Nano-Micro Letters

A Simple Method of Electrospun Tungsten Trioxide Nanofibers with Enhanced Visible-light Photocatalytic Activity

Frank Agyemang Ofori1, Faheem A Sheikh1,*, Richard Appiah-Ntiamoah1, Xinsheng Yang2, Hern Kim1,*

Abstract
icon-htmlFull Text Html
icon-pdf-smPDF w/ Links
icon-citExport Citation
Figures
+Show more

Nano-Micro Letters, , Volume 7, Issue 3, pp 291-297

First online: 04 Jun 2015 (Article)

DOI: 10.1007/s40820-015-0042-8

*Corresponding author.

E-mail: faheem99in@yahoo.com (Faheem A Sheikh); hernkim@mju.ac.kr (Hern Kim). Tel: +82 31 330 6688, Fax: +82 31 336 6336.

 

Abstract

 


TGA curves of nanofibers at 500 C, pure citric acid and PVP.
The present study involves the fabrication of tungsten trioxide (WO3) nanofibers by an electrospinning technique using polyvinyl pyrrolidone (PVP)/citric acid/tungstic acid as precursor solution. It was found that the PVP concentration was one of the most crucial processing parameters determining the final properties of WO3 nanofibers. The optimum concentration of PVP was from 75 to 94 g L-1. The average diameter of the nanofibers increases with increasing the PVP concentration, whereas, it is decreased after sintering and orthorhombic structure were formed at 500 °C. The photocatalytic properties of the as-synthesized nanofibers were also investigated by degrading methylene blue and two-fold efficiency was obtained compared with that of commercial WO3 microparticles.

 

Keywords

Tungsten trioxide; Electrospinning; Nanofiber; Photocatalysis

 

Full Text Html

 

1 Introduction

 

The textile industry effluent is a major source of water pollution which can destroy the aquatic life and influence world climates change seriously [1]. The main source of water pollution comes from dyeing and finishing process of fabrics in textile industries. It is believed that 10 to 15 % of the dyes are unintentionally wasted during the dyeing processes in major developing countries [2]. An industrial dye constitutes one of the largest groups of harmful organic compounds which is difficult to degrade naturally. Mostly, the non-fixed dyes especially the azo-dyes and other inorganic salts from textile factories tend to contain considerable amount of toxins and are highly carcinogenic. Therefore, direct contact of these dyes have harmful effects on human [3-4].

Currently, different strategies have been employed for treating the textile effluents before they are released in water bodies including microfiltration [5], chemical precipitation [6], biosorption [7], membrane separation techniques [8], nanofiltration [9], electrochemical treatment [10] solvent extraction [11], and coagulation-flocculation [12]. However, the limitations of these strategies include incomplete ion removal and production of toxic sludge are unavoidable which require further disposal of the released effluents. The residual dyes can remain for a longer period of time which are non-biodegradable and have no effect due to sunlight [13]. Hence, the aforementioned methods are not fully useful as they can only transform the dyes from one phase to another, creating new kinds of pollutants which further need to be treated with other methods such as advanced oxidation processes by photocatalytic degradation using metal oxides.

Tungsten trioxide (WO3) is one of the most popular metal oxide which has been extensively used as electrochromic devices and gas sensor for water splitting [14]. Recently, it was concluded that WO3 has a broad range of band-gap values which ensures considerable photocatalytic and photoelectrocatalytic activity under visible light illumination [15]. At this point of view, WO3 based materials as well as their photocatalysis have attracted much attention, for example, nanoparticles for degradation of lidocaine under visible and sunlight irradiation [16] and porous structure for degradation of rhodamine B dye [17]. Many efforts have also been made to enhance the photocatalytic efficiency of WO3, for example, photo-deposition of platinum in WO3 nanostructures [18], titania-WO3 nanotubular composite fabricated by electrochemical method [19] and various films based on WO3 [20], etc. However, WO3 nanofibers with large aspect ratio are rarely reported before [21,22]. It is believed that increase of surface-to-volume ratio is one of the effective ways to increase the photocatalytic efficiency [23]. In this connection, various nano-structured WO3 such as nanorods [24], nanofibers [25], nanowires [26] and nanoporous films [27] have been fabricated. Among these nanomaterials, nanofibers with superior porosity, excellent mechanical properties and desirable chemical properties make them multifunctional capabilities for various applications [28].

Generally, nanofibers are produced by three techniques of self-assembly [29], phase separation [30] and electrospinning [31], in which the electrospinning is considered to be the most preferred technique due to its facility of quantity production, tunable properties via changing the solution parameters, as well as wide applications. Till now, polymer, ceramic, metal oxide and lots of composite nanofibers have been successfully prepared via electrospinning technique [31-35]. Various electrospun WO3 based nanofibers were also investigated widely, for example, WO3 nanofibers for gas-sensing [36], core-shell WO3/TiO2 nanofibers for photocatalysis [37], polycrystalline trioxide nanofibers as ammonia sensors [38], templates for detection of biomarker molecules [39] and improved photoluminescence [25]. Especially, WO3 nanofibers can be efficiently used for photocatalyst due to its unique physical and chemical properties as above references mentioned. Recently, lots of works have been done to investigate the fabrication and properties of electrospun WO3 nanofibers [25-26, 38, 40]. However, the existing methods either need expensive precursors or long time process. In this work, we developed a simple electrospun method of fabrication WO3 nanofibers by using inexpensive precursor of polyvinylpyrrolidone (PVP)/citric acid/tungstic acid. The photoctalytic efficiency of the as-synthesized nanofibers were also investigated via degrading methylene blue.

