, Y. Yamauchi, Thermal conversion of core-shell metal-organic frameworks: a new method for selectively functionalized nanoporous hybrid carbon. J. Am. Chem. Soc. 137, 1572 -1580 (2015). https://doi.org/10.1021/ja511539a
[30] P. Zhang, B.Y. Guan, L. Yu, X.W. Lou, A long-range acting dehydratase domain as the missing link for C17-dehydration in iso-migrastatin biosynthesis. Angew. Chem. Int. Ed. 129, 7247-7251 (2017). https://doi.org/10.1002/anie.201703588
[31] Y.H. Zhu, J. Ciston, B. Zheng, X.H. Miao, C. Czarnik et al., Unravelling surface and interfacial structures of a metal–organic framework by transmission electron microscopy. Nat. Mater. 16, 532-536 (2017). https://doi.org/10.1038/nmat4852
[32] H. Hu, J.T. Zhang, B.Y. Guan, X.W. Lou, Unusual formation of CoSe@carbon nanoboxes, which have an inhomogeneous shell, for efficient lithium storage. Angew. Chem. Int. Ed. 55, 9514-9518 (2016). https://doi.org/10.1002/ange.201603852
[33] J. Shao, Z.M. Wan, H.M. Liu, H.Y. Zheng, T. Gao et al., Metal organic frameworks-derived Co3O4 hollow dodecahedrons with controllable interiors as outstanding anodes for Li storage. J. Mater. Chem. A 2, 12194-12200 (2014). https://doi.org/10.1039/C4TA01966K
[34] J.P. Perdew, K. Burke, M. Ernzerhof, Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865 (1996). https://doi.org/10.1103/PhysRevLett.77.3865
[35] J. Kürti, G. Kresse, H. Kuzmany, First-principles calculations of the radial breathing mode of single-wall carbon nanotubes. Phys. Rev. B 58, R8869 (1998). https://doi.org/10.1103/PhysRevB.58.R8869
[36] G. Kresse, J. Hafner, Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558 (1993). https://doi.org/10.1103/PhysRevB.47.558
[37] G. Kresse, J. Hafner, Ab initio molecular-dynamics simulation of the liquid-metal-amorphous-semiconductor transition in germanium. Phys. Rev. B 49, 14251 (1994). https://doi.org/10.1103/PhysRevB.49.14251
[38] G. Kresse, J. Furthmüller, Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169 (1996). https://doi.org/10.1103/physrevb.54.11169
[39] H.J. Monkhorst, J.D. Pack, Special points for Brillouin-zone integrations. Phys. Rev. B 13, 5188 (1976). https://doi.org/10.1103/PhysRevB.16.1746
[40] A. Banerjee, S. Bhatnagar, K.K. Upadhyay, P. Yadav, S. Ogale, Hollow Co0.85Se nanowire array on carbon fiber paper for high rate pseudocapacitor. ACS Appl. Mater. Interfaces 6, 18844-18852 (2014). https://doi.org/10.1021/am504333z
[41] D.S. Kong, H.T. Wang, J.J. Cha, M. Pasta, K.J. Koski, J. Yao, Y. Cui, Synthesis of MoS2 and MoSe2 films with vertically aligned layers. Nano Lett. 13, 1341-1347 (2013). https://doi.org/10.1021/nl400258t
[42] L. Yu, B.Y. Xia, X. Wang, X.W. Lou, General formation of M-MoS3 (M=Co, Ni) hollow structures with enhanced electrocatalytic activity for hydrogen evolution. Adv. Mater. 28, 92-97 (2016). https://doi.org/10.1002/adma.201504024
[43] Y. Hou, M. Qiu, T. Zhang, X.D. Zhuang, C.S. Kim, C. Yuan, X.L. Feng, Ternary porous cobalt phosphoselenide nanosheets: an efficient electrocatalyst for electrocatalytic and photoelectrochemical water splitting. Adv. Mater. 29, 1701589 (2017). https://doi.org/10.1002/adma.201701589
[44] Y.J. Xiong, J.M. McLellan, J.Y. Chen, Y.D. Yin, Z.Y. Li, Y.N. Xia, Kinetically controlled synthesis of triangular and hexagonal nanoplates of palladium and their SPR/SERS properties. J. Am. Chem. Soc. 127, 17118-17127 (2005). https://doi.org/10.1021/ja056498s
[45] J.F. Zhao, J.M. Song, C.C. Liu, B.H. Liu, H.L. Niu et al., Graphene-like cobalt selenide nanostructures: template-free solvothermal synthesis, characterization and wastewater treatment. CrystEngComm 13, 5681-5684 (2011). https://doi.org/10.1039/C1CE05323J