 

2 Experimental

 

2.1 Materials

 

PVP of Mw=1300000 was purchased from Sigma Aldrich in USA. Commercial WO3 powders (mean particle size 30 mm) were obtained from Kanto Chemical Company and methylene blue (99 % purity) from Showa Chemical Company in Japan. Ammonia solution was from Duskan Pure Chemical Company Ltd and citric acid monohydrate (99.5 % purity) was from Samchun Pure Chemicals in Republic of Korea.

 

2.2 Preparation of Solution for Electrospinning

 

The WO3 nanofibers were synthesized using an electrospinning method. Commercially available WO3 powders were dissolved in hot ammonia solution with stirring firstly. After the mixture was cooled down to room temperature, the insoluble materials were removed by filtration after which an amount of citric acid was added as chelating agent for binding WO3 [41]. Then, PVP (75 g L-1) were added into the above solution followed by magnetic stirring for about 1 day. The weight ratio of PVP/citric acid/ WO3 was kept constant at a ratio of (1.1:2.7:1.0). The mixed solution was aged on hot plate for different time to form different concentration of PVP/citric acid/tungstic acid precursor gel for electrospinning. In this work, three kinds of precursor solution were prepared in which the concentration of PVP was 75, 94 and 140 g L-1, respectively.

 

2.3 Electrospinning Solution

 

A high voltage power supply (CPS-60 K02V1, Chungpa EMT Co.in Republic of Korea) capable of generating voltages up to 30 kV was used as the electric field source for spinning of nanofibers. Solutions to be electrospun were supplied through a 20 mL plastic syringe attached with stainless steel having 22 gauges, (0.7 mm OD × 0.4 mm ID). The feeding rate of solution to be electrospun was adjusted to be 0.2 mL min-1 by using a syringe pump (KDS-100, KD Scientific, United States). The syringe was aligned perpendicular to flat bed collector of electrospinning apparatus. The wire originated from the positive electrode (anode) was connected with the needle tip of plastic syringe with an alligator clip. Finally, the solutions were electrospun at +18 kV. The distance between the needle tip and the flat bed metallic collector covered with aluminum foil was kept at 15 cm. The as-spun nanofibers were vacuously dried at 60 °C for 24 h in the presence of P2O5 to remove the residual moisture from used solvents. Further on, the samples were subjected to calcination at 500 °C for 2 h with a heating rate of 1 °C min-1.

 

2.4 Characterization

 

The morphology of the samples was examined using a scanning electron microscope (SEM, Hitachi, Japan S-3500N). The samples were coated with a thin layer of platinum-palladium for 50 sec with the discharge current of 10-15 mA for 3 reparative cycles using (Hitachi, Japan E1010) ion sputter. After coating, the micrographs were taken at an accelerating voltage of 25 kV and images were captured with magnifications of 1 K and 20 K. The thermal properties were tested by thermogravimetry/differential scanning calorimetry instrument (SETARAM TG/DSC 92). The samples were heated from 30 to 600 °C under a continuous nitrogen purge of 20 mL min-1 with a heating rate of 20 °C min-1. Information about the phases and crystallinity of nanofibers was obtained using X-ray diffractometer (XRD, X’pert-pro MPD) with Cu, Cr (λ = 1.540 A) radiation over Bragg angle ranging from 20° to 60°. For photocatalytic property, the samples were suspended (1 g L-1) in methylene blue solution (20 ppm) in a batch reactor and illumination was applied using a commercial haloline visible light illumination (500 W, Osram). The evolution of the methylene blue concentration was measured by UV-vis spectrometry (Cary 100, Varian) following its 660 nm characteristic band.

 

3 Results and Discussion

 

Figure 1 shows the SEM images of the as-electrospun nanofibers at different PVP concentrations. It was observed that the PVP concentration strongly influenced the ability of spinning, in terms of fiber formation and fiber diameters. For instance, at lower PVP concentration (i.e., less than 75 g L-1), electrospinning process could not be carried out due to low viscosity of precursor solutions (data not shown). However, when PVP concentration was 75 g L-1 or higher, the electrospinning was highly achievable for nanofibers. Figure 1a-c show respectively the results of 75, 94 and 140 g L-1 of PVP. From Fig. 1a, b, one can see that nanofibers are bead and defect-free without conglomeration, whereas, they are conglomeration when fabricated at 140 g L-1 (Fig. 1c). Figure 2 shows the size distribution of nanofibers calculated by randomly selecting 30 nanofibers from SEM images. The diameters are in the range of 40 to 280 nm when PVP concentration is 75 and 94 g L-1 and the average diameter of the nanofibers increased with PVP concentrations. These results are in agreement well with the conclusion made by Yan et al. [41].

SEM images of as-spun nanofibers for different PVP concentrations of 75 g L-1 (a), 94 g L-1 (b) and 140 g L-1 (c).

SEM images of as-spun nanofibers for different PVP concentrations of 75 g L-1 (a), 94 g L-1 (b) and 140 g L-1 (c).

Size distributions of as-spun nanofibers for different PVP concentrations of 75 g L-1 (a) and 94 g L-1 (b).

Size distributions of as-spun nanofibers for different PVP concentrations of 75 g L-1 (a) and 94 g L-1 (b).

The SEM images of the nanofibers calcined at 500 °C for different PVP concentration are shown in Fig. 3. It can be seen that the nanofibers obtained at PVP concentration of 75 and 94 g L-1 maintained good fibrous morphology (Fig. 3a, b), whereas, the nanofibous morphology fabricated at 140 g L-1 of PVP concentration was completely distorted and porous nest-like structure was formed. The size of nanofibers after calcinations was reduced to 80-100 nm for 75 and 94 g L-1 PVP concentrations due to the removal the polymer precursor. The diameter distribution in the range of 20 to 160 nm is shown in Fig. 4a, b, which is comparatively less than as-spun nanofibers. This may be indicated that the PVP precursor was removed from the nanofibers after calcination and pure metal oxide nanofibers were yielded.

SEM images of nanofibers calcined at 500 C for different PVP concentrations of 75 g L-1 (a), 94 g L-1 (b) and 140 g L-1 (c).

SEM images of nanofibers calcined at 500 C for different PVP concentrations of 75 g L-1 (a), 94 g L-1 (b) and 140 g L-1 (c).

Size distributions of nanofibers calcined at 500 C for different PVP concentrations of 75 g L-1 (a) and 94 g L-1 (b).

Size distributions of nanofibers calcined at 500 C for different PVP concentrations of 75 g L-1 (a) and 94 g L-1 (b).

In order to confirm the precursor was completely removed after calcination, TGA of pure PVP, citric acid and WO3 nanofibers were performed. The results of WO3 nanofibers indicate that residual weight is about 25 % at 500 °C, while it is 13 % for pure PVP and no citric acid remained (see Fig. 5). This indicates that the polymer in the as-spun nanofibers can be easily removed by sintering the sample at 500°C. The typical XRD pattern of WO3 nanofibers is presented in Fig. 6. The diffraction peaks agree well with the standard orthorhombic WO3 crystal (JCDPS, card no 05-03888).

TGA curves of nanofibers at 500 C, pure citric acid and PVP.

TGA curves of nanofibers at 500 C, pure citric acid and PVP.

XRD pattern of nanofibers fabricated at 75 g L-1 PVP concentration and calcined at 500 C.

XRD pattern of nanofibers fabricated at 75 g L-1 PVP concentration and calcined at 500 C.

Figure 7 shows the photocatalytic result of WO3 nanofibers by degrading methylene blue under visible light illumination. For comparison, the commercial powders (mean particle size of 30 m) were also investigated simultaneously. After irradiation for 2 h, the degradation efficiency for commercially available WO3 powders was only about 23 %, while the degradation efficiency for WO3 nanofibers (PVP: 140 g L-1) was 27 %, (PVP: 94 g L-1) 46 % and (PVP: 75 g L-1) 50 %, respectively. The degradation efficiency for nanofibers is much higher than that of commercially available WO3 particles whose mean diameter is 30 mm according to manufacturer. It can be observed that the degradation efficiency for nanofibers with the smaller diameter prepared from (PVP: 75 g L-1) was 50 % which is higher than other nanofibers combinations with lager diameter. Therefore, it can be concluded that electrospinning WO3 nanofibers with smaller diameters can significantly improve the photocatalytic activity than commercially available WO3 micro-powders.

Photocatalytic degradation of commercial WO3 powders (1), WO3 nanofibers fabricated from 75 g L-1 (2), 94 g L-1 (3) and 140 g L-1 PVP (4) precursor under visible light illumination.

Photocatalytic degradation of commercial WO3 powders (1), WO3 nanofibers fabricated from 75 g L-1 (2), 94 g L-1 (3) and 140 g L-1 PVP (4) precursor under visible light illumination.

 

4 Conclusion

 

WO3 nanofibers were fabricated by an electrospinning technique using PVP/citric acid/tungstic acid as precursor solutions. The average diameter of nanofibers is 80-100 nm and increases with PVP concentration. After sintering at 500°C for 2 h the diameter was reduced and the structure was transferred from amorphous to orthorhombic. The photocatalytic activity of WO3 nanofibers was found much higher than that of commercial WO3 powders in degradation of methylene blue under visible light illumination.

 

Acknowledgement

 

This study was supported by National Research Foundation of Korea (NRF) – Grants funded by the Ministry of Science, ICT and Future Planning (2014R1A2A2A01004352) and the Ministry of Education (2009-0093816), Republic of Korea.