[46] Z.L. Chen, R.B. Wu, M. Liu, H. Wang, H.B. Xu et al., General synthesis of dual carbon-confined metal sulfides quantum dots toward high-performance anodes for sodium-ion batteries. Adv. Funct. Mater. 27, 1702046 (2017). https://doi.org/10.1002/adfm.201702046
[47] J. Liu, C. Wu, D.D. Xiao, P. Kopold, L. Gu, P.A. van Aken, J. Maier, Y. Yu, MOF-derived hollow Co9S8 nanoparticles embedded in graphitic carbon nanocages with superior Li-ion storage. Small 12, 2354-2364 (2016). https://doi.org/10.1002/smll.201503821
[48] S.K. Park, J.K. Kim, Y.C. Kang, Excellent sodium-ion storage performances of CoSe2 nanoparticles embedded within N-doped porous graphitic carbon nanocube/carbon nanotube composite. Chem. Eng. J. 328, 546-555 (2017). https://doi.org/10.1016/j.cej.2017.07.079
[49] Q. Liu, J.L. Shi, J.M. Hu, A.M. Asiri, Y.L. Luo, X.P. Sun, CoSe2 nanowires array as a 3D electrode for highly efficient electrochemical hydrogen evolution. ACS Appl. Mater. Interfaces 7, 3877-3881 (2015). https://doi.org/10.1021/am509185x
[50] Q.Y. Yu, B. Jiang, J. Hu, C.Y. Lao, Y.Z. Gao et al., Metallic octahedral CoSe2 threaded by N-doped carbon nanotubes: a flexible framework for high-performance potassium-ion batteries. Adv. Sci. 5, 1800782 (2018). https://doi.org/10.1002/advs.201800782
[51] D.S. Kong, H.T. Wang, Z.Y. Lu, Y. Cui, CoSe2 nanoparticles grown on carbon fiber paper: an efficient and stable electrocatalyst for hydrogen evolution reaction. J. Am. Chem. Soc. 136, 4897-4900 (2014). https://doi.org/10.1021/ja501497n
[52] W. Wang, J.H. Zhou, Z.P. Wang, L.Y. Zhao, P.H. Li et al., Short-range order in mesoporous carbon boosts potassium-ion battery performance. Adv. Energy Mater. 8, 1701648 (2018). https://doi.org/10.1002/aenm.201701648
[53] Y.C. Tang, Z.B. Zhao, X.J. Hao, Y.W. Wang, Y. Liu et al., Engineering hollow polyhedrons structured from carbon-coated CoSe2 nanospheres bridged by CNTs with boosted sodium storage performance. J. Mater. Chem. A 5, 13591-13600 (2017). https://doi.org/10.1039/C7TA02665J
[54] B.R. Jia, M.L. Qin, S.M. Li, Z.L. Zhang, H.F. Lu et al., Synthesis of mesoporous single crystal Co(OH)2 nanoplate and its topotactic conversion to dual-pore mesoporous single crystal Co3O4. ACS Appl. Mater. Interfaces 8, 15582-15590 (2016). https://doi.org/10.1021/acsami.6b02768
[55] N. Xiao, W.D. Mcculloch, Y. Wu, Reversible dendrite-free potassium plating and stripping electrochemistry for potassium secondary batteries. J. Am. Chem. Soc. 139, 9475-9478 (2017). https://doi.org/10.1021/jacs.7b04945
[56] L. Fan, S. Chen, R. Ma, J. Wang, L. Wang et al., Ultrastable potassium storage performance realized by highly effective solid electrolyte interphase layer. Small 14, 1801806 (2018). https://doi.org/10.1002/smll.201801806
[57] Y. Huang, M. Xie, Z. Wang, Y. Jiang, G. Xiao et al., Fast sodium storage kinetics of lantern-like Ti0.25Sn0.75S2 connected via carbon nanotubes. Energy Storage Mater. 11, 100-111 (2018). https://doi.org/10.1016/j.ensm.2017.10.004
[58] K. Zhang, M.H. Park, L.M. Zhou, G.H. Lee, W.J. Li, Y.M. Kang, J. Chen, Urchin-like CoSe2 as a high-performance anode material for sodium-ion batteries. Adv. Funct. Mater. 26, 6728-6735 (2016). https://doi.org/10.1002/adfm.201602608
[59] J.B. Cook, H.S. Kim, Y. Yan, J.S. Ko, S. Robbennolt, B. Dunn, S.H. Tolbert, Mesoporous MoS2 as a transition metal dichalcogenide exhibiting pseudocapacitive Li and Na-ion charge storage. Adv. Energy Mater. 6, 1501937 (2016). https://doi.org/10.1002/aenm.201501937
[60] Na. Li, F. Zhang, Y.B. Tang, Hierarchical T-Nb2O5 nanostructure with hybrid mechanisms of intercalation and pseudocapacitance for potassium storage and high-performance potassium dual-ion batteries. J. Mater. Chem. A 6, 17889-17895 (2018). https://xs.scihub.ltd/10.1039/C8TA07