 

References

 

 [1] A.P. Mouritz, M.K. Bannister, P.J. Falzon, K.H. Leong, Review of applications for advanced three dimensional fibre textile composites. Compos. Pt. A-Appl. Sci. Manuf. 30(12), 1445-1461 (1999). doi:10.1016/S1359-835X(99)00034-2

[2] K.S. Karn, H. Harada, Surface water pollution in three urban territories of Nepal, India, and Bangladesh. J. Environ. Manage. 28(4), 483-496 (2001). doi:10.1007/s002670010238

[3] H.R. Pouretedal, M.H. Keshavarz, Study of Congo red photodegradation kinetic catalyzed by Zn1-XCuXS and Zn1-XNiXS nanoparticles. Int. J. Phys. Sci. 6(27), 6268-6279 (2001). doi:10.5897/IJPS09.251

[4] K.I. Konstantinou, A.A. Triantafyllos, TiO2-assisted photocatalytic degradation of azo dyes in aqueous solution: kinetic and mechanistic investigations. Appl. Catal. B. Env. 49(1), 1-14 (2004). doi:10.1016/j.apcatb.2003.11.010

[5] C.A. Buckley, Membrane technology for the treatment of dyehouse effluents. Water. Sci. Technol. 25(96), 203-209 (1992). doi:10.1016/S0958-2118(00)89257-5

[6] N.M. Mahmoodi, Photocatalytic ozonation of dyes using copper ferrite nanoparticle prepared by co-precipitation method. Desalination 279(1-3), 332-337 (2011). doi:10.1016/j.desal.2011.06.027

[7] A. Reza, F.A. Sheikh, M.Z. Abedin, H. Kim, Facile strategy for utilizing sugarcane bagasse as bio-adsorbent for the removal of contaminant form effluents of textile industry. Energy Environ. Focus 4(1), 28-33 (2015). doi:10.1166/eef.2015.1135

[8] Q. Yu, Y. Mao, X. Peng, Separation membranes constructed from inorganic nanofibers by filtration technique. Chem. Rec. 13(1), 14-27 (2013). doi:10.1002/tcr.201200011

[9] M. Riera-Torres, C. Gutiérrez-Bouzán, M. Crespi, Combination of coagulation–flocculation and nanofiltration techniques for dye removal and water reuse in textile effluents. Desalination 252(1-3), 53-59 (2010). doi:10.1016/j.desal.2009.11.002

[10] A. Mittal, R. Jain, J. Mittal, S. Varshney, Removal of yellow ME 7 GL from industrial effluent using electrochemical and adsorption techniques. Int. J. Environ. Pollut. 43(4), 308-323 (2010). doi:10.1504/IJEP.2010.036929

[11] E.M. Golet, A. Strehler, A.C. Alder, W. Giger, Determination of fluoroquinolone antibacterial agents in sewage sludge and sludge-treated soil using accelerated solvent extraction followed by solid-phase extraction. Anal. Chem. 74(21), 5455-5462 (2002). doi:10.1021/ac025762m

[12] A.K. Verma, R.R. Dash, P. Bhunia, A review on chemical coagulation/flocculation technologies for removal of colour from textile wastewaters. J. Environ. Manage 93(1), 154-168 (2012). doi:10.1016/j.jenvman.2011.09.012

[13] M. Grätzel, Dye-sensitized solar cells. J. Photochem. Photobiol. C 4(2), 145-153 (2003) doi 10.1016/S1389-5567(03)00026-1

[14] C.G. Granqvist, Electrochromic tungsten oxide flms: Review of progress. Sol. Energy Mater. Sol. Cells 60(3), 201-262 (2000). doi:10.1016/S0927-0248(99)00088-4

[15] J. Georgieva, E. Valova, S. Armyanov, N. Philippidis, I. Poulios, S. Sotiropoulos, Bi-component semiconductor oxide photoanodes for the photoelectrocatalytic oxidation of organic solutes and vapours: A short review with emphasis to TiO2–WO3 photoanodes. J. Hazard. Mater. 211-212, 30-46 (2012). doi:10.1016/j.jhazmat.2011.11.069

[16] A. Fakhri, S. Behrouzc, Photocatalytic properties of tungsten trioxide (WO3) nanoparticles for degradation of Lidocaine under visible and sunlight irradiation. Sol. Energy 112,163-168 (2015). doi:10.1016/j.solener.2014.11.014

[17] X. Yan, X. Zong, G.Q.M. Lu, L. Wang, Ordered mesoporous tungsten oxide and titanium oxide composites and their photocatalytic degradation behavior. Prog. Nat. Sci. 22(6), 654-660 (2012). doi:10.1016/j.pnsc.2012.11.016

[18] Y. Wicaksana, S. Liu, J. Scott, R. Amal, Tungsten trioxide as a visible light photocatalyst for volatile organic carbon removal. Molecules 19(11), 17747-17762 (2014). doi:10.3390/molecules191117747

[19] M.M. Momeni, Y. Ghayeb, M. Davarzadeh, Electrochemical construction of different titania–tungsten trioxide nanotubular composite and their photocatalytic activity for pollutant degradation: a recyclable photocatalysts. J. Mater. Sci. Mater. Electron. 26(3), 1560-1567 (2015). doi:10.1007/s10854-014-2575-x

[20] C. Santato, M. Ulmann, J. Augustynski, Photoelectrochemical properties of nanostructured tungsten trioxide films. J. Phys. Chem. B 105(5), 936-940 (2001). doi:10.1021/jp002232q

[21] F.A. Sheikh, J. Macossay, M.A. Kanjwal, A. Abdal-hay, M.A. Tantry, H. Kim, Titanium dioxide nanofibers and microparticles containing nickel nanoparticles. ISRN Nanomaterials, 2012, Article ID 816474, 8 pages (2012). doi 10.1155/2014/843587

[22] F.A. Sheikh, T. Cantu, J. Macossay, H. Kim, Fabrication of poly (vinylidene fluoride) (PVDF) nanofibers containing nickel nanoparticles as future energy server materials. Sci. Adv. Mater. 3(2), 216-222 (2011). doi:10.1166/sam.2011.1148

[23] A.Z. Sadek, H. Zheng, M. Breedon, V. Bansal, S.K. Bhargava, K. Latham, J. Zhu, L. Yu, Z. Hu, P.G. Spizzirri, W. Wlodarski, K. Kalantar-zadeh, High-temperature anodized WO3 nanoplatelet films for photosensitive devices. Langmuir 25(16), 9545-9551 (2009). doi:10.1021/la901944x

[24] J. Wang, E. Khoo, P.S. Lee, J. Ma, Controlled synthesis of WO3 nanorods and their electrochromic properties in H2SO4 electrolyte. J. Phys. Chem. C 113(22), 9655-9658 (2009). doi:10.1021/jp901650v

[25] X. Lu, X. Liu, W. Zhang, C. Wang, Y. Wei, Large-scale synthesis of tungsten oxide nanofibers by electrospinning. J. Colloid Interface Sci. 298(2), 996-999 (2006). doi:10.1016/j.jcis.2006.01.032

[26] H.-S. Shim, J.W. Kim, Y.-E. Sung, W.B. Kim, Electrochromic properties of tungsten oxide nanowires fabricated by electrospinning method. Sol. Energy Mater. Sol. Cells 93(12), 2062-2068 (2009). doi:10.1016/j.solmat.2009.02.008

[27] Y. Nah, A. Ghicov, D. Kim, P. Schmuki, Enhanced electrochromic properties of self-organized nanoporous WO3. Electrochem. Commun. 10(11), 1777-1780 (2008). doi:10.1016/j.elecom.2008.09.017

[28] Z.-M. Huang, Y.-Z. Zhang, M. Kotaki, S. Ramakrishna, A review on polymer nanofibers by electrospinning and their applications in nanocomposites. Compos. Sci. Technol. 63(15), 2223-2253 (2003). doi:10.1016/S0266-3538(03)00178-7

[29] M. Rolandi, R. Rolandi, Self-assembled chitin nanofibers and applications. Adv. Colloid Interface Sci. 207, 216-222 (2014). doi:10.1016/j.cis.2014.01.019

[30] P.X. Ma, R. Zhang, Synthetic nano-scale fibrous extracellular matrix. J. Biomed. Mater. Res. 46(1), 60-67 (1999). doi:10.1002/(SICI)1097-4636(199907)46:13.0.CO;2-H

[31] N.R. Dhineshbabu, G. Karunakaran, R. Suriyaprabha, P. Manivasakan, V. Rajendran, Electrospun MgO/Nylon 6 hybrid nanofibers for protective clothing. Nano-Micro Lett. 6(1), 46-54 (2014). doi:10.5101/nml.v6i1.p46-54

[32] P. Zhang, L. Wang, X. Zhang, J. Hu, G. Shao, Three-dimensional porous networks of ultra-long electrospun SnO2 nanotubes with high photocatalytic performance. Nano-Micro Lett. 7(1), 86-95 (2015). doi:10.1007/s40820-014-0022-4

[33] R. Nirmala, R. Navamathavan, S.-J. Park, H.Y. Kim, Recent progress on the fabrication of ultrafine polyamide-6 based nanofibers via electrospinning: A topical review. Nano-Micro Lett. 6(2), 89-107 (2014). doi:10.5101/nml.v6i2.p89-107

[34] F.A. Sheikh, M.A. Kanjwal, S. Saranc, W.-J. Chungc, H. Kim, Polyurethane nanofibers containing copper nanoparticles as future materials. Appl. Surf. Sci. 257(7), 3020-3026 (2011). doi:10.1016/j.apsusc.2010.10.110

[35] J.-Y. Leng, X.-J. Xu, N. Lv, H.-T. Fan, T. Zhang, Synthesis and gas-sensing characteristics of WO3 nanofibers via electrospinning. J. Colloid Interface Sci. 356(1), 54-57 (2011). doi:10.1016/j.jcis.2010.11.079

[36] I.M. Szilágyi, E. Santala, M. Heikkilä, V. Pore, M. Kemell, T. Nikitin, G. Teucher, T. Firkala, L. Khriachtchev, M. Räsänen, M. Ritala, M. Leskelä, Photocatalytic properties of WO3/TiO2 core/shell nanofibers prepared by electrospinning and atomic layer deposition. Chem. Vap. Deposition 19, 149-155 (2013). doi 10.1002/cvde.201207037