Citation Information

Zhiwei Liu, Kun Han, Ping Li, Wei (Alex) Wang, Donglin He, Qiwei Tan, Leying Wang, Yang Li, Mingli Qin, Xuanhui Qu, Tuning Metallic Co0.85Se Quantum Dots/Carbon Hollow Polyhedrons with Tertiary Hierarchical Structure for High-Performance Potassium Ion Batteries. Nano-Micro Lett.(2019) 11: 96. https://doi.org/doi.org/10.1007/s40820-019-0326-5

History

Received: 29 July 2019 / Accepted: 12 October 2019 / Published online: 01 November 2019


Additional Info

  • Type of Publishing: JOUR - Journal
  • Title: Tuning Metallic Co0.85Se Quantum Dots/Carbon Hollow Polyhedrons with Tertiary Hierarchical Structure for High-Performance Potassium Ion Batteries
  • Author: Zhiwei Liu, Kun Han, Ping Li, Wei (Alex) Wang, Donglin He, Qiwei Tan, Leying Wang, Yang Li, Mingli Qin, Xuanhui Qu
  • Year: 2019
  • Volume: 11
  • Journal Name: Nano-Micro Letters
  • ISSN: 2150-5551
  • URL: http://dx.doi.org/10.1007/s40820-019-0326-5
  • Abstract: Potassium-ion batteries (KIBs) are a potential candidate to lithium-ion batteries (LIBs) but possess unsatisfactory capacity and rate properties. Herein, the metallic cobalt selenide quantum dots (Co0.85Se-QDs) encapsulated in mesoporous carbon matrix were designed via a direct hydrothermal method. Specifically, the cobalt selenide/carbon composite (Co0.85Se-QDs/C) possesses tertiary hierarchical structure, which is the primary quantum dots, the secondary petals flake, and the tertiary hollow micro polyhedron framework. Co0.85Se-QDs are homogenously embedded into the carbon petals flake, which constitute the hollow polyhedral framework. This unique structure can take the advantages of both nanoscale and microscale features: Co0.85Se-QDs can expand in a multidimensional and ductile carbon matrix and reduce the K-intercalation stress in particle dimensions; the micro petals can restrain the agglomeration of active materials and promote the transportation of potassium ion and electron. In addition, the hollow carbon framework buffers volume expansion, maintains the structural integrity, and increases the electronic conductivity. Benefiting from this tertiary hierarchical structure, outstanding K-storage performance (402 mAh g-1 after 100 cycles at 50 mA g-1) is obtained when Co0.85Se-QDs/C used as KIBs anode. More importantly, the selenization process in this work is newly reported and can be generally extended to prepare other quantum dots encapsulated in edge-limited frameworks for excellent energy storage.
  • Publish Date: Friday, 01 November 2019
  • Start Page: 96
  • DOI: 10.1007/s40820-019-0326-5