[37] G. Wang, Y. Ji, X. Huang, X. Yang, P.-I. Gouma, M. Dudley, Fabrication and characterization of polycrystalline wo3 nanofibers and their application for ammonia sensing. J. Phys. Chem. B 110(47), 23777-23782 (2006). doi:10.1021/jp0635819

[38] S.-J. Choi, S.-J. Kim, W.-T. Koo, H.-J. Cho, I.-D. Kim, Catalyst-loaded porous WO3 nanofibers using catalyst-decorated polystyrene colloid templates for detection of biomarker molecules. Chem. Commun. 2015, 1-4 (2015). doi:10.1039/C4CC09725D

[39] T.-A. Nguyen, T.-S. Jun, M. Rashid, Y.S. Kim, Synthesis of mesoporous tungsten oxide nanofibers using the electrospinning method. Mater. Lett. 65(17-18), 2823-2825 (2011). doi:10.1016/j.matlet.2011.05.103

[40] X. Bai, H. Ji, P. Gao, Y. Zhang, X. Sun, Morphology, phase structure and acetone sensitive properties of copper-doped tungsten oxide sensors. Sens. Actuators B 193(31), 100-106 (2014). doi:10.1016/j.snb.2013.11.059

[41] X.Yan, G. Liu, Preparation, characterization, and solution viscosity of polystyrene-block-polyisoprene nanofiber fractions. Langmuir 20(11), 4677-4683 (2004). doi:10.1021/la049955b

References

[1] A.P. Mouritz, M.K. Bannister, P.J. Falzon, K.H. Leong, Review of applications for advanced three dimensional fibre textile composites. Compos. Pt. A-Appl. Sci. Manuf. 30(12), 1445-1461 (1999). doi:10.1016/S1359-835X(99)00034-2

[2] K.S. Karn, H. Harada, Surface water pollution in three urban territories of Nepal, India, and Bangladesh. J. Environ. Manage. 28(4), 483-496 (2001). doi:10.1007/s002670010238

[3] H.R. Pouretedal, M.H. Keshavarz, Study of Congo red photodegradation kinetic catalyzed by Zn1-XCuXS and Zn1-XNiXS nanoparticles. Int. J. Phys. Sci. 6(27), 6268-6279 (2001). doi:10.5897/IJPS09.251

[4] K.I. Konstantinou, A.A. Triantafyllos, TiO2-assisted photocatalytic degradation of azo dyes in aqueous solution: kinetic and mechanistic investigations. Appl. Catal. B. Env. 49(1), 1-14 (2004). doi:10.1016/j.apcatb.2003.11.010

[5] C.A. Buckley, Membrane technology for the treatment of dyehouse effluents. Water. Sci. Technol. 25(96), 203-209 (1992). doi:10.1016/S0958-2118(00)89257-5

[6] N.M. Mahmoodi, Photocatalytic ozonation of dyes using copper ferrite nanoparticle prepared by co-precipitation method. Desalination 279(1-3), 332-337 (2011). doi:10.1016/j.desal.2011.06.027

[7] A. Reza, F.A. Sheikh, M.Z. Abedin, H. Kim, Facile strategy for utilizing sugarcane bagasse as bio-adsorbent for the removal of contaminant form effluents of textile industry. Energy Environ. Focus 4(1), 28-33 (2015). doi:10.1166/eef.2015.1135

[8] Q. Yu, Y. Mao, X. Peng, Separation membranes constructed from inorganic nanofibers by filtration technique. Chem. Rec. 13(1), 14-27 (2013). doi:10.1002/tcr.201200011

[9] M. Riera-Torres, C. Gutiérrez-Bouzán, M. Crespi, Combination of coagulation–flocculation and nanofiltration techniques for dye removal and water reuse in textile effluents. Desalination 252(1-3), 53-59 (2010). doi:10.1016/j.desal.2009.11.002

[10] A. Mittal, R. Jain, J. Mittal, S. Varshney, Removal of yellow ME 7 GL from industrial effluent using electrochemical and adsorption techniques. Int. J. Environ. Pollut. 43(4), 308-323 (2010). doi:10.1504/IJEP.2010.036929

[11] E.M. Golet, A. Strehler, A.C. Alder, W. Giger, Determination of fluoroquinolone antibacterial agents in sewage sludge and sludge-treated soil using accelerated solvent extraction followed by solid-phase extraction. Anal. Chem. 74(21), 5455-5462 (2002). doi:10.1021/ac025762m

[12] A.K. Verma, R.R. Dash, P. Bhunia, A review on chemical coagulation/flocculation technologies for removal of colour from textile wastewaters. J. Environ. Manage 93(1), 154-168 (2012). doi:10.1016/j.jenvman.2011.09.012

[13] M. Grätzel, Dye-sensitized solar cells. J. Photochem. Photobiol. C 4(2), 145-153 (2003) doi 10.1016/S1389-5567(03)00026-1

[14] C.G. Granqvist, Electrochromic tungsten oxide flms: Review of progress. Sol. Energy Mater. Sol. Cells 60(3), 201-262 (2000). doi:10.1016/S0927-0248(99)00088-4

[15] J. Georgieva, E. Valova, S. Armyanov, N. Philippidis, I. Poulios, S. Sotiropoulos, Bi-component semiconductor oxide photoanodes for the photoelectrocatalytic oxidation of organic solutes and vapours: A short review with emphasis to TiO2–WO3 photoanodes. J. Hazard. Mater. 211-212, 30-46 (2012). doi:10.1016/j.jhazmat.2011.11.069

[16] A. Fakhri, S. Behrouzc, Photocatalytic properties of tungsten trioxide (WO3) nanoparticles for degradation of Lidocaine under visible and sunlight irradiation. Sol. Energy 112,163-168 (2015). doi:10.1016/j.solener.2014.11.014

[17] X. Yan, X. Zong, G.Q.M. Lu, L. Wang, Ordered mesoporous tungsten oxide and titanium oxide composites and their photocatalytic degradation behavior. Prog. Nat. Sci. 22(6), 654-660 (2012). doi:10.1016/j.pnsc.2012.11.016

[18] Y. Wicaksana, S. Liu, J. Scott, R. Amal, Tungsten trioxide as a visible light photocatalyst for volatile organic carbon removal. Molecules 19(11), 17747-17762 (2014). doi:10.3390/molecules191117747

[19] M.M. Momeni, Y. Ghayeb, M. Davarzadeh, Electrochemical construction of different titania–tungsten trioxide nanotubular composite and their photocatalytic activity for pollutant degradation: a recyclable photocatalysts. J. Mater. Sci. Mater. Electron. 26(3), 1560-1567 (2015). doi:10.1007/s10854-014-2575-x

[20] C. Santato, M. Ulmann, J. Augustynski, Photoelectrochemical properties of nanostructured tungsten trioxide films. J. Phys. Chem. B 105(5), 936-940 (2001). doi:10.1021/jp002232q

[21] F.A. Sheikh, J. Macossay, M.A. Kanjwal, A. Abdal-hay, M.A. Tantry, H. Kim, Titanium dioxide nanofibers and microparticles containing nickel nanoparticles. ISRN Nanomaterials, 2012, Article ID 816474, 8 pages (2012). doi 10.1155/2014/843587

[22] F.A. Sheikh, T. Cantu, J. Macossay, H. Kim, Fabrication of poly (vinylidene fluoride) (PVDF) nanofibers containing nickel nanoparticles as future energy server materials. Sci. Adv. Mater. 3(2), 216-222 (2011). doi:10.1166/sam.2011.1148

[23] A.Z. Sadek, H. Zheng, M. Breedon, V. Bansal, S.K. Bhargava, K. Latham, J. Zhu, L. Yu, Z. Hu, P.G. Spizzirri, W. Wlodarski, K. Kalantar-zadeh, High-temperature anodized WO3 nanoplatelet films for photosensitive devices. Langmuir 25(16), 9545-9551 (2009). doi:10.1021/la901944x

[24] J. Wang, E. Khoo, P.S. Lee, J. Ma, Controlled synthesis of WO3 nanorods and their electrochromic properties in H2SO4 electrolyte. J. Phys. Chem. C 113(22), 9655-9658 (2009). doi:10.1021/jp901650v

[25] X. Lu, X. Liu, W. Zhang, C. Wang, Y. Wei, Large-scale synthesis of tungsten oxide nanofibers by electrospinning. J. Colloid Interface Sci. 298(2), 996-999 (2006). doi:10.1016/j.jcis.2006.01.032

[26] H.-S. Shim, J.W. Kim, Y.-E. Sung, W.B. Kim, Electrochromic properties of tungsten oxide nanowires fabricated by electrospinning method. Sol. Energy Mater. Sol. Cells 93(12), 2062-2068 (2009). doi:10.1016/j.solmat.2009.02.008

[27] Y. Nah, A. Ghicov, D. Kim, P. Schmuki, Enhanced electrochromic properties of self-organized nanoporous WO3. Electrochem. Commun. 10(11), 1777-1780 (2008). doi:10.1016/j.elecom.2008.09.017

[28] Z.-M. Huang, Y.-Z. Zhang, M. Kotaki, S. Ramakrishna, A review on polymer nanofibers by electrospinning and their applications in nanocomposites. Compos. Sci. Technol. 63(15), 2223-2253 (2003). doi:10.1016/S0266-3538(03)00178-7

[29] M. Rolandi, R. Rolandi, Self-assembled chitin nanofibers and applications. Adv. Colloid Interface Sci. 207, 216-222 (2014). doi:10.1016/j.cis.2014.01.019

[30] P.X. Ma, R. Zhang, Synthetic nano-scale fibrous extracellular matrix. J. Biomed. Mater. Res. 46(1), 60-67 (1999). doi:10.1002/(SICI)1097-4636(199907)46:13.0.CO;2-H

[31] N.R. Dhineshbabu, G. Karunakaran, R. Suriyaprabha, P. Manivasakan, V. Rajendran, Electrospun MgO/Nylon 6 hybrid nanofibers for protective clothing. Nano-Micro Lett. 6(1), 46-54 (2014). doi:10.5101/nml.v6i1.p46-54

[32] P. Zhang, L. Wang, X. Zhang, J. Hu, G. Shao, Three-dimensional porous networks of ultra-long electrospun SnO2 nanotubes with high photocatalytic performance. Nano-Micro Lett. 7(1), 86-95 (2015). doi:10.1007/s40820-014-0022-4

[33] R. Nirmala, R. Navamathavan, S.-J. Park, H.Y. Kim, Recent progress on the fabrication of ultrafine polyamide-6 based nanofibers via electrospinning: A topical review. Nano-Micro Lett. 6(2), 89-107 (2014). doi:10.5101/nml.v6i2.p89-107

[34] F.A. Sheikh, M.A. Kanjwal, S. Saranc, W.-J. Chungc, H. Kim, Polyurethane nanofibers containing copper nanoparticles as future materials. Appl. Surf. Sci. 257(7), 3020-3026 (2011). doi:10.1016/j.apsusc.2010.10.110

[35] J.-Y. Leng, X.-J. Xu, N. Lv, H.-T. Fan, T. Zhang, Synthesis and gas-sensing characteristics of WO3 nanofibers via electrospinning. J. Colloid Interface Sci. 356(1), 54-57 (2011). doi:10.1016/j.jcis.2010.11.079

[36] I.M. Szilágyi, E. Santala, M. Heikkilä, V. Pore, M. Kemell, T. Nikitin, G. Teucher, T. Firkala, L. Khriachtchev, M. Räsänen, M. Ritala, M. Leskelä, Photocatalytic properties of WO3/TiO2 core/shell nanofibers prepared by electrospinning and atomic layer deposition. Chem. Vap. Deposition 19, 149-155 (2013). doi 10.1002/cvde.201207037

[37] G. Wang, Y. Ji, X. Huang, X. Yang, P.-I. Gouma, M. Dudley, Fabrication and characterization of polycrystalline wo3 nanofibers and their application for ammonia sensing. J. Phys. Chem. B 110(47), 23777-23782 (2006). doi:10.1021/jp0635819

[38] S.-J. Choi, S.-J. Kim, W.-T. Koo, H.-J. Cho, I.-D. Kim, Catalyst-loaded porous WO3 nanofibers using catalyst-decorated polystyrene colloid templates for detection of biomarker molecules. Chem. Commun. 2015, 1-4 (2015). doi:10.1039/C4CC09725D

[39] T.-A. Nguyen, T.-S. Jun, M. Rashid, Y.S. Kim, Synthesis of mesoporous tungsten oxide nanofibers using the electrospinning method. Mater. Lett. 65(17-18), 2823-2825 (2011). doi:10.1016/j.matlet.2011.05.103

[40] X. Bai, H. Ji, P. Gao, Y. Zhang, X. Sun, Morphology, phase structure and acetone sensitive properties of copper-doped tungsten oxide sensors. Sens. Actuators B 193(31), 100-106 (2014). doi:10.1016/j.snb.2013.11.059

[41] X.Yan, G. Liu, Preparation, characterization, and solution viscosity of polystyrene-block-polyisoprene nanofiber fractions. Langmuir 20(11), 4677-4683 (2004). doi:10.1021/la049955b

Citation Information

Frank Agyemang Ofori, Faheem A Sheikh, Richard Appiah-Ntiamoah, Xinsheng Yang, Hern Kim, A Simple Method of Electrospun Tungsten Trioxide Nanofibers with Enhanced Visible-light Photocatalytic Activity. Nano-Micro Lett. 7(3), 291-297 (2015). http://dx.doi.org/10.1007/s40820-015-0042-8

History

Received: 6 February 2015 / Accepted: 31 March 2015

 


Additional Info

  • Type of Publishing: JOUR - Journal
  • Title:

    A Simple Method of Electrospun Tungsten Trioxide Nanofibers with Enhanced Visible-light Photocatalytic Activity

  • Author: Frank Agyemang Ofori, Faheem A Sheikh, Richard Appiah-Ntiamoah, Xinsheng Yang, Hern Kim
  • Year: 2015
  • Volume: 7
  • Issue: 3
  • Journal Name: Nano-Micro Letters
  • Publisher: OPEN ACCESS HOUSE SCIENCE & TECHNOLOGY
  • ISSN: 2150-5551
  • URL: http://dx.doi.org/10.1007/s40820-015-0042-8
  • Abstract:

    The present study involves the fabrication of tungsten trioxide (WO3) nanofibers by an electrospinning technique using polyvinyl pyrrolidone (PVP)/citric acid/tungstic acid as precursor solution. It was found that the PVP concentration was one of the most crucial processing parameters determining the final properties of WO3 nanofibers. The optimum concentration of PVP was from 75 to 94 g L-1. The average diameter of the nanofibers increases with increasing the PVP concentration, whereas, it is decreased after sintering and orthorhombic structure were formed at 500 °C. The photocatalytic properties of the as-synthesized nanofibers were also investigated by degrading methylene blue and two-fold efficiency was obtained compared with that of commercial WOmicroparticles.

  • Publish Date: Wednesday, 01 July 2015
  • Start Page: 291
  • Endpage: 297
  • DOI: 10.1007/s40820-015-0042-8